Direct observation of indentation deformation and cracking of silicate glasses

Published online by Cambridge University Press:  03 August 2015

Satoshi Yoshida ,
Mitsuo Kato ,
Akiko Yokota ,
Shohei Sasaki ,
Akihiro Yamada ,
Jun Matsuoka ,
Naohiro Soga  and
Charles R. Kurkjian
Satoshi Yoshida*
Affiliation:
Center for Glass Science and Technology, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan; and Department of Materials Science, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan
Mitsuo Kato
Affiliation:
Center for Glass Science and Technology, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan
Akiko Yokota
Affiliation:
Center for Glass Science and Technology, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan
Shohei Sasaki
Affiliation:
Department of Materials Science, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan
Akihiro Yamada
Affiliation:
Center for Glass Science and Technology, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan; and Department of Materials Science, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan
Jun Matsuoka
Affiliation:
Center for Glass Science and Technology, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan; and Department of Materials Science, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan
Naohiro Soga
Affiliation:
Center for Glass Science and Technology, The University of Shiga Prefecture, Hikone, Shiga 522-8533, Japan
Charles R. Kurkjian
Affiliation:
Rutgers University, New Brunswick, New Jersey 08854, USA
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Indentation deformation of glass under a sharp diamond indenter causes cracking during and after a loading–unloading cycle. To get a deeper insight into the indentation cracking in glass, it is critical to understand the elastic and inelastic deformation behavior of glass under the indenter. In this study, in situ observations during Vickers indentations are carried out for silica, soda-lime, and lead–silicate glasses. It is found that the true contact area during indentation is different from the area estimated from the contact depth and the indenter geometry, and that the ridges of a Vickers indenter affect the contact shape during indentation. The contact region of silicate glasses under a Vickers indenter is not a regular square but a concave square. This results in edge cracking during indentation. It is concluded that the contact shape and the deformation mechanism of glass under the indenter are closely related to its cracking behaviors.

