Effects of Surface Preparation on Epitaxial GaN on 6H-SiC Deposited Via MOCVD

Published online by Cambridge University Press:  13 June 2014

Z. Y. Xie
Affiliation:
Department of Chemical Engineering, Kansas State University, Manhattan, KS 66506
C. H. Wei
Affiliation:
Department of Chemical Engineering, Kansas State University, Manhattan, KS 66506
L. Y. Li
Affiliation:
Department of Chemical Engineering, Kansas State University, Manhattan, KS 66506
J. H. Edgar
Affiliation:
Department of Chemical Engineering, Kansas State University, Manhattan, KS 66506
J. Chaudhuri
Affiliation:
Department of Mechanical Engineering, Wichita State University, Wichita, KS 67208
C. Ignatiev
Affiliation:
Department of Mechanical Engineering, Wichita State University, Wichita, KS 67208

Abstract

A comparison was made of 6H-SiC surfaces etched with H2, C2H4/H2, and HCl/H2, and the resulting crystal quality of epitaxial GaN films deposited on these substrates. To remove the many fine scratches and to smooth the rough surfaces typical of commercial SiC substrates, the Si-face 6H-SiC substrates were etched in H2, C2H4/H2, and HCl/H2 at 145 °C. GaN was subsequently deposited on these etched surfaces after first depositing a low temperature GaN buffer layer via metalorganic chemical vapor deposition (MOCVD). The surface morphologies after etching and after GaN deposition were characterized by atomic force microscopy and Normaski differential interference contrast microscopy, while the crystal quality of the GaN films was assessed by double crystal x-ray rocking curves and x-ray topography. 6H-SiC substrate surfaces were improved in terms of the removal of scratches and the reduction of surface roughness, and both surface morphology and crystal quality of the subsequently deposited GaN films were enhanced. However, the dislocation density was not decreased by the surface etching. The best GaN film was produced by etching the substrate in pure H2 for 40 minutes before growth. Recommendations for the optimum substrate treatment are made.

Type
Research Article
Copyright
Copyright © 1999 Materials Research Society

Introduction

GaN has long been a promising material for optoelectronic devices operating in the blue to ultra-violet region [Reference Jacob, Boulou and Bios1-Reference Amano, Sawaki, Akasaki and Toyoda2], but the lack of GaN bulk crystals hinders the improvement of GaN epitaxial film quality. Sapphire is the most common substrate for GaN epitaxy, but because of large differences in lattice constants(13.8%) and thermal expansion coefficients(25.4%), the threading dislocation density is typically high in the GaN film. In contrast, 6H-SiC has a smaller lattice mismatch (3.5%) with GaN, making it a better candidate for GaN growth [Reference Lin, Sverdlov, Zhou and Morkoc3].

High quality GaN was successfully deposited on 6H-SiC substrates via MOCVD by several groups [Reference Tanaka, Iwai and Aoyagi4-Reference Lin, Cheng, Chi, Feng, Guo, Hong and Chen6], but no detailed investigation of the effects of the 6H-SiC substrate surface treatment prior to GaN growth has been reported. Compared to sapphire, the surface quality of commercial 6H-SiC substrates is poor, containing various defects that may deteriorate the quality of epitaxial layer. Some defects, such as dislocations, and micropipes (holes approximately a micrometer in diameter) originate in the bulk of the substrate, while other defects such as ridges and scratches result from the lapping and polishing process. The later defects can be almost fully removed by etching the surface with hydrogen, with or without propane or HCl [Reference Powell, Larkin and Abel7-Reference Hallin, Owman, Mårtensson, Ellison, Konstantinov, Kordina and Janzén8]. In the case of SiC epitaxy, defects in the film propagating from the substrate are minimized by in situ etching of substrates [Reference Powell, Larkin and Abel7-Reference Hallin, Owman, Mårtensson, Ellison, Konstantinov, Kordina and Janzén8]. Furthermore, to avoid the formation of double position boundaries(DPB), 6H-SiC (off-axis) are etched and annealed to produce surface step heights corresponding to an integral multiple of the 6H-SiC unit cell (15 Å) [Reference Owman, Hallin, Mårtensson and Janzén9-Reference Smith, Tsen, Sverdlov, Martin and Morkoc10]. The effect of the substrate is expected to be similar for GaN, hence, much attention should be given both to growth conditions and surface preparation of 6H-SiC for GaN epitaxial growth.

