Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Effect of Anodization Bath Chemistry on Photochemical Water Splitting Using Titania Nanotubes

  • Gopal K. Mor, Oomman K. Varghese, Maggie Paulose, Karthik Shankar, Craig A. Grimes
  • Journal:
    MRS Online Proceedings Library Archive / Volume 836 / 2004
    Published online by Cambridge University Press:
    01 February 2011, L1.9
    Print publication:
    2004

  • In this study highly-ordered titania nanotube arrays of variable wall-thickness and length are used to photocleave water under ultraviolet irradiation. We demonstrate that the wall thickness, and length, of the nanotubes can be controlled via anodization bath composition and temperature. The nanotube length and wall thickness are key parameters influencing the magnitude of the photoanodic response and the overall efficiency of the water-splitting reaction. For 22 nm inner-pore diameter nanotube-arrays 6 μm in length, with 9 nm wall thickness, upon 320–400 nm illumination at an intensity of 100 mW/cm2, hydrogen gas was generated at the power-time normalized rate of 51 mL/hr•W at an overall conversion efficiency of 12.5%. To the best of our knowledge, this hydrogen generation rate is the highest reported for a titania-based photoelectrochemical cell.