Keywords

amorphoushardnessfracture
Type
Articles
Information
Journal of Materials Research , Volume 30 , Issue 15 , 14 August 2015 , pp. 2291 - 2299
Copyright
Copyright © Materials Research Society 2015 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Ernsberger, F.M.: Role of densification in deformation of glasses under point loading. J. Am. Ceram. Soc. 51, 545 (1968).Google Scholar
Peter, K.W.: Densification and flow phenomena of glass in indentation. J. Non-Cryst. Solids 5, 103 (1970).Google Scholar
Lim, Y.Y. and Chaudhri, M.M.: Indentation of elastic solids with a rigid Vickers pyramidal indenter. Mech. Mater. 38, 1213 (2006).Google Scholar
Deuschle, J., Deuschle, H.M., Enders, S., and Arzt, E.: Contact area determination in indentation testing of elastomers. J. Mater. Res. 24, 736 (2009).Google Scholar
Lawn, B.R. and Marshall, D.B.: Hardness, toughness and brittleness: An indentation analysis. J. Am. Ceram. Soc. 62, 347 (1979).CrossRefGoogle Scholar
Wada, M., Furukawa, H., and Fujita, K.: Crack resistance of glass on Vickers indentation. Proc. Xth Int. Congr. Glass 11, 39 (1974).Google Scholar
Arora, A., Marshall, D.B., Lawn, B.R., and Swain, M.V.: Indentation deformation/fracture of normal and anomalous glasses. J. Non-Cryst. Solids 31, 415 (1979).Google Scholar
Sehgal, J. and Ito, S.: Brittleness of glass. J. Non-Cryst. Solids 253, 126 (1999).Google Scholar
Sehgal, J. and Ito, S.: A new low-brittleness glass in the soda-lime-silica glass family. J. Am. Ceram. Soc. 81, 2485 (1998).Google Scholar
Chiang, S.S., Marshall, D.B., and Evans, A.G.: The response of solids to elastic/plastic indentation I. Stresses and residual stresses. J. Appl. Phys. 53, 298 (1982).Google Scholar
Yoffe, E.H.: Elastic stress fields causes by indenting brittle materials. Philos. Mag. A 46, 617 (1982).Google Scholar
Yoshida, S., Sangleboeuf, J-C., and Rouxel, T.: Quantitative evaluation of indentation-induced densification in glass. J. Mater. Res. 20, 3404 (2005).Google Scholar
Kato, Y., Yamazaki, H., Yoshida, S., and Matsuoka, J.: Effect of densification on crack initiation under Vickers indentation test. J. Non-Cryst. Solids 356, 1768 (2010).Google Scholar
Sellappan, P., Rouxel, T., Celarie, F., Becker, E., Houizot, P., and Conradt, R.: Composition dependence of indentation deformation and indentation cracking in glass. Acta. Mater. 61, 5949 (2013).Google Scholar
Marshall, D.B. and Lawn, B.R.: Residual stress effects in sharp-contact cracking: I. Indentation fracture mechanics. J. Mater. Sci. 14, 2001 (1979).Google Scholar
Lawn, B.R., Dabbs, T.P., and Fairbanks, C.J.: Kinetics of shear-activated indentation crack initiation in soda-lime glass. J. Mater. Sci. 18, 2785 (1983).Google Scholar
Cook, R.F. and Pharr, G.M.: Direct observation of indentation cracking in glass and ceramics. J. Am. Ceram. Soc. 73, 787 (1990).Google Scholar
Cook, R.F. and Liniger, E.G.: Kinetics of indentation cracking in glass. J. Am. Ceram. Soc. 76, 1096 (1993).Google Scholar
Tandon, R. and Cook, R.F.: Cone crack nucleation at sharp contacts. J. Am. Ceram. Soc. 75, 2877 (1992).CrossRefGoogle Scholar
Cook, R.F., Liniger, E.G., and Pascucci, M.R.: Indentation fracture of polycrystalline cubic materials. J. Hard Mater. 5, 190 (1994).Google Scholar
Thurn, J., Morris, D.J., and Cook, R.F.: Depth-sensing indentation at macroscopic dimensions. J. Mater. Res. 17, 2679 (2002).Google Scholar
Morris, D.J. and Cook, R.F.: In-situ observation of cube-corner indentation of soda-lime glass and fused silica. J. Am. Ceram. Soc. 87, 1494 (2004).Google Scholar
Sakai, M., Hakiri, N., and Miyajima, T.: Instrumented indentation microscope: A powerful tool for the mechanical characterization in microscales. J. Mater. Res. 21, 2298 (2006).CrossRefGoogle Scholar
Miyajima, T. and Sakai, M.: Optical indentation microscopy—a new family of instrumented indentation testing. Philos. Mag. 86, 5729 (2006).Google Scholar
Oliver, W.C. and Pharr, G.M.: An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564 (1992).Google Scholar
Oliver, W.C. and Pharr, G.M.: Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology. J. Mater. Res. 19, 3 (2004).Google Scholar
Kurkjian, C.R., Kammlott, G.W., and Chaudhri, M.M.: Indentation behavior of soda-lime silica glass, fused silica, and single-crystal quartz at liquid nitrogen temperature. J. Am. Ceram. Soc. 78, 737 (1995).Google Scholar
Kurkjian, C.R. and Allameh, S.: Unpublished work (2001).Google Scholar
Gross, T.M. and Tomozawa, M.: Crack-free high load Vickers indentation of silica glass. J. Non-Cryst. Solids 354, 5567 (2008).CrossRefGoogle Scholar
Chaudhri, M.M. and Yoffe, E.H.: The area of contact between a small sphere and a flat surface. Philos. Mag. A 44, 667 (1981).Google Scholar
Muller, A.M. and Green, D.J.: Elastic indentation response of float glass surfaces. J. Am. Ceram. Soc. 93, 209 (2010).Google Scholar
Sakai, M.: Elastic recovery in the unloading process of pyramidal microindentation. J. Mater. Res. 18, 1631 (2003).Google Scholar
Giannakopoulos, A.E. and Suresh, S.: Determination of elastoplastic properties by instrumented sharp indentation. Scr. Mater. 40, 1191 (1999).Google Scholar
Kato, Y., Yamazaki, H., Itakura, S., Yoshida, S., and Matsuoka, J.: Load dependence of densification in glass during Vickers indentation test. J. Ceram. Soc. Jpn. 119, 110 (2011).Google Scholar
Rouxel, T., Ji, H., Hammouda, T., and Moréac, A.: Poisson's ratio and the densification of glass under high pressure. Phys. Rev. Lett. 100, 225501 (2008).Google Scholar
Lawn, B.R. and Howes, V.R.: Elastic recovery at hardness indentations. J. Mater. Sci. 16, 2745 (1981).Google Scholar
Yoshida, S., Sangleboeuf, J-C., and Rouxel, T.: Indentation-induced densification of soda-lime silicate glass. Int. J. Mater. Res. 98, 361 (2007).Google Scholar
Abe, T.: The mechanical behaviour of glass near its yield point. In Symposium sur la resistance mecanique du verre et les moyens de l'ameliorer Union scientifique continentale du verre. Charleroi, Belgium, 1962; p. 551.Google Scholar
Baikova, L.G., Pukh, V.P., and Talalakin, S.N.: Damages to high-strength glass in microindentation. Sov. Phys. Solid State 15, 1437 (1974).Google Scholar
Dabbs, T.P., Marshall, D.B., and Lawn, B.R.: Flaw generation by indentation in glass fibers. J. Am. Ceram. Soc. 63, 224 (1980).Google Scholar
Lathabai, S., Rödel, J., Lawn, B.R., and Dabbs, T.P.: Fracture mechanics model for subthreshold indentation flaws: I. Equilibrium fracture. J. Mater. Sci. 26, 2157 (1991).Google Scholar
Taylor, A.T. and Matthewson, M.J.: The fatigue behavior of Vickers indentations in fused silica optical fibers. In Proceedings of the International Wire & Cable Symposium. IWCS Inc., Eatontown, NJ, 1997; p. 910.Google Scholar
Wilantewicz, T.: Crack initiation behavior of optical glasses. Ph.D. Thesis, Alfred University, Alfred, NY, 2005; p. 87.Google Scholar