The deintercalation of a low-defect kaolinite intercalated with hydrazine was studied by X-ray diffraction, diffuse reflectance infrared spectroscopy (DRIFT), and Raman microscopy over 30 d. X-ray diffraction showed that the kaolinite was fully intercalated. More than 120 h were required for the hydrazine-intercalate to decompose. The Raman spectra of the hydrazine intercalate showed only a single band at 3620 cm−1, which was attributed to the innerhydroxyl group. Upon deintercalation, additional Raman bands were observed at 3626 and 3613 cm−1. These bands decreased in intensity with further deintercalation. As deintercalation proceeded, the bands assigned to the inner-surface hydroxyl groups at 3695, 3682, 3670, and 3650 cm−1 occurred and increased in intensity. DRIFT spectra showed two bands at 3620 and 3626 cm−1 for the fully intercalated kaolinite only. Upon deintercalation, an additional band assigned to intercalated water was observed at 3599 cm−1 and increased in intensity at the expense of the 3626-cm−1 band. Bands attributed to the innersurface hydroxyl groups increased in intensity with deintercalation. Both the Raman and DRIFT spectra showed complexity in the NH-stretching region with two sets of NH-symmetric and antisymmetric stretching bands. Deintercalation was followed by the loss of intensity of these bands. Significant changes were also observed in the hydroxyl deformation and water-bending modes as a result of deintercalation. A model of hydrazine intercalation of kaolinite based on the insertion of a hydrazine-water unit is proposed. The hydrated end of the hydrazine molecule hydrogen bonds with the innersurface hydroxyl groups resulting in the formation of a band at 3626 cm−1 in the DRIFT spectra.

Polarized micro-Raman spectra of a single large crystal of Keokuk kaolinite were recorded in the OH-stretching region with the laser beam directed along the different crystal axes. The Raman spectra are characterized by five OH-stretching bands at 3694, 3683, 3668, 3650 and 3620 cm−1 labeled A, Z, B, C and D, respectively. The relative intensities of these five bands depend on the orientation of the crystal and the scattering geometry. The spectra agree with the assertion that bands A and Z arise from out-of-plane vibrations, whereas band D corresponds to an in-plane vibration. The area ratios of the various bands were calculated from fitted curves of spectra recorded with the electric vector of the laser beam parallel to different crystallographic planes. The increments in the relative areas of bands B and C were parallel to those of bands A and Z and it appears that out-of-plane vibrations made considerable contributions to these bands also. From the change of area ratios with the change in the direction of the electric vector of the laser beam, bands A and Z were attributed to LO and TO frequencies of one inner-surface hydroxyl vibration. Bands A + Z, B, C and D were attributed to the vibrations of the hydroxyls assigned by Bish (1993) as OH(3), OH(4), OH(2) and OH(1), respectively. These observations were supported by photoacoustic and transmission IR spectra.