Up until about 2005, the main application of halloysites had been as an alternative raw material to kaolinite for ceramics. Since then, however, there has been an exponential increase in studies aimed at applications of halloysite nanotubes, now widely referred to as HNTs. The readily available and relatively cheap nanotubular forms of halloysite have potential uses in nanocomposites with polymers, as carriers for active agents, e.g. in medicine, agriculture, cosmetics and environmental remediation, as well as in nanotemplating, as supports for catalyst immobilization and as heterogeneous catalysts.

The strongly coloured Cu-triethylenetetramine complex (Cu-Trien) provides a fast and easy way to measure the cation exchange capacity of clay samples, but the reliability of this method has been questioned in recent publications. This work identifies several reasons for the poor reliability, thus improving both the precision and accuracy of the CEC method. Pure Trien is shown here to intercalate as does the Cu-Trien complex. Hence, the purity of Trien and also the Cu/Trien ratio require special attention. Using cold Cu-Trien solutions produces systematic deviations in CEC determinations caused by errors in the pipetted volumes. The present study demonstrates, for the first time, that the Cu-Trien complex protonates and changes its effective charge beyond 2+. Based on titration experiments at three different temperatures, a correction function is derived for calculating the total charge of the Cu-Trien complex as a function of pH. Accounting for these pH-corrected charges indicates that Cu-Trien may well be insensitive to edge charges on smectite. Finally, it is shown here that the ratio of sample mass to the initial amount of Cu-Trien is critical because excess adsorption of Cu-Trien in addition to CEC sensu strictu was observed.

The EPR spectrum of a previously unreported paramagnetic centre formed in kaolin minerals by exposure to γ radiation is described. This centre, which is referred to here as the ‘C-centre’, was seen initially during an investigation of the radiation dose response of the EPR signal in the natural Lampang kaolin from northern Thailand, and its EPR properties are now presented for a purified sample from this material. They suggest a paramagnetic centre with rhombic symmetry based on O− associated with a single 27Al atom. Computer simulations suggest spin Hamiltonian parameters of g1 = 1.976, g3 = 2.0417 and A(27Al) = 2.10 mT, with g2 ≈ 2.01. This C-centre was also seen as a minor radiationinduced component in both crude and purified Ranong kaolin samples, along with a stronger signal from the B-centre radical. It seems to be associated with the kaolinite component, but was lost on annealing to 300°C after which only the signal from the A-centre was visible.

The design of nanostructured materials based on natural components, such as clay minerals, offers new solutions to biomedical challenges such as more efficient and storage-stable vaccines. Clay-lipid hybrid materials have proved useful as adjuvants in influenza vaccines and with a possible projection to leishmaniasis vaccines and other pathogens. Self-assembly of phospholipid molecules on the surface of microfibrous sepiolite and lamellar Mg/Al layered double hydroxide renders a biocompatible lipid bilayer membrane that ensures non-degrading immobilization of proteins and other biological species including viral particles and DNA (deoxyribonucleic acid). Immunization tests in mice showed the superior immunogenicity of a clay-lipid-supported virus compared to a commercial aluminium hydroxide adjuvant.

Halloysite with tubular morphology is formed in a wide range of geological environments from the alteration of various rock types. Intrusive acidic coarse-grained rocks, such as granites, pegmatites and anorthosite, with large potash and sodic feldspars contents, are subsequently altered to kaolinite, halloysite and other clay minerals by weathering or shallow hydrothermal fluid activity. Processing to separate the halloysite-kaolinite fraction from the altered host rock provides a product which can be used as a paper filler and in ceramics and fibreglass, among other uses, with various deposits in Brazil, China, Thailand and elsewhere. In the Kerikeri-Matauri Bay district of Northland, North Island, New Zealand, volcanic alkali rhyolite was extruded as domes and cooled rapidly with fine-grained feldspar subsequently altered to halloysite. The IMERYS plant in Matauri Bay separates the clay from the quartz-cristobalite matrix with an ∼20% yield of halloysite. The principal market is for high-quality porcelain and bone china that require low levels of Fe2O3 and TiO2. Deposits with high levels of halloysite occur in China, Turkey and the USA. The Dragon mine in Utah, USAwas recently reopened by Applied Minerals Inc. and now produces halloysite from zones of up to 100% white halloysite. Smaller occurrences of tubular halloysite are mined in China, Turkey and elsewhere from masses of comparatively pure clay that appear to have crystallized directly from solutions in which Al and Si were soluble.

