Intercalation compounds of styrene and quaternary ammonium montmorillonite were prepared by immersion of the clay in styrene monomer. The intercalation of stearyltrimethylammonium (CH3(CH2)17N(CH3)3+)-montmorillonite and styrene showed an expansion of the basal spacing to a constant value of ∼32 Å after immersion for 10 days. After polymerization, the amount of polystyrene in the interlayer region was determined by thermal gravimetric analysis. Styrene adsorption initially increased with increasing quaternary ammonium cation and then became approximately constant when loading of the quaternary ammonium cation exceeded 100 meq/100 g clay. The volume resistivity of the stearyltrimethylammonium-montmorilionite-polystyrene complex, which was determined with a high resistance meter, was greater than that of both the quaternary ammonium-montmorillonite and the montmorillonite, and increased in proportion to the amount of polymer adsorbed. These data indicate that polystyrene improved the insulating properties of the clay films.

Titanium dioxide (TiO2) is a semiconductor that can be applied in different technological areas. In this work, we investigated the modifications of the electrical properties of thin films composed of TiO2 nanoparticles produced with different morphologies. The solvothermal route used for the synthesis allowed the production of nanoparticles with functionalized surfaces due to oleate groups. It was possible to modulate nanocrystals shape and size due to the detachment crystal growth mechanism, by changing the reaction time. Nanorods were obtained using 4 h of synthesis, and an increase in the reaction time to 64 h led to a bipyramidal morphology. The functionalization by the organic ligand allowed the preparation of stable colloidal solutions, which were used to prepare thin films by the dip-coating method. The films presented a homogeneous surface, an average thickness around 100 nm, and no agglomerations were observed. The electrical resistance measurements indicated a typical behavior of semiconductors, and they were dependent on the nanoparticle morphology. An exploratory test indicated that the thin films prepared using nanorod particles presented a higher electrical response compared with isotropic particles, when exposed in a liquefied petroleum gas vapor atmosphere. Therefore, the morphology of the nanoparticles is a key factor for the further application of these thin films in gas sensing. Employing an easy methodology which required simple apparatus, and by using reaction time modulation only, it was possible to prepare homogeneous thin films with a tunable electrical response.

The aim of this research was to develop the UV-cured epoxy/carbon composites. The rheological properties of the uncured neat epoxy and epoxy composite with graphite, graphene, and multi-walled carbon nanotube (MWCNT) were evaluated to observe the macroscopic flow behavior and the microstructure by shear force. The results showed that epoxy/carbon composites at high filler content exhibited shear-thinning behavior with a high yield stress value and epoxy/MWCNT at 30 phr showed this characteristic obviously. The fractured surface and particle dispersion in the epoxy matrix were evaluated by scanning electron microscopy and transmission electron microscopy, respectively. Epoxy/carbon composites at high filler content displayed rough fracture surface with particle agglomeration, thus the electrical conductivity increased. The result showed that the epoxy/MWCNT composites had high potential to use as a conductive adhesive with a 3D printing process due to high electrical conductivity with high viscosity that could be formed easily during processing.

Atomically thin 2D materials exhibit strong intralayer covalent bonding and weak interlayer van der Waals interactions, offering unique high in-plane strength and out-of-plane flexibility. While atom-thick nature of 2D materials may cause uncontrolled intrinsic/extrinsic deformation in multiple length scales, it also provides new opportunities for exploring coupling between heterogeneous deformations and emerging functionalities in controllable and scalable ways for electronic, optical, and optoelectronic applications. In this review, we discuss (i) the mechanical characteristics of 2D materials, (ii) uncontrolled inherent deformation and extrinsic heterogeneity present in 2D materials, (iii) experimental strategies for controlled heterogeneous deformation of 2D materials, (iv) 3D structure-induced novel functionalities via crumple/wrinkle structure or kirigami structures, and (v) heterogeneous strain-induced emerging functionalities in exciton and phase engineering. Overall, heterogeneous deformation offers unique advantages for 2D materials research by enabling spatial tunability of 2D materials' interactions with photons, electrons, and molecules in a programmable and controlled manner.

