The acid hydrolysis products of trioctahedral fluorohectorite and phlogopite have been investigated by XRD, MAS NMR spectroscopy and nitrogen BET surface area analysis in an effort to assess the relative importance of edge attack and gallery access mechanisms. A dramatic loss of X-ray crystallinity and the formation of Q3 and Q4 SiO4 sites accompanied the depletion of Mg2+ from the octahedral sheet of both 2:1 layered structures. Depending on the extent of hydrolysis, the products derived from fluorohectorite exhibited surface areas up to 208 m2/g, whereas phlogopite hydrolysis products gave values <20 m2/g. The dramatic differences in surface areas were not related to differences in hydrolysis mechanisms. 19F MAS NMR studies indicated that the hydrolysis of fluorohectorite occurred primarily by an edge attack mechanism equivalent to the hydrolysis pathway for phlogopite. A gallery access mechanism contributed to the hydrolysis of fluorohectorite only at the later stages of octahedral Mg2+ depletion. Solvation effects appeared to be important in determining the surface areas of the reaction products derived from the swelling (fluorohectorite) and non-swelling (phlogopite) precursors.

The potential of platy nanofillers like clays in polymer nanocomposites is mostly determined by their aspect ratio. The degree of improvement that may be achieved in respect to reinforcement, gas-barrier properties and flame retardancy critically depends on the aspect ratio. Thus, increasing the aspect ratio is highly desirable in order to explore the full potential of the clay filler. Mechanical shear stress as generated in the grinding chamber of a stirred media mill (ball mill) induced an efficient exfoliation of highly hydrated and therefore ‘shear-labile’ synthetic Mg-fluorohectorite in aqueous dispersion. The attainable degree of exfoliation can be tuned and controlled through the shear forces applied by changing process parameters such as solid content and grinding media diameter. Characterization and evaluation of the exfoliation efficiency during milling was achieved by combining and cross-validating data obtained by powder X-ray diffraction (XRD), static light scattering (SLS), specific surface area measurements applying the Brunauer-Emmett-Teller (BET) equation, and scanning electron microscopy (SEM). This led to the identification of optimal processing parameters, allowing for control of the degree of exfoliation and, consequently, the aspect ratio of the nanoplatelets. Not surprisingly, besides exfoliation, increasing the magnitude of the shear stress also resulted in some reduction in platelet size.

The clay platelets obtained showed a high average aspect ratio (>600), several times greater than that of original synthetic fluorohectorite. The increase of aspect ratio was reflected in a significant enhancement of both specific surface area and cation exchange capacity (CEC) of the external basal surfaces. This method has substantial advantages compared to microfluidizer processing with respect to feasibility, batch size and particle diameter size preservation. The exfoliated nanoplatelets obtained by milling have great potential to improve mechanical properties of polymer layered silicate nanocomposites (PLSN).