Photocatalytic degradation of polluted water by means of minerals, such as clays and oxides, which have surfaces that exhibit catalytic properties, has been suggested to be a useful new strategy to promote both organic and inorganic pollutant degradation. Nevertheless, much still remains to be studied about the capability of mixed metal oxides derived from lanthanum-containing layered double hydroxides to promote pollutant removal by means of photocatalytic degradation with the mineral surfaces. The objective of the present study was to investigate the synthesis of ternary MgAlLa mixed-metal oxides (MgAlLa-M) with various Mg/Al/La molar ratios through a hydrotalcite-like precursor route by co-precipitation of appropriate amounts of metal salts from homogeneous solution, followed by calcination at 600°C. The crystal structure, surface morphology, and optical properties of the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR), and UV-Vis diffuse reflectance spectroscopy (DRS). Analysis by XRD showed that MgO, La2O3, MgAl2O4, and La10Al4O21 phases coexisted in calcined samples as MgAlLa-M. The samples showed a small band gap of 3.11–3.35 eV according to DRS. The photocatalytic activities of the samples were evaluated by degradation of methylene blue (MB) under visible light irradiation. MgAlLa-M had better photocatalytic properties than hydrotalcite precursors, and the MgAlLa-0.5-M possessed the best photocatalytic activity. The photocatalytic degradation efficiency of MB dye with MgAlLa-0.5-M under visible light irradiation for 1 h was 99.89% in the presence of H2O2, which exceeded the binary MgAl-M (84.06%) under the same conditions. The high photocatalytic activity of the sample was attributed to the addition of La(III). In addition, the possible mechanism of photocatalytic degradation of MB by MgAlLa-M was discussed. The results showed that •O2– plays a major role in the MgAlLa-0.5-M/H2O2 system.

Microporous structure in zeolite leads to diffusion limitation, which causes coke formation and is harmful to catalytic reactions. Hierarchical zeolite containing primary microporosity and secondary porosity at the meso- and macroscales has received much attention due to its enhanced mass transport. Hierarchical Y zeolites were obtained by treating NH4-Y zeolite with high-temperature calcining and acid-base leaching. The results demonstrated that the calcined zeolite showed great crystallinity after acid-base leaching. The mechanism of introduction of mesopores was demonstrated in detail. The calcination transformed framework Al to extra-framework Al and enlarged the defect by acid and alkali. The mesopores increased with the calcining temperature and holding time. The relationship between the heating rate and the removal of Al species was non-linear; a heating rate of 100°C/h exhibited good protection for the zeolite structure.

The adsorption of bovine serum albumin (BSA) protein is important for protein research but remains a great challenge. Here, the hydrothermal method and calcination in a hydrogen-argon mixed atmosphere were used to obtain ordered mono-crystalline magnetic Fe3O4 nanorings with controllable size and uniform structure, which were applied to the adsorption of BSA protein. The results showed that the magnetic Fe3O4 nanorings prepared have the advantages of good crystallinity, controllable morphology, and excellent magnetic response. The Fe3O4 nanorings had an outer diameter of ~160–180 nm, inner diameter of ~80–110 nm, and height of 70 to ~110 nm. The amount of BSA adsorbed by magnetic Fe3O4 nanorings increased with increasing protein concentration; when the concentration of BSA was ~2.75 mg·mL-1 the adsorption amount approached saturation. When the pH value of the solution was ~5, the Fe3O4 nanorings absorption of BSA was greatest. With increasing adsorption time, the amount adsorbed increased gradually. Adsorption equilibrium was reached after 3 h. According to the formula, the saturated adsorption capacity of BSA per gram of magnetic Fe3O4 nanorings was 325.2 mg.

Graphical Abstract

Lubricants are an essential component in high-performance mechanical equipment, but traditional lubricants are becoming inadequate for meeting the increasing demands for anti-friction and anti-wear properties and they discharge harmful chemicals to the environment. The purpose of the present study was to explore the use of sepiolite as a novel oil additive to extend the performance of lubricants. Sepiolite nanofibers were first treated by acid followed by a dry air flow, aimed at increasing the pore volume and decreasing the particle size. Then the nanofibers were further modified by an organosilane coupling agent to reduce the surface free energy and to improve the dispersion stability in lubricant. A significant improvement in the performance of the lubricant was achieved by using the modified sepiolite nanofibers as an additive. When the amount of modified sepiolite nanofibers added was 1.5 wt.%, the best performance was demonstrated by the lubricant, showing a viscosity increase at 40°C and 100°C, and an increase in resistance to oxidation. Moreover, the acid value and pour point decreased, and the copper sheet corrosion level dropped to its lowest value.