Relaxor ferroelectrics have drawn attention for possible applications in solid-state cooling and thermal energy harvesting, owing to their electrothermal energy conversion properties. Here, we have synthesized and characterized the structure–property correlations of a new Sn- and Nb-doped (Ba,Ca)TiO3 relaxor ferroelectric with large pyroelectric and electrocaloric effects over a broad temperature range. We observed two peaks for the temperature-dependent pyroelectric coefficient: (i) -(∂P/∂T) ∼ 563 μC/(m2 K) at T∼ 270 K and (ii) -(∂P/∂T) ∼ 1021 μC/(m2 K) at T∼ 320 K. In addition, a broad peak for electrocaloric temperature change is observed near 320 K with a relative cooling power of ∼17 J/kg. These properties could be correlated to structural changes observed using X-ray diffraction at two different temperature ranges in the material. Analysis of high-energy X-ray scattering and specific heat capacity data revealed a transition from the cubic to tetragonal phase near Tm∼ 320 K, whereas an additional increase in the tetragonality (c/a) of the polar phase is observed below Ts∼ 270 K.

A simple model system towards an impedance-probing strain sensor based on conducting tough hydrogels is demonstrated. A poly(acrylamide) hydrogel, cross-linked with N,N’-methylene-bis(acrylamide) was contacted with carbon fibres for electrical impedance analysis. The conductivity of the salt-containing hydrogel was determined to be 114 ± 10 mS/cm. Upon stretching the hydrogel samples to their fourfold initial length, the impedance response increased according to a power law. This was used to establish a sensing equation for the relation between the resistive component of the impedance signal and the applied mechanical strain under tension. This work contributes to the development of highly stretchable and soft strain sensors for applications in soft robotics.

The majority of highly efficient perovskite light-emitting diodes (PeLED) contain PEDOT:PSS (poly(3,4-ethylenedioxythiophene):polystyrenesulfonate) as hole transport layer (HTL). However, the hygroscopic and acidic nature of PEDOT:PSS may lead to deterioration of PeLED performance. Moreover, due to its inferior electron-blocking properties, an additional electron-blocking layer (EBL) is required to establish charge balance and consequently obtain superior emission characteristics in typically electron-rich PeLED structures. In this work, PTAA (poly(bis(4-phenyl)(2,4,6-trimethylphenyl)amine)) serving both as HTL and EBL is employed to substitute PEDOT:PSS in PeLED. The perovskite CsPbBr3 is chosen as emissive layer (EML) material due to its high color purity and photoluminescence (PL) quantum yield. Dense CsPbBr3 films are fabricated on PTAA-coated ITO substrates by employing a one-step spin-coating approach based on nonstoichiometric perovskite precursor solutions. To suppress non-radiative recombination, a small amount of methylammonium bromide (MABr) is incorporated in the CsPbBr3 lattice. The resulting films exhibit excellent coverage and PL intensity. PeLED containing pure CsPbBr3 films as EML show a green emission with a peak at 520 nm, maximum luminance of 11,000 cd/m2, an external quantum efficiency (EQE) of 3.3 % and a current efficiency (CE) of 10.3 cd/A. Further enhancement to 21,000 cd/m2, 7.5 % and 27.0 cd/A is demonstrated by PeLED with MABr-doped CsPbBr3 layers.

Bio-reduction agents are being explored to synthesised nanoparticles to minimize the effects of toxic chemicals. The present study was focused on green approach for the synthesis of zinc oxide nanoparticles using aqueous seeds extract of Papaver somniferum. The biosynthesised ZnO NPs (27.8nm) were characterized by using of spectroscopy and microscopy instruments. The surface morphology and the structural analysis confirms the formation of hexagonal nanostructure and a pure zincite nature of ZnO nanoparticles (NPs) respectively. The EDS spectrum confirms pure ZnO NPs were synthesised. From electrochemical properties, the CV indicates both anodic and cathodic sweep are quasi-reversible properties whose intensity increases with the scan rates. The bode plot shows the maximum angles of 74o which is an indication of a higher conductivity of ZnO NPs.