In this letter, we studied the etching of 6H-SiC substrates using H2, C2H/H2, and HCl/H2 to remove scratches and pits. The quality of the substrtate surfaces thus produced were characterized, then GaN films were epitaxially deposited on these substrates. Finally, GaN films were examined, and a correlation between the surface treatment and film quality, both bulk structure and surface features, was developed.

Experiment

Substrate etching was performed in a cold-wall horizontal quartz reactor with an inside diameter of 50 mm operated at atmospheric pressure. The substrates were heated by a boron nitride coated graphite susceptor, and their temperature was measured both with an optical pyrometer and an R-type thermocouple, which were calibrated by the melting point of Si. The substrates were n-type, on-axis Si-face 6H-SiC (0001) wafers. Prior to etching, the substrates were ultrasonically degreased in organic solvents, dipped in 10% HF acid, and rinsed in deionized water. The etching temperature was fixed at 1450 °C for all experiments, and the other experimental conditions were summarized in Table I.

Table I. Summary of on-axis Si-face 6H-SiC (0001) substrate etching conditions.

Sample Etching Time (mins) FWHM of DCX (arcsec)
1 no treatment N/A 423
2 H2 etching 10 395
3 H2 etching 40 378
4 100 ppm C2H4/H2 etching 40 398
5 0.5% HCl/H2 etching 10 418

The subsequent growth of GaN was performed in a vertical-type MOVPE reactor operated at low pressure (76 Torr). Before loading into the reactor, the etched substrates were also degreased and dipped in HF acid. Trimethylgallium (TMG) and ammonia (NH3) were the Ga and N sources, and Pd-cell purified H2 was used as the carrier gas. The substrates in table I were loaded into the reactor simultaneously for one run, and preheated at 1100 °C for 10 minutes in H2 for surface cleaning using a rf induction heater. To compare the effects of substrate etching on the subsequent GaN growth, the experimental conditions were the same for each run, and all deposits had a GaN buffer layer deposited at 550 °C.

The resulting etched 6H-SiC surfaces and the final GaN films were characterized by Nomarski differential interference contrast microscopy (NDIC) and atomic force microscopy (AFM). The quality of the GaN films was assessed by X-ray double crystal rocking curves and X-ray double crystal topography.

Results and Discussion

The AFM image of an as-received on-axis Si-face 6H-SiC substrate shows randomly oriented scratches, varying in depth and width (Fig. 1a). Some extreme scratches were broad (∼200 nm) and deep (10 nm), and disturbed the nucleation and surface morphology of the GaN film. Other defects such as micropipes and epitaxial pits were also observed (not shown). However, after etching 10 minutes in H2, the scratches began to disappear, and a periodic texture in one direction ([1-100]) of roughly parallel ridges formed as seen in Fig. 1b. The large shallow trench caused by a nonuniform etching rate on the (0001) surface at an early stage of etching. After etching for 40 minutes, the surface became smoother, and the scratches were completely removed (Fig. 1c). The terrace pattern was clear with a wider terrace (approximately 0.5 µm) than that (0.2 µm) in Fig. 1b. The etching behavior of C2H4/H2 mixture was similar to the H2 with a slightly slower etch rate. The width and smoothness of the terraces from C2H4/H2 etching were narrower and rougher than those for H2 etching due to the low etching rate. Fig. 1d shows the surface after etching in 0.5% HCl/H2 for 10 minutes. Although the etch rate was higher, the residual scratches interrupted by terraces were still observed because of a short etching time. In terms of surface root mean square (RMS) values, the surface roughness was reduced from approximately 1.85 nm to below 1.0 nm for all etched 6H-SiC surfaces with a best surface morphology for H2 etching for 40 minutes.

Figure 1. AFM images of 6H-SiC substrates, (a) as-received, no treatment, (b) after H2 etching for 10 mins, (c) after H2 etching for 40 mins, (d) after 0.5 % HCl/H2 etching for 10 mins.

Our 6H-SiC etching results were largely consistent with other groups [Reference Hallin, Owman, Mårtensson, Ellison, Konstantinov, Kordina and Janzén8, Reference Karisson and Nordell11] with the exception that no well-defined straight step structure was observed, which we contributed to the low etching temperature. Nevertheless, most scratches were removed using the above etching method, and the improved surfaces were obtained.

