Recristallisation dynamique d’alliages à basse densité fer-aluminium*

Published online by Cambridge University Press:  04 November 2011

C. Castan ,
F. Montheillet  and
A. Perlade
C. Castan
Affiliation:
ArcelorMittal, R&D Packaging, Voie Romaine, BP 30320, 57283 Maizières-lès-Metz Cedex, France. e-mail : [email protected]
F. Montheillet
Affiliation:
École des Mines, Centre SMS, CNRS UMR 5146, 158 Cours Fauriel, 42023 St-Etienne Cedex 2, France; e-mail : [email protected]
A. Perlade
Affiliation:
ArcelorMittal, R&D Automotive Products, Voie Romaine, BP 30320, 57283 Maizières-lès-Metz Cedex, France; e-mail : [email protected]
Get access

Abstract

Les alliages ferritiques Fe-8 %Al possèdent des propriétés physiques et mécaniques prometteuses pour le développement et la conception de nouveaux types d’aciers allégés. Ces alliages présentent cependant des défauts de surface appelés « roping », apparaissant après l’étape d’emboutissage à froid. La formation de ces défauts est principalement attribuée à la distribution hétérogène des orientations des grains. Dans cette étude, les effets de la quantité de déformation, de la vitesse de déformation et de la température ont été examinés en utilisant la torsion à chaud. Les essais ont été réalisés à des températures comprises entre 900 °C et 1100 °C et des vitesses de déformation comprises entre 0,1 s-1 et 10 s-1. Il a été montré que deux types de recristallisation dynamique pouvaient intervenir durant la déformation à chaud : la recristallisation dynamique continue et la recristallisation dynamique discontinue.

Keywords

Aciers ferritiques allégésalliages fer-aluminiumropingrecristallisation dynamique continuerecristallisation dynamique discontinueLightweight steelsiron-aluminium alloysropingcontinuous dynamic recrystallizationdiscontinuous dynamic recrystallization
Type
Research Article
Information
Metallurgical Research & Technology , Volume 108 , Issue 3 , 2011 , pp. 141 - 153
Copyright
© EDP Sciences, 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Références

G. Frommeyer, E.J. Drewes, B. Engl, Physical and mechanical properties of iron-aluminium-(Mn, Si) lightweight steels, La Revue de Métallurgie, 2000, pp. 1245-1253
F. Montheillet, Métallurgie en mise en forme à chaud, Techniques de l’ingénieur, M 3 031
Holt, D.L., J. Appl. Phys. (1970) 3197-3201
Amelinckx, A., Dekeyser, W., Solid State Physics 8 (1959) 325-499
Montheillet, F., Springer Wien New York (2004) 203-256
J. Baczynski, J.J. Jonas, Texture development during the torsion testing of ff-iron and two IF steels, Acta Materialia, 1996, pp. 4273-4288
Lim, S.M., El Wahabi, M., Desrayaud, C., Montheillet, F., Mater. Sci. Eng. 460-461 (2007) 532-541
MacKenzie, J.K., Biometrika 45 (1958) 229-240
Glover, G., Sellars, C.M., Metall. Trans. 4 (1973) 765-775
Tsuji, N., Matsubara, Y., Saito, Y., Scripta Materialia 37 (1997) 477-484
Narayana Murty, S.V.S., Torizuka, S., Nagai, K., Kitai, T., Kogo, Y., Scripta Materialia 53 (2005) 763-768
Hinton, J.S., Beynon, J.H., ISIJ Int. 47 (2007) 1465-1474
Chovet, C., Gourdet, S., Montheillet, F., Mater. Trans. 41 (2000) 109-112