Synthesis and Sintering Characteristics of TiC – Ni – Ti – (Al) Nanocomposites

Published online by Cambridge University Press:  21 March 2011

Kai Vohwinkel  and
Rasit Koc
Kai Vohwinkel
Affiliation:
Department of Mechanical Engineering and Energy Processes, Southern Illinois University at Carbondale, Carbondale, IL 62901, USA
Rasit Koc
Affiliation:
Department of Mechanical Engineering and Energy Processes, Southern Illinois University at Carbondale, Carbondale, IL 62901, USA
Get access

Abstract

The sintering behavior of submicron / nanosize TiC powders was investigated. The TiC powders (31 wt.% carbon) are synthesized from a carbon coated precursor and have excess carbon content. Ti, Ni and Al powders were added to have in-situ intermetallic binders for sintering. The composition TiC-5 wt.% Ti (pellet 1) shows pure TiC in the XRD analysis after sintering. The composition TiC-30 wt.% Ni3Al (pellet 3) shows the formation of the liquid phase Ni3Al. No liquid phase can be clearly identified in the XRD pattern of pellet 2 (TiC-30 wt.% Ni3Ti). However the SEM micrograph of pellet 2 shows similarity to the SEM image of pellet 3 concerning the formation of liquid phase.

Pellets 1 and 2 show densifications of 100 % TD (theoretical density), whereas pellet 3 is only 90 % TD. Pellet 3 has the highest hardness (2511 HV) and fracture toughness (12.08 MPa m1/2).

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 676: Symposium Y – Synthesis, Functional Properties and Applications of Nanostructures , 2001 , Y3.22
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] “Sintering properties of submicron TiC powders from carbon coated titania precursor”, Koc, R., Meng, Chang, Swift, G. A., J. of Materials Science, 35, 3131–3141, 2000 Google Scholar
[2] “Development of high toughness, high strength aluminide-bonded carbide ceramics” Becher, Paul F., Plucknett, Kevin P., Tiegs, Terry N., Schneibel, Joachim H. and Subramanian, Ramesh, Advanced Industrial Materials (AIM) Program, Annual Progress Report, FY 1996 Google Scholar
[3] Koc, R. and Glatzmaier, G., U. S. Patent Ni: 5,417,952 (1995)Google Scholar