High pyroelectric properties of (Pb0.87La0.02Ba0.1)(Zr0.75Sn0.25–xTix)O3 ceramics near AFE/RFE phase boundary under DC bias field

Published online by Cambridge University Press:  31 May 2011

Qingfeng Zhang*
Affiliation:
Department of Electronic Science and Technology, Huazhong University of Science and Technology, Wuhan 430074, China
Shenglin Jiang
Affiliation:
Department of Electronic Science and Technology, Huazhong University of Science and Technology, Wuhan 430074, China
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

(Pb0.87La0.02Ba0.1)(Zr0.75Sn0.25–xTix)O3 (PLBZST, 0.07 ≤ x ≤ 0.09) ceramics were prepared by the conventional solid state reaction process, and their crystal structural, ferroelectric (FE), dielectric, and pyroelectric properties were systemically investigated. A transformation from antiferroelectric (AFE) phase to FE phase was observed when x was higher than 0.08. With the content of Ti increasing from 0.07 to 0.09, the dielectric peak was steeper and the pyroelectric coefficient was greater under direct current (DC) bias fields. As the DC bias field increased from 300 V/mm to 600 V/mm, the pyroelectric coefficient increased from 4500 to 10500 μC/m2·K for PLBZST specimens with 0.09. Thus, large pyroelectric response is beneficial for the development of infrared sensors.

Type
Articles
Copyright
Copyright © Materials Research Society 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Whatmore, R.: Pyroelectric devices and materials. Rep. Prog. Phys. 49, 1335 (1986).CrossRefGoogle Scholar
2.Rogalski, A.: Infrared detectors: Status and trends. Prog. Quantum Electron. 27, 59 (2003).CrossRefGoogle Scholar
3.Watton, R.: PyX3: Ir bolometers and thermal imaging: The role of ferroelectric materials. Ferroelectrics 133, 5 (1992).CrossRefGoogle Scholar
4.Clarke, R., Glazer, A.M., Ainger, F.W., Appleby, D., Poole, N.J., and Porter, S. G.: Phase transitions in lead zirconate titanate and their applications in thermal detectors. Ferroelectrics 11, 359 (1976).CrossRefGoogle Scholar
5.Shaw, C.P., Gupta, S., Stringfellow, S.B., Navarro, A., Alcock, J.R., and Whatmore, R.W.: Pyroelectric properties of Mn-doped lead zirconate-lead titanate-lead magnesium niobate ceramics. J. Eur. Ceram. Soc. 22, 2123 (2002).CrossRefGoogle Scholar
6.Zhang, G.Z., Jiang, S.L., Zeng, Y.K., Zhang, Y.Y., Zhang, Q.F., and Yu, Y.: High pyroelectric properties of porous Ba0.67Sr0.33TiO3 for uncooled infrared detectors. J. Am. Ceram. Soc. 92, 3132 (2009).CrossRefGoogle Scholar
7.Whatmore, R.W., Osbond, P.C., and Shorrocks, N.M.: Ferroelectric materials for thermal IR detectors. Ferroelectrics 76, 351 (1987).CrossRefGoogle Scholar
8.Kang, D.S., Han, M.S., Lee, S.G., and Song, S.H.: Dielectric and pyroelectric properties of barium strontium calcium titanate ceramics. J. Eur. Ceram. Soc. 23, 515 (2003).CrossRefGoogle Scholar
9.Lu, S.G., Xu, Z.K., and Chen, H.: Tunability and relaxor properties of ferroelectric barium stannate titanate ceramics. Appl. Phys. Lett. 85, 5319 (2004).CrossRefGoogle Scholar
10.Yu, Z., Ang, C., Guo, R., and Bhalla, A.S.: Dielectric properties and high tunability of BaTi0.7Zr0.3O3 ceramics under DC electric field. Appl. Phys. Lett. 81, 1285 (2002).CrossRefGoogle Scholar
11.Padmini, P., Taylor, T.R., Lefevre, M.J., Nagra, A.S., York, R.A., and Speck, J.S.: Realization of high tunability barium strontium titanate thin films by rf magnetron sputtering. Appl. Phys. Lett. 75, 3186 (1999).CrossRefGoogle Scholar
12.Berlinncourt, D.: Transducers using forced transitions between ferroelectric and antiferroelectric states. IEEE Trans. Sonics Ultrason. 13, 116 (1966).CrossRefGoogle Scholar
13.Jaffe, B.: Antiferroelectric ceramics with field-enforced transitions: A new nonlinear circuit element. Proc. IRE 49, 1264 (1961).CrossRefGoogle Scholar
14.Jaffe, B., Cook, W.R., and Jaffe, H.: Non-perovskite oxide piezoelectrics and ferroelectrics, in Piezoelectric Ceramics, Chap.9 (Academic Press, New York, 1971).Google Scholar
15.Pan, W.Y., Dam, C.Q., Zhang, Q.M., and Cross, L.E.: Large displacement transducers based on electric field forced phase transitions in the tetragonal (PbLa)(Ti, Zr, Sn)O3 family of ceramics. J. Appl. Phys. 66, 6014 (1989).CrossRefGoogle Scholar
16.Yang, P. and Payne, D.A.: The effect of external field symmetry on the antiferroelectric-ferroelectric phase transformation. J. Appl. Phys. 80, 4001 (1996).CrossRefGoogle Scholar
17.Chen, Z.L., Yao, X., Cross, L.E., Chen, Z.L., Yao, X., and Cross, L.E.: Depolarization behavior, and reversible pyroelectricity in lead scandium tantalate ceramics under DC biases. Ferroelectrics 49, 213 (1983).Google Scholar
18.Lyddane, R.H., Sachs, R.G., and Tellers, E.: On the polar vibrations of alkali halides. Phys. Rev. 59, 673 (1941).CrossRefGoogle Scholar
19.Liu, W., Wang, G.S., Cao, S., Mao, C.L., Cao, F., and Dong, X.L.: The effect of excess PbO on dielectric and pyroelectric properties of lead scandium tantalate ceramics. J. Am. Ceram. Soc. 93, 2735 (2010).CrossRefGoogle Scholar
20.Pokharel, B.P. and Pandey, D.: Dielectric studies of phase transitions in Pb1-xBaxZrO3. J. Appl. Phys. 88, 5364 (2000).CrossRefGoogle Scholar
21.Lim, S.S., Han, M.S., Hahn, S.R., and Lee, S.G.: Dielectric and pyroelectric properties of (Ba, Sr, Ca) TiO3 ceramics for uncooled infrared detectors. Jpn. J. Appl. Phys. 39, 4835 (2000).Google Scholar
22.Jun, Y.H., Kim, T.Y., and Jang, H.M.: (Ba, Sr)TiO3 system under DC-bias field: I. Improvement on the thermostability of pyroelectric response by Zr-substitution. Ferroelectrics 193, 109 (1997).CrossRefGoogle Scholar
23.Yoo, J.H. and Gao, W.: Pyroelectric and dielectric bolometer properties of Sr modified BaTiO3 ceramics. J. Mater. Sci. 34, 5361 (1999).CrossRefGoogle Scholar