Plants produce energy in a sustainable way, they are very effective in converting light energy into a useable form. Utilising certain parts of plants in technology could become an efficient way to enhance energy production and improve sustainability. Integrating plants with technology would offer a ‘green’ way of producing elements for electronic circuits and reduce heavy metal waste. In this paper, we demonstrate that conducting polymers can be incorporated into living system such as celery. Electrical impedance analysis was used to establish the conductivity of celery with a conducting polymer (PEDOT:PSS) into its vascular system. It was demonstrated that electronic celery exhibited conductivity values of up to 0.55 ± 0.03 S/cm. This conductivity value was sufficient to demonstrate the potential of celery electronics where celery stalks are used as electrodes in simple circuits.

This study aims to create controlled fine space by electrospinning, and to develop the electrode materials for high-performance energy devices. With the popularization of mobile devices, household appliances, hybrid vehicles, electric vehicles, and the like, the use of power storage devices is expanding, and further performance improvements are required. In this study, a novel electrode material was developed by compositing Si with carbon nanofibers derived from polyacrylonitrile (PAN) by electrospinning and heat treatment. The texture and structure of the nanofibers were observed and analyzed by scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDX) and transmission electron microscopy (TEM) combined with image processing. Nano spaces were created in the CNFs and Si particles were able to be contained in the CNFs. In the second and subsequent cycles of the charge/discharge experiments of lithium ion battery (LIB) electrode made from the materials, the capacity was more than twice the theoretical capacity using graphite, and good cycle performance was obtained.

This study investigated the effect of production and curing parameters on the mechanical performance of compressed earth blocks (CEBs) stabilized with 0-20 wt % CCR (calcium carbide residue). Kaolinite (K) and quartz (Q)-rich earthen materials were mixed with the CCR and used to mould CEBs at optimum moisture content (OMC) and OMC+2 % of the dry mixtures, cured at 20 °C, ambient temperature in the lab (30±5 °C) and 40 °C for 0-90 days. After curing, the reactivity of the materials and compressive strength of dry CEBs were tested. Increasing the moulding moisture from OMC to OMC+2 decreased the compressive strength 0.3 times (4.4 to 3.3 MPa) for the CEBs stabilized with 20 % CCR cured at 30±5 °C for 45 days. Similarly, the compressive strength (4.4 MPa) was reached by CEBs stabilized with 10 and 20 % CCR after 28 and 45 days of curing, respectively. At 40 °C, the compressive strength increased 3.3 times (1.1 to 4.7 MPa with 0 to 20 % CCR) for K-rich and 2.5 times (2 to 7.1 MPa) for Q˗rich materials. At 20 °C, the compressive strength increased only 1.3 times (1.1 to 2.5 MPa) for K˗rich and barely 0.7 times (2 to 3.4 MPa) for Q-rich materials. These suggest that CCR is useful for stabilization and improving the performances of CEBs in hot regions.

Three-dimensional nano-mulberries consisting of SnO2 nanoparticles have been successfully anchored onto the surfaces of reduced graphene oxide (RGO) to construct hierarchical hybrids—SnO2@RGO with a one-pot approach. The SnO2 nano-mulberries with different amounts of RGO have been produced for optimizing their composition effect on Li storage performance. Specifically, SnO2@RGO hybrids incorporated with optimized amount of RGO nanosheets (∼20.8%) exhibit highly enhanced capacity of ∼1025 mA h/g at 0.1 A/g and a reversible capacity of 750 mA h/g over 100 cycles at 0.2 A/g. The materials also deliver much better rate performance with average specific capacity of ∼498 mA h/g at 2 A/g in comparison with that of SnO2 nano-mulberries. After cycling for 600 times at 1 A/g, the SnO2@RGO electrodes still maintain high reversible capacity of ∼602 mA h/g, corresponding to 35% of the second cycle and 133% of the 70th discharge capacity.