Newly discovered K-bentonite beds, interstratified with limestones/dolomitic limestones of the Upper Devonian–Lower Carboniferous Yılanlı Formation, are exposed in the northwestern Black Sea region of Turkey, around Zonguldak and Bartın. K-bentonite samples collected from four different locations: the Gavurpınarı and Yılanlı Burnu quarries from the Bartın area, the Çimşir Çukurları quarry from the Şapça area, and the Güdüllü and Gökgöl highway tunnel section near Zonguldak city were investigated using optical microscopy, X-ray diffraction and inductively coupled plasma mass spectrometry in order to reveal their mineralogical and geochemical characteristics and understand their origin and evolution. The K-bentonites occur at different levels in the Yılanlı Formation as 2–40 cm-thick, greenish to yellowish beds cropping out several hundred metres along strike. Preliminary biostratigraphic data suggest that the protoliths of the Bartın (Gavurpınarı and Yılanlı Burnu) and Güdüllü K-bentonites were deposited at around the boundary between the Frasnian and Famennian, whereas those in the Şapça and Gökgöl sections are slightly younger (Devonian–Carboniferous boundary interval). The lithofacies types of the host carbonate rocks suggest an ‘epeiric’ shallow carbonate platform environment. Illite and mixed-layer illite-smectite were the major clay minerals in the K-bentonites. The K-bentonites from the Bartın area display a high degree of illitization and consist mainly of illite indicating high-grade diagenesis, whereas illite-smectite-rich samples from the Şapca and Gökgöl tunnel locations reflect relatively lower diagenetic conditions. According to their geochemical compositions, two groups of K-bentonites were distinguished, one with alkali basalt (Bartın area and Güdüllü locations) and one with trachyte affinities (Gökgöl tunnel and Şapça locations). Geochemical fingerprinting of K-bentonites by trace and rare earth element (REE) data suggest that tephras with alkali basalt composition have been derived by a source formed in a ‘continental back-arc’ setting, whereas the source of K-bentonites with trachytic precursors is related to ‘continental within-plate rifting’. An evaluation of the global Late Devonian and Devonian–Carboniferous volcanism suggests that the bentonite precursors may be related to late-Variscan magmatism in Laurussia.

The nitric-acid dissolution of chrysotile was investigated with the aim of revealing the effect of pH on its structure. Chrysotile becomes more soluble at lower pH, with the octahedral, brucite sheet more readily dissolved than the tetrahedral sheet. The dissolution of the brucite sheet increases the pH of the solvent, because of the release of OH− groups along with the Mg2+ ions. At pH 2.00, the characteristic cylindrical fibre bundle structure of chrysotile is retained after dissolution, although the outside surface of each fibre becomes rough. Chrysotile remains fibrous upon dissolution at pH 1.08, but the fibres are no longer crystalline and their cylindrical structure collapses. The nitric-acid treatments result in an increase in both the specific surface area and the pore volume of chrysotile.

The present study investigated the removal of methylene blue (MB) and orange II (OII) dyes from synthetic wastewater by means of adsorption and photocatalysis using natural kaolins. ForMB adsorption, the raw kaolinite-rich samples showed the greatest adsorption capacity, with rapid uptake (90% after 20 min). The experimental results were fitted better using the Langmuir isotherm model parameters compared to the Freundlich model, suggesting that the adsorption corresponds to monolayer coverage of MB molecules over the kaolinite surface. For OII, neither the Langmuir nor the Freundlich model gave reliable results, because the adsorption of anionic dye molecules by the clayey particles is not favoured.

Mixtures of kaolinite/Degussa TiO2 were also prepared, and their photocatalytic properties under UVlight exposure were investigated. Decolourization of MB solutions was observed, even in a mixture with low TiO2 content. This is related to the combined effect of adsorption and photocatalysis and, unlike the pure clay samples, the efficiency of such mixtures against OII was only slightly weaker (80–94%).

For TiO2-impregnated clays, with the kaolinite layers separated by sol-gel TiO2 particles, the MB removal was slow and effective only after >24 h due to the complexity of the bonding of MB molecules. On the other hand, the removal performance against OII solutions was very efficient (nearly 100%) within only 2 h. This excellent performance was attributed to morphological changes in clay particles.

