Tensile, fatigue, and corrosion fatigue behavior of high performance die cast aluminum alloy

Published online by Cambridge University Press:  05 March 2015

Zuqi Hu  and
Shusen Wu
Zuqi Hu*
Affiliation:
Material Institution of China Academy of Engineering Physics, Mianyang 621900, People's Republic of China
Shusen Wu
Affiliation:
State Key Lab of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, People's Republic of China
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

High performance die castings are urgently expected to be used as structural components subjected to dynamic loading. Therefore, tensile properties, fatigue, and corrosion-fatigue behavior of automotive die cast AlMg5Si2Mn alloy are studied in the current work. The results indicate that the tensile strength and yield strength of the as-cast specimens are obviously lower than those of the age-treated specimens, while the elongation decreases with increasing aging time. Neutral corrosive environment (3.5% NaCl solution) dramatically decreases the fatigue limits from 75 to 50 MPa. Fatigue lives of the directly corroded and precorroded specimens are close to each other. The values of material constants m and C are in the range of 5.756–5.874 and 2.421 × 10−10 to 4.285 × 10−9, respectively. Obscure fatigue striations and featureless facets are observed in crack propagation regions. Anodic dissolution is dominantly responsible for the premature crack initiation and stress corrosion cracking leading to the formation of fractured α-Al matrix.

Keywords

high pressure die castingaluminum alloycrack initiationcrack growth mechanismstress corrosion cracking
Type
Articles
Information
Journal of Materials Research , Volume 30 , Issue 6 , 28 March 2015 , pp. 833 - 840
Copyright
Copyright © Materials Research Society 2015 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Brungs, D.: Light weight design with light metal castings. Mater. Des. 18(4–6), 285 (1997).CrossRefGoogle Scholar
Cole, G.S. and Sherman, A.M.: Light weight materials for automotive applications. Mater. Charact. 35(1), 3 (1995).CrossRefGoogle Scholar
Kaufmann, H. and Uggowitzer, P.J.: Fundamentals of the new rheocasting process for magnesium alloys. Adv. Eng. Mater. 3(12), 963 (2001).3.0.CO;2-X>CrossRefGoogle Scholar
Kaufmann, H. and Uggowitzer, P.J.: Metallurgy and Processing of High-Integrity Light Metal Pressure Castings (Schiele & Schön, Germany, 2007).Google Scholar
Hu, Z., Wan, L., Wu, S., Wu, H., and Liu, X.: Microstructure and mechanical properties of high strength die-casting Al–Mg–Si–Mn alloy. Mater. Des. 46, 451 (2013).CrossRefGoogle Scholar
Ji, S., Watson, D., Fan, Z., and White, M.: Development of a super ductile diecast Al–Mg–Si alloy. Mater. Sci. Eng., A 556, 824 (2012).CrossRefGoogle Scholar
Otarawanna, S., Gourlay, C.M., Laukli, H.I., and Dahle, A.K.: The thickness of defect bands in high-pressure die castings. Mater. Charact. 12(60), 1432 (2009).CrossRefGoogle Scholar
Otarawanna, S., Gourlay, C.M., Laukli, H.I., and Dahle, A.K.: Formation of the surface layer in hypoeutectic Al-alloy high-pressure die castings. Mater. Chem. Phys. 130(1–2), 254 (2011).CrossRefGoogle Scholar
Wan, L., Hu, Z., Wu, S., and Liu, X.: Mechanical properties and fatigue behavior of vacuum-assist die cast AlMgSiMn alloy. Mater. Sci. Eng., A 576, 252 (2013).CrossRefGoogle Scholar
Hu, Z., Wan, L., Lü, S., Zhu, P., and Wu, S.: Research on the microstructure, fatigue and corrosion behavior of permanent mold and die cast aluminum alloy. Mater. Des. 55, 353 (2014).CrossRefGoogle Scholar
Chlistovsky, R.M., Heffernan, P.J., and DuQuesnay, D.L.: Corrosion-fatigue behaviour of 7075-T651 aluminum alloy subjected to periodic overloads. Int. J. Fatigue 29(9–11), 1941 (2007).CrossRefGoogle Scholar
Zupanc, U. and Grum, J.: Effect of pitting corrosion on fatigue performance of shot-peened aluminium alloy 7075-T651. J. Mater. Process. Technol. 210(9), 1197 (2010).CrossRefGoogle Scholar
Jones, K. and Hoeppner, D.W.: Prior corrosion and fatigue of 2024-T3 aluminum alloy. Corros. Sci. 48(10), 3109 (2006).CrossRefGoogle Scholar
Paris, P. and Erdogan, F.: A critical analysis of crack propagation laws. J. Basic Eng. 4(85), 528 (1963).CrossRefGoogle Scholar
Suresh, S.: Fatigue of Materials (Cambridge University Press, England, 1991); pp. 95.Google Scholar
Lados, D.A., Apelian, D., Jones, P.E., and Major, J.F.: Microstructural mechanisms controlling fatigue crack growth in Al–Si–Mg cast alloys. Mater. Sci. Eng., A 468–470, 237 (2007).CrossRefGoogle Scholar
Venkateswaran, P., Ganesh Sundara Raman, S., Pathak, S.D., Miyashita, Y., and Mutoh, Y.: Fatigue crack growth behaviour of a die-cast magnesium alloy AZ91D. Mater. Lett. 58(20), 2525 (2004).CrossRefGoogle Scholar
Elber, W.: Fatigue crack closure under cyclic tension. Eng. Fract. Mech. 2(1), 37 (1970).Google Scholar
Yi, J.Z., Gao, Y.X., Lee, P.D., and Lindley, T.C.: Effect of Fe-content on fatigue crack initiation and propagation in a cast aluminum–silicon alloy (A356–T6). Mater. Sci. Eng., A 386(1–2), 396 (2004).CrossRefGoogle Scholar
Lin, C-K. and Yang, S-T.: Corrosion fatigue behavior of 7050 aluminum alloys in different tempers. Eng. Fract. Mech. 59(6), 779 (1998).CrossRefGoogle Scholar
Menzemer, C. and Srivatsan, T.S.: The effect of environment on fatigue crack growth behavior of aluminum alloy 5456. Mater. Sci. Eng., A 271(1–2), 188 (1999).CrossRefGoogle Scholar
Hartman, A.: On the effect of oxygen and water vapor on the propagation of fatigue cracks in 2024-T3 alclad sheet. Int. J. Fract. Mech. 1(3), 167 (1965).CrossRefGoogle Scholar
Meyn, D.A.: Fractographic diagnosis of stress corrosion cracking in Al-Zn-Mg alloys. Corrosion 26(10), 427 (1970).CrossRefGoogle Scholar
Vargel, C.: Corrosion of Aluminium (Elsevier Science, England, 2004); pp. 67.Google Scholar