Three-dimensional graphene (3D-GN)/Cu/Fe3O4 composite support materials were synthesized by a modified chemical reduction method using graphene oxide precursor. A 3D-GN/Cu/Fe3O4 biosensor was prepared by coating the electrode with laccase. The electrochemical properties of the biosensor were investigated by cyclic voltammetry (CV) and differential pulse voltammetry using potassium ferricyanide, phosphate-buffered saline (PBS) solution, and bisphenol A (BPA) solution. The current response of 3D-GN/Cu/Fe3O4 biosensors presents a remarkable sensitivity based on CV. The linear range of BPA is 7.2–18 μM using differential pulse voltammetry in PBS solution (pH = 4.0). A linear fitting equation of the laccase biosensor was observed for the current response as a function of BPA concentration. The detection limit was decreased to 1.7 μM. The detection approach herein turns out to be highly sensitive, has a wide linear range, and exhibits excellent stability.

The activated carbon paper (ACP) has been designed as the active electrode material of supercapacitor to improve its capacitive performance. ACP is prepared by electrochemical nitrate ion–assisted exfoliation, sulfate ion–assisted exfoliation, and subsequent hydrothermal reduction processes. The as-prepared ACP shows obviously rougher surface along with the expanded layer distance. ACP exhibits higher specific capacitance of 380 mF/cm2 at 1 mA/cm2 than that of 21 mF/cm2 for carbon paper. ACP electrode shows the cycling capacitance retention of 98% after 5000 cycles at 10 mA/cm2. The symmetric ACP supercapacitor is constructed using ACP electrode and H2SO4 involved polyvinyl alcohol gel electrolyte. ACP supercapacitor presents the specific capacitance of 97 mF/cm2, the energy density of 0.343 mW h/cm3, and the output voltage of 1.6 V at 1 mA/cm2. ACP with high capacitance performance presents the promising supercapacitor application for the electrochemical energy storage.

Machine learning (ML) and artificial intelligence (AI) are quickly becoming commonplace in materials research. In addition to the standard workflow of fitting a model to a large set of data in order to make predictions, the materials community is finding novel and meaningful ways to integrate AI within their work. This has led to an acceleration not only of materials design and discovery, but also of other aspects of materials research as well, including faster computational models, the development of autonomous and intelligent “robot researchers,” and the automatic discovery of physical models. In this issue, we highlight a few of these applications and argue that AI/ML is delivering real-world, practical solutions to materials problems. It is also clear that we need AI/ML methods and models, “dialects” that are better adapted to materials research.

In this work, atomic layer deposition (ALD), as a novel strategy, has been applied to deposit MgO on nano-sized porous Si (pSi) dendrites obtained by etching Al–Si alloy for LIBs. The reversible specific capacity of pSi@MgO electrode is 969.4 mA h/g after 100 cycles at 100 mA/g between 0.01 and 1.5 V, and it presents the discharge specific capacities of 1253.0, 885.5, 642.4, 366.2, and 101.4 mA h/g at 100, 500, 1000, 2000, and 5000 mA/g, respectively. What is more, it delivers a high reversible capacity of 765.1 mA h/g even at 500 mA/g after 200 cycles. The performance improvement can be attributed to the protection of the MgO layer and built-in space of porous Si for volume expansion upon cycling. These results illustrate that ALD derived coating is a powerful strategy to enhance electrical properties of anode materials with huge volume change for lithium-ion batteries.