Smectite-rich clays are to be used in nuclear repositories for sealing in the radioactive waste. As the radioactive decay produces heat it may affect the chemical, physical and hydromechanical properties of the clay components in the repository. An ‘alternative buffer material’ (ABM) experiment is a Svensk Kärnbränslehantering AB (SKB)-led in situ heating test placed in boreholes in the Äspö tunnel (Sweden). The 2nd ABM package was dismantled in April 2013, after 6.5 y of equilibration with Äspö groundwater and 5 y of heating. The objective was to investigate the long-term effects of the iron heater and Äspö groundwater on four of 31 compacted blocks made of MX-80, Deponit CaN and Friedland clays.

Compared to the starting materials, major changes in the exchangeable cation populations were observed. Within horizontal profiles, water-soluble sulfate, Ca, K and Mg increased; poorly crystalline Fe oxide contents decreased; total Mg, Ca and S increased; and a decrease in the amounts of total Na and K away from the host rock towards the heater was observed. At the boundary with the heater, an increase in the total Fe content, decreases in total Si and Al contents, precipitation of gypsum and anhydrite, dissolution of cristobalite and feldspars, and indications of the formation of trioctahedral clay minerals were observed. A decrease in swelling pressure for the Friedland clay (in drill-cored samples) was recorded which was recovered after grinding and recompaction. No effects of hydraulic conductivity were found, after 6.5 y of reaction time, in the subsurface of any of materials studied.

Twenty one samples of relatively pure tubular halloysites (HNTs) from localities in Australia, China, New Zealand, Scotland, Turkey and the USA have been investigated by X-ray diffraction (XRD), infrared spectroscopy (IR) and electron microscopy. The halloysites occur in cylindrical tubular forms with circular or elliptical cross sections and curved layers and also as prismatic tubular forms with polygonal cross sections and flat faces. Measurements of particle size indicate a range from 40 to 12,700 nm for tube lengths and from 20 to 600 nm for diameters. Size distributions are positively skewed with mean lengths ranging from 170 to 950 nm and mean diameters from 50 to 160 nm. Cylindrical tubes are systematically smaller than prismatic ones. Features related to order/ disorder in XRD patterns e.g. as measured by a ‘cylindrical/prismatic’ (CP) index and IR spectra as measured by an ‘OH-stretching band ratio’ are related to the proportions of cylindrical vs. prismatic tubes and correlated with other physical measurements such as specific surface area and cation exchange capacity. The relationships of size to geometric form, along with evidence for the existence of the prismatic form in the hydrated state and the same 2M1 stacking sequence irrespective of hydration state (i.e. 10 vs. 7 Å) or form, suggests that prismatic halloysites are the result of continued growth of cylindrical forms.

An homogenous intercalated compound of dioctahedral 1:1 clay mineral with cesium chloride was prepared by immersing an homogeneous 8.4 Å hydrated nacrite in a CsCl-saturated solution. The nacrite/CsCl complex obtained was studied using X-ray diffraction and thermogravimetric analysis (TGA). The best agreement between the observed and the simulated ρ(z) (R = 7%) was obtained with one Cl− ion, one Cs+ ion and onewater molecule (per half-unit cell). The cation was located near the oxygen atom plane, while the anion was located near the hydroxyl groups of the adjacent layer. The number of the species intercalated in nacrite/CsCl was confirmed by TGA analysis. The best agreement between the calculated and the experimental hkl reflections, with h and/or k ≠ 0, corresponded to a stacking of 70% and 30% for T1 = −0.35a − 0.20b + 10.50n and T2 = +b/3 + 10.5n, respectively. These results indicate that the surface hydroxyls form hydrogen bonds with Cl− ions. The Cs+ ions are situated near the ditrigonal cavities of the tetrahedral sheet and they interact with the surface oxygen atoms whereas the H2O molecules interact with the intercalated species.

Greece is a major bentonite producer, with Milos Island being one of the largest bentonite mining centres in the world. In addition to the bentonite deposits which are well known, various other occurrences exist in the islands of Chios and Samos, Eastern Aegean and in some areas of Thrace, in NE Greece. These bentonites are associated with volcanic activity and their age ranges from Lower Oligocene in Thrace, to Lower–Middle Miocene in Chios and to Upper Miocene in Samos. Although some of these materials have been utilized since ancient times (e.g. the Samian Earth), these bentonites have been mined only at a local scale. In this study the first data on the mineralogical and geochemical characteristics of these bentonites are presented.

