Investigations on servicing damage mechanisms of Cr35Ni45Nb alloy under complex conditions

Published online by Cambridge University Press:  10 May 2016

Jiangchu Xiao  and
Maicang Zhang
Jiangchu Xiao*
Affiliation:
School of Material science and engineering, University of Science & Technology Beijing, Beijing 100083, China
Maicang Zhang*
Affiliation:
School of Material science and engineering, University of Science & Technology Beijing, Beijing 100083, China
*
b) e-mail: [email protected]
a) Address all correspondence to these authors. e-mail: [email protected]
Get access

Abstract

The damage induced by oxidation and stress during the service process of Cr35Ni45Nb alloy and their influences on the microstructure evolution and creep rupture life of this alloy were studied. Continuity, compactness, and high temperature stability of the oxide layers are conductive to the performance of the alloy. A slight but complete layer of oxidation on surface improves the creep rupture life of the specimens. However, being exposed to long-term oxidation is observed to be counter-productive. Temperature stress generated during the air-cooling process creates large carbides near the surface of the specimen's cracks. Moreover, tiny carbides are precipitated from γ matrix and interfacial defects due to creep stress, but strip carbides are dissolved due to creep stress and the Gibbs–Thomson effect.

Keywords

heat-resisting alloyerosionservice damage
Type
Articles
Information
Journal of Materials Research , Volume 31 , Issue 14 , 28 July 2016 , pp. 2156 - 2163
Check for updates
Copyright
Copyright © Materials Research Society 2016 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

