Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Properties of Au/Pb(Zr0.52Ti0.48)O3/ Bi4Ti3O12/p-Si Ferroelectric Memory Diodes

  • Jun Yu, Hua Wang, Xiaomin Dong, Wenli Zhou, Yunbo Wang, Lili Zhu
  • Journal:
    MRS Online Proceedings Library Archive / Volume 655 / 2000
    Published online by Cambridge University Press:
    21 March 2011, CC5.1.1
    Print publication:
    2000

  • A ferroelectric memory diodes that consists of Au/Pb(Zr0.52Ti0.48)O3/Bi4Ti3O12/p-Si multilayer configuration was fabricated by pulsed laser deposition (PLD) technique. The ferroelectric properties and the electrical characteristics of the ferroelectric film system were investigated. The polarization-voltage curve of Pb(Zr0.52Ti0.48)O3/Bi4Ti3O12 thin films system had an asymmetry hysteresis loop with Pr=20μC/cm2 and Ec=48 kV/cm, and the decay in remnant polarization was only 10% after 109 switching cycles. The C-V curve and the I-V curve showed memory effects derived from the ferroelectric polarization of PZT/BIT films. The current density was 6.7×10−8A/cm2 at a voltage of +4V, and the conductivity behavior is discussed. The results suggested that the growth of the BIT ferroelectric layer is helpful to good ferroelectric properties, fatigue and capacitance retention characteristics.