The resulting GaN films had mirror-like surfaces as observed by the naked eye. However, some interesting features were illuminated by Normaski differential interference contrast microscopy. Fig 2a is the surface of the GaN film deposited on the untreated 6H-SiC substrate. There is a high density of cracks, caused by the residual stress for the heteroepitaxial growth [Reference Hiramatsu, Detchprohm and Akasaki12-Reference Nakamura13], between which very smooth GaN surfaces dominate. A relatively high density (1.6×103/cm2) of pits or pinholes (nominally 5 μm in diameter) was mostly distributed along the cracks or at crack intersections. When GaN was deposited on the substrate etched by H2 for 40 minutes, the resulting GaN surface was similar to that in Fig. 2a, except that the density of pits decreased by a factor of four (4.0×102/cm2), and the pit diameter also decreased to 3 μm. Regardless of which etch was used, the density of pinholes was decreased compared to that of the untreated substrate surface.

Figure 2. NDIC images of GaN films grown on 6H-SiC substrates, (a) as-received, no treatment, (b) after H2 etching for 40 mins. Magnification: 200X

What caused these pits? To answer this question, we compared our GaN surface morphologies with those obtained by other groups. Weeks et al. [Reference Weeks, Bremser, Ailey, Carlson, Perry, Piner, El-Masry and Davis5] deposited GaN thin films on vicinal and on-axis 6H-SiC (0001) substrates using high temperature AlN buffer layers. Many small pits (nominally 30 nm in diameter) were observed, and the pit density was decreased by increasing the AlN deposition temperature. Random pinholes were also seen on the resulting GaN surfaces, and the density was decreased by increasing the GaN growth temperature. This phenomena was attributed to the possibly incomplete coalescence of GaN. Our observations were consistent with their results; however, the density of the pits increased when the 6H-SiC substrate surface quality was poor. The density and size of pits were increased greatly (5.3×103/cm2 and 7.5 μm in diameter respectively) when a high density of etch pits was intentionally introduced on the substrate surface after the etching of the 6H-SiC substrate in 2% HCl/H2 for 30 minutes at 1450 °C. Therefore, the incomplete coalescence of GaN was attributed to the micropipes or deep pits originating on the 6H-SiC substrate surface. GaN nucleation on these defects is difficult; if nucleation does occur, the GaN can not fill the defects, and leaves the GaN can not completely coalesce on these defects. Not only circular defects (pits or holes), but also wide and deep scratches can cause the incomplete coalescence of GaN films. Fig. 3a shows GaN surfaces separated by several deep and large scratches. The rough GaN surface was due to the unoptimized growth condition. The side walls of scratches on the 6H-SiC substrates have different orientations, which results in low growth rate or growth direction not parallel to c-axis, compared to the growth on the basal plane of (0001). Sometimes, even shallow scratches disturbed the nucleation and growth of GaN. As shown in Fig. 3b, the GaN growth pattern was disturbed by the scratches with concentrated steps grown along the scratches. The reason of the resulting pinholes on GaN films will be further studied and presented in another paper.

Figure 3. NDIC images of GaN film surfaces, (a) incomplete coalescence of GaN film separated by the substrate scratches, (b) the GaN film surface was disturbed by the scratches. Magnification: 400X.

Table I. displays the FWHM of the resulting GaN films deposited on the substrates etched at different conditions. The results are consistent with surface quality as evaluated by AFM. The FWHM of the GaN film grown on as-received substrate (sample1) had highest value, and thus the poorest crystal quality. The FWHM decreased with the increasing of H2 etching time (sample 2 and 3). The crystal quality of the GaN film deposited on sample 4 was between sample 2 and 3 due to the slower etching rate with the adding of C2H4. The last sample (sample 5) had a FWHM value close to sample 1, since the residual surface scratches were not completely removed. Although the FWHM has high values caused by unoptimized growth conditions, these values are comparable to each other because they were deposited in the same run. As a result, the GaN deposited on the 40 minute H2 etched substrate has the best quality, which is consistent with the AFM results.