The Samos bentonites of UpperMiocene age are medium–lowgrade (40–70% smectite) and crop out in the SE margin of the Karlovasi Basin formed at the expense of acidic pyroclastic flows mainly in a subaeriallacustrine environment. They consist mainly of Ca-rich medium–high-charge montmorillonite, opal-CT and sanidine with minor quartz and locallymordenite. The Chios bentonites of Lower–MiddleMiocene agewere formed at the expense of trachyandesitic tuffs in a lacustrine environment in the Neogene Basin at theSEpart of the island. They consist mainly of Ca,Mg-rich high-charge montmorillonite (33–75%), similar to the SAz-1, and opal-CT, minor plagioclase, chlorite, plagioclase, carbonates and traces of talc and serpentine. In Thrace, LowerOligocene pyroclastic flows, tuffs and lavas of acidic-intermediate compositionwere altered to zeolites and bentonites in the sedimentary basins of the Feres-Pefka, Skaloma and Sappes areas. The parent pyroclastic rockswere altered to Ca-rich and in places,Na-rich, dioctahedralmontmorillonite or Fe-rich beidellite (Sappes area) and with minor opal-CT,mordenite, quartz, plagioclase and, in places, illite. The bentonites are medium–high grade (50–58% smectite in Feres-Pefka, 74–86% in Skaloma and 29–40% in Sappes).

The bentonites havemoderate cation exchange capacity andmoderate/lowswelling index and viscosity and they are not suitable for the drilling and foundry industries. However, preliminary results show that after processing, most of the depositsmight be utilized in high added-value applications such as bleaching earths or in the synthesis of clay-based polymer nanocomposites.

Two 20-cm long columns of MX-80 bentonite compacted at a nominal dry density of 1.7 g/cm3 with a water content of 17% were tested in thermo-hydraulic (TH) cells with the aim of simulating the conditions of a sealing material in a nuclear waste repository. On top of the columns a hydration surface simulated the host rock supplying groundwater and at the bottom a heater simulated the waste canister. The tests comprised two phases: a heating phase and a ‘heating + hydration’ phase. The temperatures at the ends of the columns were set during the last phase to 30°C at the top and 140°C at the bottom, respectively. The thermo-hydraulic treatment resulted in major changes along the bentonite columns. These changes led to significant gradients along the column with respect to the physical state (water content, dry density) and geochemistry of the bentonite. Smectite dissolution processes occurred. As a result, colloids were probably produced, particularly in the more hydrated areas. In the warmest part of the columns precipitation of carbonates took place, caused by their solubility decrease with temperature and the evaporation. The increase in water content reduced the ionic strength of the pore water in the more hydrated areas where species such as gypsum were dissolved. The solubilized ions were transported towards the bottom of the columns; Na+, Ca+, Mg2+ and SO42− moved at a similar rate and K+ and Cl− moved farther. These solubilized ions precipitated in the form of salts farther away along the columns as the test was longer. The TH treatment implied the loss of exchangeable positions in the smectite, particularly towards the heater. The cation exchange complex was also modified.

In the northernmost Calchaquí Valley (Salta, Argentina), the Paleogene continental sediments show a transition from smectite, at the top, to R3 I-S (>90% illite) through R1 I-S (65–80% illite), in contrast to the remaining sectors, containing smectite up to the bottom. Samples at the base of the succession were characterized by high-quality step-scan X-ray diffraction (XRD), scanning electron microscopy (SEM) and analytical high-resolution transmission electron microscopy (HRTEM). Analysis by SEM demonstrated dissolution of primary phases (feldspars, micas and quartz) and crystallization of illite, I-S and kaolinite. As this alteration is not pervasive, an intermediate fluid/rock ratio could be inferred. The lattice-fringe images of the samples from upper parts of the sequence show abundant I1-rich areas, whereas in the lower parts of the sequence, illite packets and I3 I-S coexist and compositions evolve towards muscovite (tetrahedral-charge increase, principally compensated by Mgby- Al substitution in octahedral sites and by a slight decrease in Ca in interlayer sites). As burial temperatures were probably similar in all the samples, depth was not responsible for the illite formation at the bottom. The TEM textures suggest that illitization proceeded mainly by dissolution-crystallization. The active faults close to the northern Calchaquí Valley probably promoted the circulation of hot, deep fluids, favouring illitization.