Adsorption of uranyl (UO22+) ions to mineral surfaces is a potentially effective method for removing this hazardous metal from water, but other toxic trace metal ions (Xn+: Rb+, Sr2+, Cr3+, Mn2+, Ni2+, Zn2+, Cd2+) in uraniferous wastewaters compete with UO22+ for adsorption sites and thus may diminish the capacity of adsorbents to sequester UO22+. A better understanding of competitive adsorption among these metal ions and the development of better adsorbents are, therefore, of critical importance. The purpose of the present study was to synthesize and characterize magnetic adsorbents, consisting of MFe2O4 (M = Mn, Fe, Zn, Co, or Ni) nanoparticles synthesized on montmorillonite (Mnt) edge sites, and to investigate their use as adsorbents for UO22+, including competitive adsorption with trace metal ions. Selective adsorption was studied using Langmuir, Freundlich, and Dubinin-Radushkevich isotherms, and the results showed that Xn+ ions were adsorbed primarily on MFe2O4-montmorillonite surfaces, and the UO22+ ions were adsorbed on the interfaces between montmorillonite edge surfaces and MFe2O4 nanoparticles. Using the Freundlich model, the interface adsorption capacity of UO22+ reached 25.1 mg·g–1 in mixed solution. Further, the UO22+ and Cr3+ ions had a redox reaction on the interfaces with synergistic adsorption. Herein, the adsorption capacity of Cr3+ was 60.2 mg·g–1 using the Freundlich isotherm. The results demonstrated that the MFe2O4-montmorillonite with highly selective adsorption of UO22+ ions is applicable to UO22+ treatment in the presence of toxic trace metal ions.

Graphical abstract

Hydrophobicity, high viscosity, and dispersion are important properties for organo-montmorillonites, and all organo-montmorillonite configurations have yet to be fully characterized with respect to this property. High-viscosity montmorillonite (Mnt) is useful in gels and as an adsorber. The current study focused on modifying Mnt using organic cations and anions of various chain lengths in batch experiments with various concentrations and ratios. The viscosity of organic Mnt reached up to 395 mP.s. Molecular dynamics simulations and X-ray diffraction (XRD) were used to identify the conditions and arrangement of organic cations and anions in the Mnt interlayer area. The intercalation mechanism of organic cations and anions was also determined, providing a theoretical basis for the preparation of high-viscosity Mnt.

Waste brownfield-site soils contaminated with heavy metals such as Zn and Cr are of critical environmental concern because of the rapid urbanization and industrialization that is occurring in China. Thermal treatment can fix heavy metals in specific mineral structures, which might be a promising technology for remediation and reutilization of the metal-contaminated soils. The objective of the present study was to elucidate the stabilization mechanisms of Zn and Cr through thermal treatment of mixtures of ZnO + Cr2O3 to form ZnCr2O4 and to confirm that Zn and Cr were incorporated simultaneously into the spinel structure. The incorporation efficiency for Zn was quantified, with the value ranging from 70.6 to 100% over the temperature range 700–1300°C. Leaching results further confirmed that ZnCr2O4 spinel was a superior product for Zn and Cr immobilization. Then, by artificially sintering Zn- and Cr-enriched soils, both Zn and Cr were immobilized effectively (with three orders of magnitude reduction in Zn leachability) in the ZnCr2O4 spinel as the predominant product phase. In addition, multiple heavy metals such as Zn, Cu, and Cr in the actual brownfield-site soils were well immobilized after sintering, which confirmed the potential for practical application of the thermal treatment technology utilized in this study.

Adsorption desulfurization is a potential new method for deep desulfurization of fuel oil. The development of adsorbents with high adsorption capacity and selectivity is the core of deep adsorption desulfurization. The adsorption behavior of thiophene in MCM-41 mesoporous materials modified by various metal ions was studied in order to understand the adsorption desulfurization process of molecular sieves. The Fe-, Co-, and Zn-modified MCM-41 materials were prepared using a one-step in situ hydrothermal synthesis method. The modified MCM-41 molecular sieves maintained the mesoporous structure, and the metal ions had specific dispersion on the surface of the molecular sieves. Adsorption of thiophene on the surfaces of molecular sieves had both physical and chemical characteristics. The adsorption desulfurization performance of the modified molecular sieve was superior to that of the pure silica molecular sieve. In the simulated gasoline with sulfur content of 220 μg/g, when the amount of adsorbent used was 100 mg, the adsorptive desulfurization performance tended to be in equilibrium, and the optimum adsorption temperature was 30°C. Fe-MCM-41 and MCM-41 molecular sieves reached adsorption equilibrium after ~60 min, but the desulfurization rate of Co-MCM-41 and Zn-MCM-41 still increased slightly. The kinetic simulation results indicated that the pseudo-second-order kinetics adsorption model described well the adsorption process of thiophene on molecular sieves. The molecular sieve Fe-MCM-41 had the best desulfurization performance with an equilibrium adsorption capacity of 14.02 mg/g and the desulfurization rate was ~90%.