An x-ray double crystal topograph was performed on sample 3. The reflection direction was [00.2]. The low angle grain boundaries were clearly identified to be repeated in the film. Linear defects were screw and mixed dislocations, which are common both in SiC substrates and GaN films. There is no evident difference between GaN samples deposited on untreated or etched 6H-SiC substrates. Dislocation defects presents in the substrates would propagate into epitaxial film, and can not been removed by the etching method.

Conclusions

In summary, the as-received commercial 6H-SiC substrates were etched using H2, C2H4/H2, and HCl/H2 with a best surface improvement for the etching in H2 for 40 minutes. The surface morphologies of those samples deposited on the etched substrates improved in terms of the decreasing of the pinhole density. These pinholes and other defects were attributed to the scratches, micropipes, and pits originating on the as-received 6H-SiC substrates. The crystal quality was increased as measured by DCX. However, the density of dislocation was not decreased by the substrate surface etching. The optimized etching condition is a 40-minute H2 etching at 145 °C which was verified by the resulting GaN film surface morphology, and narrowing of FWHM of DCX. The improvement of GaN films in surface morphology and crystal quality is a direct result of the improved substrate surfaces. Therefore, the surface etching of 6H-SiC is an effective way to improve the quality of GaN epitaxial films until the surface defects of as-received 6H-SiC substrates are reduced.

Acknowledgments

The authors gratefully acknowledge financial support by National Science Foundation (NSF) grant number DMR-9627333.

Footnotes

MRS Internet J. Nitride Semicond. Res. 4S1, G3.39(1999)

References

Jacob, G., Boulou, M., and Bios, D., J. Lumin. 17, 263 (1978).Google Scholar
Amano, H., Sawaki, N., Akasaki, I., and Toyoda, Y., Appl. Phys. Lett. 48, 353 (1986).Google Scholar
Lin, M. E., Sverdlov, B., Zhou, G. L., and Morkoc, H., Appl. Phys. Lett. 62, 3479 (1993).Google Scholar
Tanaka, S., Iwai, S., and Aoyagi, Y., J. Cryst. Growth 170, 329 (1997).CrossRefGoogle Scholar
Weeks, T. W. Jr., Bremser, M. D., Ailey, K. S., Carlson, E., Perry, W. G., Piner, E. L., El-Masry, N. A., and Davis, R. F., J. Mater. Res. 11 (4), 1011 (1996).Google Scholar
Lin, C. F., Cheng, H. C., Chi, G. C., Feng, M. S., Guo, J. D., Hong, J. M., and Chen, C. Y., J. Appl. Phys. 82 (5), 2378 (1997).Google Scholar
Powell, J. A., Larkin, D. J., and Abel, P. B., J. Electron. Mater.24, 295 (1995).Google Scholar
Hallin, C., Owman, F., Mårtensson, P., Ellison, A., Konstantinov, A., Kordina, O., and Janzén, E., J. Cryst. Growth, 181 241 (1997).Google Scholar
Owman, F., Hallin, C., Mårtensson, P., and Janzén, E., J. Cryst. Growth 167, 391 (1996).Google Scholar
Smith, D. J., Tsen, S.-C. Y., Sverdlov, B. N., Martin, G., and Morkoc, H., Solid-State Elec. 41 (2), 349 (1997).CrossRefGoogle Scholar
Karisson, S., and Nordell, N., Mater. Sci. Forum 264-268, 363 (1998).Google Scholar
Hiramatsu, K., Detchprohm, T., and Akasaki, I., Jpn. J. Appl. Phys. 32, 1528 (1993).CrossRefGoogle Scholar
Nakamura, S., J. Cryst. Growth 170, 11 (1997).Google Scholar
Figure 0

Table I. Summary of on-axis Si-face 6H-SiC (0001) substrate etching conditions.

Figure 1

Figure 1. AFM images of 6H-SiC substrates, (a) as-received, no treatment, (b) after H2 etching for 10 mins, (c) after H2 etching for 40 mins, (d) after 0.5 % HCl/H2 etching for 10 mins.

Figure 2

Figure 2. NDIC images of GaN films grown on 6H-SiC substrates, (a) as-received, no treatment, (b) after H2 etching for 40 mins. Magnification: 200X

Figure 3

Figure 3. NDIC images of GaN film surfaces, (a) incomplete coalescence of GaN film separated by the substrate scratches, (b) the GaN film surface was disturbed by the scratches. Magnification: 400X.