Bi0.5Na0.5TiO3 (BNT)-based lead-free materials are important for piezoelectric actuator, and several researchers have studied the effect of B-site complex ion doping on strain in (Bi0.5Na0.5)TiO3–SrTiO3. In this work, a paraelectric perovskite Sr(Zn1/3Nb2/3)O3 (SZN) with B-site complex structure was introduced into 0.80(Bi0.5Na0.5)TiO3–0.20SrTiO3 (BNTST) to investigate the phase structure and electrical properties as well as the field-induced strain behavior. The results showed that SZN substitution decreases the rhombohedrality 90-γ and induces the transition from dominant ferroelectric to nonergodic relaxor by shifting its TF-R to lower temperatures. Moreover, the field-induced ferroelectric domains cannot remain stable at room temperature when SZN substitution is large than 1.0 mol%. These behaviors induced the transition between nonergodic relaxor and ergodic relaxor, which contributed to its large strain and related properties. In this work, this material gave the largest bipolar strain of 0.43% and large normalized unipolar strain of 505 pm/V at the SZN content of 2 mol% under 8 kV/mm, and showed good temperature stability up to 100 °C. The above encouraging results may be helpful for further investigation of BNTST-based ternary systems in search of a potential Pb-free piezoelectric material.

In situ transmission electron microscope (TEM) characterization techniques provide valuable information on structure–property correlations to understand the behavior of materials at the nanoscale. However, understanding nanoscale structures and their interaction with the electron beam is pivotal for the reliable interpretation of in situ/ex situ TEM studies. Here, we report that oxides commonly used in nanoelectronic applications, such as transistor gate oxides or memristive devices, are prone to electron beam induced damage that causes small structural changes even under very low dose conditions, eventually changing their electrical properties as examined via in situ measurements. In this work, silicon, titanium, and niobium oxide thin films are used for in situ TEM electrical characterization studies. The electron beam induced reduction of the oxides turns these insulators into conductors. The conductivity change is reversible by exposure to air, supporting the idea of electron beam reduction of oxides as primary damage mechanism. Through these measurements we propose a limit for the critical dose to be considered for in situ scanning electron microscopy and TEM characterization studies.

Doping, as a primary technique to modify semiconductor transport, has achieved tremendous success in the past decades. For example, boron and phosphorus doping of Si modulates the dominant carrier type between p-type and n-type, serving as the backbone for the modern microelectronic technologies. Doped III-V semiconducting systems exhibit phenomenal optoelectronic properties. Magnesium doped gallium nitride plays an important role to build efficient blue light-emitting diode (LED), which won Nobel Prize in physics in 2014. The rise of two-dimensional (2D) materials sheds light on their potential in next generation electronic, optoelectronic, and quantum applications. These properties can further be controlled via doping of 2D materials, however, many challenges still remain in this field. Here, we present a rapid review on the recent achievements and challenges in the metastable and substitutional doping of 2D materials, followed by providing an outlook on integrating 2D materials into more advanced electronic architectures.

Zinc oxide (ZnO) is a n-type transparent semiconductor which can be processed by low cost techniques (such as spray-pyrolysis and spin-coating) and can be applied as the active layer of thin-films transistors (TFTs). The electrical properties of ZnO films are strongly affected when the device is exposed to room conditions and/or UV-light, suggesting possible applications as UV or/and gas sensors. Atmospheric oxygen molecules adsorbed on ZnO surface act as charge traps, decreasing the material conductivity. The incidence of UV-light causes an increase of the material conductivity due to the photogeneration of electron-hole pairs via direct band-to-band transitions (classic photoconductivity process) and due to the desorption of oxygen molecules, which presents a relatively slower response and is a less understood mechanism. In the current paper, we study the influence of environmental parameters, such as temperature, humidity and UV-light intensity, on the electrical properties of spin-coated ZnO thin films to understand the role of the desorption mechanism on the photoconductivity process. The analysis of the device current vs. time curves shows the existence of two light-induced desorption mechanisms: i) one which increases the electrical conductivity of the ZnO film (desorption-like process) and ii) a second one which decreases the conductivity (adsorption-like process). A Plackett-Burman design of experiment (DOE) was used to study the influence of characterization factors like UV intensity, temperature and humidity on electrical parameters obtained from the experimental curves. We observed that the desorption-like process is a first order mechanism, exhibiting desorption rate proportional to n(t), where n(t) represents the adsorbate concentration as a function of the time, whereas the adsorption-like mechanism exhibits a desorption rate proportional to the forth power of n(t).