The aim of the present study was to examine effects of black liquor-montmorillonite (BL-Mnt) complexes on the mechanical and thermal properties of epichlorohydrin rubber. Considering the stability effect of lignin and the barrier property of clay minerals, a significant enhancement of thermo-oxidative aging properties of ECO/BL-Mnt composites was expected. Poly (epichlorohydrin-co-ethylene oxide) (ECO) composites filled with BL-Mnt complex were prepared by mechanical mixing on a two-roll mill. The ECO/BL-Mnt composites were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). Both XRD and TEM data showed that the filler particles were well dispersed throughout the ECO/BL-Mnt composites. The tensile strength, elongation at break, and 100% modulus of the rubber composite were 14.0 MPa, 457%, and 3.9 MPa, respectively, at a 50% loading of BL-Mnt. The retention of tensile strength was 99% after thermal oxidative aging in an air-circulating oven for 72 h at 100°C. Evidence indicated that ECO/BL-Mnt composites with good mechanical properties and thermo-oxidative aging properties were obtained.

To apply hydrotalcites more effectively to the problem of dye wastewater, the effects of divalent metal ions on the structure and stability of hydrotalcites, especially on their photocatalytic activity, were compared. In the present study, M/Cr hydrotalcites (M3Cr-CO3-LDHs) (in which M = Mg, Co, Ni, Cu, Zn), where the M/Cr molar ratio was 3, were prepared by the co-precipitation method. The structures and properties were characterized using powder X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), thermogravimetric-differential thermal analysis (TG-DTA), and UV-Visible diffuse reflectance spectroscopy (UV-Vis DRS). The results showed that five kinds of M3Cr-CO3-LDHs were synthesized successfully, and the layered structure of the samples obtained was regular and the crystal phase was single. When methylene blue (MB) solution was exposed to ZnCr-CO3-LDHs, H2O2, and visible light irradiation, more than 90.67% of the methylene blue (MB) was removed after 140 min. The photocatalytic activity of the samples was in the order: Co3Cr-CO3-LDHs > Mg3Cr-CO3-LDHs > Cu3Cr-CO3-LDHs > Zn3Cr-CO3-LDHs > Ni3Cr-CO3-LDHs. The results of a catalytic mechanism study showed that photocatalytic degradation of MB involved a demethylation reaction, with the reactive species containing •O2-, •OH, and h+.

Photo-assisted selective catalytic reduction (photo-SCR) has been considered as a promising strategy for NOx removal in recent decades. The purpose of the present work was to test the effectiveness of La1–xPrxCoO3, supported on the surface of natural palygorskite (Pal) by a facile sol-gel method, as a photo-SCR for the removal of NOx from wastewaters. The structure, acidity, and the redox property of the prepared La1–xPrxCoO3/Pal nanocomposite were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), UV-Visible diffuse reflectance spectroscopy (UV-Vis DRS), and X-ray photoelectron spectroscopy (XPS). Density functional theory (DFT) calculations were employed to determine the valence bands. The La1–xPrxCoO3/Pal catalysts were then tested for SCR removal of NOx with the assistance of photo-irradiation. The photo-SCR results revealed that the NOx conversion and the N2-selectivity were greatly improved by this method and reached >95% when carried out at the relatively low temperature of 200°C and with the Pr doping at x = 0.5. The improvements were attributed to the co-precipitation of a PrCoO3 phase as in a solid solution forming a coherent heterojunction of PrCoO3/La0.5Pr0.5CoO3 on the Pal surface.

Chitosan (CTS) modified montmorillonite (Mnt) composites (CTS-Mnt), which have been widely reported for the adsorption of heavy-metal ions and biological dyes, have not been applied to the field of mycotoxin adsorption. The current study was focused on the preparation of CTS-Mnt by calcination as a mycotoxin adsorbent for the efficient removal of aflatoxin B1 (AFB1). The CTS-Mnt samples obtained were characterized using X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and nitrogen adsorption/desorption analysis. The CTS-Mnt samples prepared at various calcination temperatures exhibited varying structural configurations, surface hydrophobicities, and texture properties. The results revealed that stable CTS-Mnt speciments, obtained at <350°C, displayed superior adsorption capacity for AFB1 from a simulated gastrointestinal tract, increasing from 0.51 mg/g of raw Mnt to 4.97 mg/g. With increased calcination temperature, the effect of pH on the adsorption process of AFB1 becomes negligible. This study demonstrates that the novel CTS-Mnt has tremendous potential as an AFB1 adsorbent.