Contributing Editor: Jürgen Eckert

References

REFERENCES

Khodamorad, S.H., Haghshenas Fatmehsari, D., Rezaie, H., and Sadeghipour, A.: Analysis of ethylene cracking furnace tubes. Eng. Failure Anal. 21, 1 (2012).Google Scholar
Kaya, A.A., Krauklis, P., and Young, D.J.: Microstructure of HK40 alloy after high temperature service in oxidizing/carburizing environment. Mater. Charact. 49(1), 11 (2002).Google Scholar
Grabke, H.J. and Wolf, I.: Carburization and oxidation. Mater. Sci. Eng. 87, 23 (1987).Google Scholar
Zhu, Z., Cheng, C., Zhao, J., and Wang, L.: High temperature corrosion and microstructure deterioration of KHR35H radiant tubes in continuous annealing furnace. Eng. Failure Anal. 21, 59 (2012).Google Scholar
Borjali, S., Allahkaram, S.R., and Khosravi, H.: Effects of working temperature and carbon diffusion on the microstructure of high pressure heat-resistant stainless steel tubes used in pyrolysis furnaces during service condition. Mater. Des. 34, 65 (2012).Google Scholar
Schnaas, A. and Grabke, H.J.: High-temperature corrosion and creep of Ni–Cr–Fe alloys in carburizing and oxidizing environments. Oxid. Met. 12(5), 387 (1978).Google Scholar
Grabke, H.J., Ohla, K., Peters, J., and Wolf, I.: Radiotracer studies of carbon permeation through oxide scales on commercial high temperature alloys and model alloys. Mater. Corros. 34(10), 495 (1983).Google Scholar
Shinohara, T., Kohchi, I., Shibata, K., Sugitani, J., and Tsuchida, K.: Development of nondestructive technique for measuring carburization thickness and of a new carburization-resistant alloy. Mater. Corros. 37(7), 410 (1986).Google Scholar
Steurbaut, C., Grabke, H.J., Stobbe, D., Van Buren, F.R., Korf, S.J., and Defrancq, J.: Kinetic studies of coke formation and removal on HP40 in cycled atmospheres at high temperatures. Mater. Corros. 49(5), 352 (1998).Google Scholar
Xu, N., Monceau, D., Young, D., and Furtado, J.: High temperature corrosion of cast heat resisting steels in CO + CO2 gas mixtures. Corros. Sci. 50(8), 2398 (2008).Google Scholar
Das, S.K., Ghosh, R.N., and Sondhi, S.: Prediction of carbide free layer formation in Fe–Ni–Cr austenitic steel process heater tube. Corros. Eng., Sci. Technol. 47(2), 121 (2012).Google Scholar
Wang, W.Z., Xuan, F.Z., Wang, Z.D., Wang, B., and Liu, C.J.: Effect of overheating temperature on the microstructure and creep behavior of HP40Nb alloy. Mater. Des. 32(7), 4010 (2011).Google Scholar
Li, L.X. and Mao, F.R.: Calculation of the carburization stress of the ethylene cracking furnace tubes. Machinery Design & Manufacture 47(6), 42 (2009).Google Scholar
Duan, X.Z. and Zhang, Y.M.: The creep and corrosion behavior of M38G superalloy with ternary Al–Zr–Y coating. J. Chin. Soc. Corrosion Protect. 14(1), 53 (1994).Google Scholar
Huang, K.X.: Iron and Steel Metallurgy Principle (Metallurgical Industry Press, Beijing, 1990).Google Scholar
Wang, H., Du, C.Y., Li, W., Peng, Y.C., and Zhang, M.C.: Research on behavior and mechanism of high temperature oxidation for Cr35Ni45Nb heat-resistant steel under servicing condition. Hot Work. Technol. 43(18), 101 (2014).Google Scholar
de Almeida, L.H., Ribeiro, A.F., and Le May, I.: Microstructural characterization of modified 25Cr–35Ni centrifugally cast steel furnace tubes. Mater. Charact. 49(3), 219 (2002).Google Scholar
Mostafaei, M., Shamanian, M., Purmohamad, H., Amini, M., and Saatchi, A.: Microstructural degradation of two cast heat resistant reformer tubes after long term service exposure. Eng Fail Anal. 18(1), 164 (2011).Google Scholar
Robertson, J. and Manning, M.I.: Limits to adherence of oxide scales. Mater. Sci. Technol. 6(1), 81 (1990).Google Scholar
Petkovic-Luton, R. and Ramanarayanan, T.A.: Mixed-oxidant attack of high-temperature alloys in carbon-and oxygen-containing environments. Oxid. Met. 34(5–6), 381 (1990).Google Scholar
Zhang, J.S.: High Temperature Deformation and Fracture of Materials (Science Press, Beijing, 2007).Google Scholar
Wu, X.Q., Yang, Y.S., Zhan, Q., and Hu, Z.Q.: Structure degradation of HP cracking tube during service. Acta Metall. Sin. 34, 1043 (1998).Google Scholar
Pan, T., Zhang, Z.G., Bai, B.Z., and Fang, H.S.: Study of thermal stress and strain energy γ-Fe matrix around inclusion caused by thermal coefficient difference. Acta Metall. Sin. 39(10), 1037 (2009).Google Scholar
Brooksbank, D. and Andrews, K.W.: Stress fields around inclusions and their relation to mechanical properties. Prod. Appl. Clean Steels 1972, 186 (1972).Google Scholar
Hillert, M., Lai, H.Y., and Liu, G.X.: Alloy Diffusion and Thermodynamics (Metallurgical Industry Press, Beijing, 1984).Google Scholar
Li, Q.B. and Wang, X.C.: Diffusion Controlled Reaction and Thermodynamics in Alloys (Liaoning Science and Technology Publishing House, 1984).Google Scholar
Xie, J., Yu, J.J., Sun, X.F., Jin, T., and Sun, Y.: Carbide evolution behavior of K416B as-casting Ni-based surperalloy with high W content during high temperature creep. Acta Metall. Sin. 51(4), 458 (2015).Google Scholar
Liu, Z.C.: Metal Solid State Phase Transformation Tutorial (Metallurgical Industry Press, Beijing, 2003).Google Scholar
Shanmugam, S., Ramisetti, N.K., Misra, R., Mannering, T., Panda, D., and Jansto, S.: Effect of cooling rate on the microstructure and mechanical properties of Nb-microalloyed steels. Mater. Sci. Eng., A 460, 335 (2007).Google Scholar