The self-assembly of optically active building blocks into functional nanocrystals as high-activity photocatalysts is a key in the field of photocatalysis. Cobalt porphyrin with abundant catalytic properties is extensively studied in photocatalytic water oxidation and CO2 reduction. Here, we present the fabrication of cobalt porphyrin nanocrystals through a surfactant-assisted interfacial self-assembly process using Co-tetra(4-pyridyl) porphyrin as building block. The self-assembly process relies on the combined noncovalent interactions such as π-π stacking and axial Co-N coordination between individual porphyrin molecules within surfactant micelles. Tuning different reaction conditions (temperature, the ratio of co-solvent DMF) and types of surfactant, various nanocrystals with well-defined 1D to 3D morphologies such as nanowires, nanorods and nano hexagonal prism were obtained. Due to the ordered accumulation of molecules, the nanocrystals exhibit the properties of the enhanced capability of visible light capture and can conduce to improve the transport and separation efficiency of the photogenerated carriers, which is important for photocatalysis. Further studies of photocatalytic CO2 reduction are being performed to address the relationship between the size and shape of the nanocrystals with the photocatalytic activity.

While the use of iron oxide nanoparticles as magnetic resonance contrast agents for clinical imaging is established, they are more recently experiencing renewed interest as alternatives to gadolinium-based contrast agents. Ultra-small iron oxide nanoparticles have unique pharmacokinetics, metabolic and imaging properties. These properties have led to improved techniques for imaging a variety of vascular, oncologic and inflammatory conditions with iron oxide nanoparticles. Current research efforts are aimed at harnessing the characteristics of these nanoparticles to advance magnetic resonance imaging techniques and explore new therapeutic potentials. While there are some limitations to the use of iron oxide nanoparticles, including allergies to parenteral iron and iron storage disorders, the practicable applications for these agents will continue to expand. The purpose of this review is to provide a brief overview of the history and synthesis of iron oxide nanoparticles, their current applications in clinical imaging and their prospective clinical applications.

The interaction of spherical gold nanoparticles (AuNPs) of 20nm elaborated by Turkevich method with the erythrocytes ghosts (7-8 μm) cell membrane was evaluated. The AuNPs-Membrane interaction was determined using confocal microscope, Uv-Vis spectroscopy and SEM analysis. The result show that nanoparticles larger than 20nm are adhered to the erythrocyte ghost membrane due their size and surface modification. Smaller AuNPs enter onto the cell by simple diffusion through the plasmatic membrane voids, these data may favor the best design and application in the treatments applied in biomedicine.

Lanthanum aluminate-lanthanum zirconate composite was synthesized by using coprecipitation and powders were dried by spray-drying. Pseudoboehmite was used as a precursor of lanthanum aluminate during the precipitation process. Highly crystalline phases were obtained. Lanthanum zirconate exhibits a pyrochlore structure at lower synthesis temperature (>1500°C). Due drying technique lanthanum aluminate particles appear surrounded by lanthanum zirconate. No other remaining phases were observed and the phase distribution in the composite was homogeneous.

Sensors based on the surface plasmon resonance (SPR) technique are useful devices to detect and monitor interactions between biomolecules in real-time. SPR is a label-free method that monitors the variation of reflectivity of a biochip composed of a metal-coated glass prism and can be applied in several areas, such as biotechnology, food safety and clinical diagnosis. In the last years, several researchers have proven the efficiency of metallic nanoparticles (NPs) in the enhancement of SPR signal. This feature allowed the detection of biomolecules at very low concentration. Aiming to further enhance SPR signal towards the detection of proteins at low concentration and by a simple procedure, the present work compared the performance of gold and platinum bimetallic NPs (AuPtNPs) with that of monometallic gold NPs (AuNPs) in the enhancement of SPR signal. In order to evaluate the NPs, protein peanut agglutin (PNA) was used as target analyte and anti-PNA antibody was used as sensing molecule. Firstly NPs were functionalized with anti-PNA antibody and incubated with a solution containing PNA. Then, the NPs bound to PNA were injected into the SPR equipment containing a biochip previously modified with anti-PNA antibody. The results demonstrated that the AuPtNPs provided a 91-fold increase compared to the direct detection of free PNA in solution. In comparison with AuNPs, the signal generated by AuPtNPs was about 4 times higher. This encouraging result indicated that the application of bimetallic NPs may be a better strategy to further enhance sensitivity of SPR biosensors and could drive the development of new strategies that are not only simple, but also able to detect proteins at low concentrations, which is of great importance, especially in clinical diagnostics.

The application of intense pulsed light (IPL) to printed copper nanoparticle (CuNP) films enables rapid curing on low temperature substrates in ambient conditions. In this work, we printed CuNP ink on liquid crystal polymer (LCP; Vectra A resin) and then cured the films using a high energy density light pulse. High-resolution SEM images of the cured films revealed that the CuNPs on LCP were fused together. Optimal curing parameters were a 5 ms pulse, 75% duty cycle, and an energy density range of 4.2–5.2 J⋅cm-2. Sheet resistance, Rs, values as low as ~0.1 Ω⋅sq-1were obtained. The LCP substrate took on a yellowed appearance after the application of five pulses and exhibited a surface free energy increase. A filter that blocked wavelengths <450 nm was placed over the printed copper film on LCP. As expected, the presence of the filter decreased the total energy density and produced a cured film with high Rs; however, when the energy density was increased in the presence of the filter, the Rs remained high (0.95 Ω⋅sq-1). This preliminary work indicates that additional studies are required not only to understand low thermal budget curing on LCP, but also to elucidate the properties of substrates that enable low Rs.