Preparing Titania Fibers and Their Photocatalytic Activity

Published online by Cambridge University Press:  15 February 2011

H. Koike ,
Y. Oki  and
Y. Takeuchi
H. Koike
Affiliation:
Basic Chemicals Research Laboratory, Sumitomo Chemical Co., Ltd., Ehime, JAPAN
Y. Oki
Affiliation:
Basic Chemicals Research Laboratory, Sumitomo Chemical Co., Ltd., Ehime, JAPAN
Y. Takeuchi
Affiliation:
Basic Chemicals Research Laboratory, Sumitomo Chemical Co., Ltd., Ehime, JAPAN
Get access

Abstract

Continuous titania fibers were prepared by a polytitanoxane precursor method. Polytitanoxane was synthesized through hydrolysis and polymerization reaction between partially chelated titanium isopropoxide and water without acid catalyst. Polytitanoxane, which was precipitated from an isopropanol solution by adding adequate amount of water to titanium isopropoxide, was then dried and dissolved in tetrahydrofuran. The concentrated viscous solution of polytitanoxane was considerably stable to further self-condensation and had good spinnability. The precursor fiber which was obtained by spinning the solution was calcined to form titania fibers.

Two types of titania fibers were obtained under different calcination conditions from the same precursor fiber; Dense fiber with high tensile strength of higher than 1 GPa, and porous fiber with high surface area of more than 10 m2/g.

Photocatalytic activity of those fibers was studied using the phenol mineralization reaction in water. The phenol degradation ability of high-surface-area titania fiber was almost the same as that of commercial titania powder for photocatalyst.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 549: Symposium FF – Advanced Catalytic Materials - 1998 , 1998 , 141
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Sakka, S. in Sol-gel Technology for Thin Films, Fibers, Preforms, Electronics and Specialty Shapes, edited by Klein, L.C. (Noyes Publications, Park Ridge, N.J., 1988), p. 140–161.Google Scholar
2. Kamiya, K., Tanimoto, K., and Yoko, T., J. Mat. Sci. Lett., 5, p.402–404 (1986).Google Scholar
3. Gunji, T., Nagao, Y., Misono, T., and Abe, Y., J. Polym. Sci. part A, 29, p.941–947 (1991).Google Scholar
4. Hoffmann, M., Martin, S., Choi, W., and Bahnemann, D., Chem. Rev., 95, p.69–96 (1995).Google Scholar
5. Brezová, V., Blažkovd, A., Brezňan, M., Kottáš, P., and Ćeppan, M., Collect. Czech. Chem. Commun., 60, p.788–794 (1995).Google Scholar