The incorporation of triturated tire particles as an aggregate in the concrete mixture is one of the ways to take advantage of this Waste Rubber (WR) in order to improve concrete properties, such as mechanical behavior. In this research we evaluated mechanical behavior of concrete specimens prepared with different amounts WR, which partially substituted the fine aggregate, under an indirect tensile test. In contrast with other’s researcher’s findings, our results show that the specimens with 5% WR present the highest value of indirect tensile strength (TP) of 4.36 MPa. Polynomial relationships between TP and compression strength (f´c), where Tp ranges from 0.1f´c to 0.2f´c. Specimens with the 0, 5 and 10% WR content show two types of failure: normal tension and tiple-cleft failure, described in the norm ASTM 1144-89. Nevertheless, specimens with 15 and 20% WR show a new failure not described in the norm, which is thought to be occurring due to the high amount of WR used.

A new generation of cementitious materials is being engineered to selectively inhibit the growth of Acidithiobacillus, which are a key genera of acid-generating bacteria responsible for microbially induced concrete corrosion (MICC). In this context, the substitution of metal-laden granular activated carbon (GAC) particles and/or steel slag for a fraction of the fine aggregates traditionally used in concrete mixture has proven useful. While the antimicrobial properties of specific heavy metals (i.e. copper and cobalt) have been leveraged to inhibit acid-generating bacteria growth on sewer pipes, few studies have researched how biocidal aggregates may affect the microstructural and mechanical properties of cementitious materials. We report here on the effects that these biocidal aggregates substitutions can have on compressive strength, flowability, and setting times of cement-based formulations. Results showed that increases in compressive strength, regardless of the presence or absence of biocidal metals, resulted from the GAC incorporation where sand replacement was 3% by mass or lower, while flowability decreased when percentages higher than 3% of GAC was incorporated in a cement mix. When substituting fine aggregate with steel slag particles in mass ratios between 5% and 40%, compressive strength was not affected, regardless of the presence or absence of copper. Setting times were not affected by the inclusion of GAC or steel slag particles except when substituting GAC particles at 10% of the fine aggregate mass; under this condition both initial and final setting times were decreased. Results suggest that in order to have enhanced inhibition potential against acidophilic microorganisms and equal or improved mechanical properties, a combination of 1% metal-laden GAC and 40% copper-laden steel slag is an optimum fine aggregate substitution scenario.

Geopolymeric mortars with volumetric fractions of 0.6:1:0.3 for a binder powder, fine sand and sodium hydroxide solution (12M), respectively; have been fabricated by mixing the solid materials and the subsequent addition of sodium hydroxide solution 12M to form a workable paste, to later be cured for 28 days at room temperature. The microstructures of the fabricated materials reveal the existence of two phases with notable difference, one continuous to the geopolymer binder phase and another discontinuous of fine sand particles agglutinated by the binder phase. Mechanical compression tests are performed at a constant compression rate of 0.05 mm/min and at temperatures ranged from room temperature to 500°C. The mechanical results are ranged from 19 and 69 MPa for all the materials studied. On the other hand, there was an increase in mechanical resistance up to test temperatures of 200°C and the progressive reduction of resistance at temperatures above 200°C, with a fragile-ductile transition zone between 400 and 500°C and completely ductile behavior from test temperatures of 500°C.

This paper presents a novel way to obtain reinforced pores by the dissociation of mixed carbides during sintering. Porous materials have a wide range of applications such as dampeners, light structures, etc. But usually pores act as points of stress concentration and crack nucleation, harming the mechanical properties of these materials. Methods have been developed to control the shape and size of pores but, until now, there are no techniques that allow reinforcing the material around the pores. To address this, steels were prepared by adding 1, 3 and 5 wt.% of Mo1.5Cr0.5C mixed carbide particles to a iron matrix by metal injection moulding. The results showed that during sintering, the dissociation of the carbide followed by the dissolution of the elements in the matrix generated rounded secondary pores with a reinforced vicinity, which increased the mechanical strength of the materials. The presence of rounded pores encircled by an enriched vicinity can allow the production of porous materials with exceptional fatigue strength and fracture toughness.

The constant search for the improvement of the performance of materials of industrial application, evaluated under aspects of weight reduction, greater resistance, greater resistance to wear and better thermal stability, among others, associated with the search for the development of ecologically viable products, that convert the context of environmental degradation in preservation and sustainability, reflects the need to conduct research that results in new materials. The objective of this work is to obtain composites of the AA6061 aluminum alloy reinforced with different contents of coke coal blast-furnace slag by powder metallurgy. The processing of these materials was done by sieving, mixing and compacting powders of reinforced aluminum alloy with 5, 10 and 15% of blast-furnace slag. The cold uniaxial compaction was realized at a pressure of 500MPa. The obtained materials were sintered at 580°C for 3h under inert atmosphere. Unreinforced aluminum alloy samples were also produced. The characterization of the materials was realized by density and hardness measurements and three-point bending tests. The analysis of its microstructure was realized by scanning electron microscopy. As results, the composites presented a homogeneous distribution of the reinforcing particles and also a progressive improvement of the hardness and the bending strength with the increase of the slag content, producing an increase of 79% in hardness and 128% in flexural strength, when compared to the material without reinforcement obtained by the same process. Such results give the coke coal blast-furnace slag a new possibility of exploitation in the metal-mechanical sector, besides contributing with the environmental issue.

A method for the fabrication of interconnected ceramic sponges was used in the present work, designed by using a combination of two different, aqueous gel casting and sacrificial template, using aluminum nitride powder (99.97%) with a mean size of 2.4 micrometers. Two types of sponges were made by using two different monomers, acrylamide and methacrylamide, the resultants sponges have 60% of porosity after being sintered and pyrolyzed at temperature of 1673 K using an inert atmosphere of argon for 1 h. The hydrolysis evolution of this ceramic powder during the gelcasting process was studied by measuring the pH during the stirring time, the microstructure changes during the time of exposure were observed in a SEM. XRD were made to study the present phases after the gel was eliminated by thermal treatment at 873 K using an oxidizing atmosphere, observing a formation of up to 4 %wt. of cubic alumina phase which was made after the hydrolysis products. Infrared spectroscopy was used to study the changes in the ceramic powder.