Hydrated halloysite was discovered in books, a morphology previously associated exclusively with kaolinite. From ∼1.5 to ∼1500 μm in length, the books showed significantly greater mean Fe contents (Fe2O3 = 5.2 wt.%) than tubes (Fe2O3 = 3.2 wt.%), and expanded rapidly with formamide. They occurred, along with halloysite tubes, spheroids and plates, in highly porous yet poorly permeable, silt-dominated, Si-rich, pumiceous rhyolitic tephra deposits aged ∼0.93 Ma (Te Puna tephra) and ∼0.27 Ma (Te Ranga tephra) at three sites ∼10–20 m stratigraphically below the modern landsurface in the Tauranga area, eastern North Island, New Zealand. The book-bearing tephras were at or near saturation, but have experienced intermittent partial drying, favouring the proposed changes: solubilized volcanic glass + plagioclase→halloysite spheroids→halloysite tubes→halloysite plates→ halloysite books. Unlike parallel studies elsewhere involving both halloysite and kaolinite, kaolinite has not formed in Tauranga presumably because the low permeability ensures that the sites largely remain locally wet so that the halloysite books are metastable. An implication of the discovery is that some halloysite books in similar settings may have been misidentified previously as kaolinite.

The use of Mg-montmorillonite in the production of organoclay without sodium activation was investigated. For this purpose, organophilization experiments were carried out by varying the concentration of two surfactants: hexadecyltrimethylammonium (HDTMA+) and dodecyltrimethylammonium (DTMA+) ions. These surfactantswere used at concentrations 0.7, 1.0 and 1.5 times that of the cation exchange capacity (62.6 meq/100 g) of the clay, with a reaction time of 8 h at temperatures of 25 and 80°C. X-ray diffraction (XRD) results confirmed the intercalation for both in natura and activated samples. The Fourier-transforminfrared (FTIR) spectroscopy and XRD results showed that the ratio of gauche/trans conformers decreased with increased basal spacing. The results of thermodifferential and thermogravimetric analysis (DTA/DTG) confirmed the thermal stability of the organoclay up to 200°C, permitting the use of suchmaterial in the synthesis of polymer/clay nanocomposites obtained by the melt blending. Thus, Mg-montmorillonite can be intercalated with alkylammonium ions without prior Na-activation to form organoclays. The possibility of using natural (non-activated) Mg-montmorillonite represents a significant difference in terms of processing cost in comparison with existing Ca-montmorillonite in Brazil or even with imported bentonites that require Na-activation during beneficiation.

Compacted bentonite is to be used as a component of an engineered barrier system to retard the migration of radionuclides in the geological disposal of radioactive waste. In such an environment, montmorillonite in compacted bentonite might be altered to illite due to the hydrothermal reactions caused by the decay heat of radionuclides. In the present study, the diffusion and retention behaviour of Cs in compacted montmorillonite containing illitewas investigated using through-diffusion experiments. The experimental results showed that the flux of Cs attributed to the surface diffusion was independent of the sorption of Cs on illite, indicating that the Cs sorbed on illite was immobile or considerably less mobile than the Cs sorbed on montmorillonite. Consequently, the illite content in compacted bentonite is expected to enhance the sorption capacity of Cs without causing surface diffusion.

Aung et al. (2014, 2015) described the activation of kaolin samples to remove coloured pigments from rice-bran oil, the effects of various treatments on their decolourization capacity, and the characterization of these kaolin samples by physical methods. This research used a kaolin sample from Ranong in southern Thailand, and investigated the effects of grinding and heat treatment prior to acid activation of the mineral. The various activated mineral phases were then characterized by a combination of X-ray diffraction, Fourier-Transform infrared spectroscopy and X-ray fluorescence. This work represented an extension of research reported previously by Worasith et al. (2011a), in which various samples of the same Ranong kaolin were characterized after grinding and acid activation, and their capacities to decolourize rice-bran oil evaluated (Worasith et al., 2011b). However, despite the similarities in the experiments, there are some important differences in the results presented in these two sets of publications, which raise questions concerning the conduct of this type of research and the generality of any conclusions derived.

The objective of the DOPAS international project is to design a sealing-plug system for deep geological repository (DGR) use, to provide detailed plans for the design of such plugs, to test the characteristics of the materials to be used and the construction technology and to install four experimental in situ plugs. The Czech experimental pressure and sealing-plug (EPSP) experiment is being conducted in a rock environment consisting of granitoids at the Josef Regional Underground Research Centre. The concept of the experiment is based primarily on the use of materials and technology available in the Czech Republic and the principal aim is to demonstrate the technical viability and functioning of a pressure-resistant plug located in a future DGR. The completion of the EPSP experiment will contribute towards both the demonstration of how sealing-plug systems behave under real underground conditions and the long-term safety of a future DGR in the Czech Republic.