Genthelvite from pegmatite veins hosted by the albite-enriched granite (ca.1.8 Ga) corresponding to the Sn–Nb–Ta (F, REE, Li, Zr, U, Th) Madeira deposit, Amazonas, Brazil was studied. Genthelvite, the exclusive Be-bearing mineral within the deposit, occurs as massive crystals of up to 4.7 cm in size. Compositions are homogeneous within individual crystals, although there is moderate variation in the overall composition reflecting relatively limited substitutions within the helvine–genthelvite–danalite solid-solution series, with relatively high Zn contents (36.96 to 49.45 wt.% ZnO), lower Mn contents (0.61 to 3.03 wt.% MnO), and variable Fe contents (2.10 to 10.94 wt.% FeO), completing an existing compositional gap in this system. Genthelvite formed in an alkaline and subaluminous environment, under stable conditions within the late-evolved fluids, at relatively high temperature (>400°C), in a reducing environment. The extremely high concentration of fluorine in the magma and the crystallisation of magmatic galena resulted in an effective reduction of H2S fugacity. This resulted in the stabilisation of genthelvite during the transition from the late magmatic to early hydrothermal stages of the albite-enriched granite evolution. The variability in Fe content within genthelvite is associated primarily with localised variations in the mineral assemblage (e.g. the presence of riebeckite and polylithionite). Genthelvite was altered by low-temperature aqueous fluids rich in F which resulted in the incorporation of Fe, Mn, Mg, Pb, Ba, Na, K, U and REE into the Zn2+ structural site and the allocation of excess Si, Al, Ti and P in the IVSi and IVBe structural sites. The substantial content of U and REE substituting for Zn, together with Si substituting for Be, is charge balanced by the presence of vacancies at the A site.

Arsenoústalečite is a new mineral discovered in a sample collected from the abandoned Ústaleč deposit near Horažďovice, SW Bohemia, Czech Republic. It occurs as rare anhedral grains, up to 40 μm in size, in a calcite gangue, associated with stibioústalečite, hakite-(Hg), berzelianite and uraninite. Arsenoústalečite is dark grey, with a metallic lustre. Mohs hardness is ca. 3½–4; calculated density is 5.730 g/cm3. In reflected light, arsenoústalečite is pale grey with a yellowish shade; it is isotropic. Internal reflections were not observed. Reflectance values for the four COM wavelengths in air [R (%) λ (nm)] are: 33.3 (470); 33.1 (546); 33.0 (589); and 32.9 (650). The empirical formula of arsenoústalečite is (Cu5.81Ag0.17)Σ5.98(Cu5.95Fe0.02Zn0.02Hg0.01)Σ6.00(As1.40Sb0.87Te1.73)Σ4.00(Se10.30S2.32)Σ12.61. The ideal formula is Cu12(As2Te2)Se13, which requires (in wt.%) Cu 34.76, As 6.83, Te 11.63, Se 46.78, total 100.00. Arsenoústalečite is cubic, I$\bar{4}$3m, with unit-cell parameters a = 10.6580(19) Å, V = 1210.7(6) Å3 and Z = 2. The strongest reflections of the calculated powder X-ray diffraction pattern [d, Å (I, %) hkl] are: 3.077 (100) 222, 2.848 (10) 321, 1.946 (12) 521, 1.884(52) 440 and 1.608(21) 622. According to the single-crystal X-ray diffraction data (R1 = 0.0285 on the basis of 334 unique reflections with Fo > 4σFo and 24 refined parameters), arsenoústalečite is isotypic with other tetrahedrite-group minerals. The crystal structure of co-existing stibioústalečite, with an empirical formula of (Cu5.69Ag0.07)Σ5.76(Cu5.80Zn0.13Fe0.06Hg0.01)Σ6.00(Sb1.82As0.42Te1.76)Σ4.00(Se9.52S3.10)Σ12.62 and unit-cell parameters a = 10.6975(16) Å, V = 1224.2(5) Å3 and Z = 2, was refined to R1 = 0.0191 on the basis of 267 unique reflections with Fo > 4σFo and 24 refined parameters. Structural relationships and crystal-chemistry of both members of the ústalečite series are discussed. Arsenoústalečite is named after its type locality, the Ústaleč deposit and its chemical composition. The mineral and its name have been approved by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (IMA2022-116).

This study describes a new variety of chalcedony with a unique inhomogeneous bluish green hue, named aquaprase. It was discovered in Africa and is considered to be a valuable addition to the gem trade. A multi-methodological approach was used to examine its chemistry, mineralogy and microstructure, which were then compared to those of chrysoprase and agate, two of the most popular varieties of chalcedony. Optical microscopy revealed a complex microstructural heterogeneity in the different colour intensity areas/bands of aquaprase and agate, whereas chrysoprase exhibited a more homogeneous coexistence of micro- and cryptocrystalline quartz. High-resolution synchrotron XRD was essential for highlighting the complex assemblage of various types of α-quartz in aquaprase and agate (which differ in terms of crystal size and/or cell parameters). Micro-Raman spectroscopy revealed α-quartz and moganite in all three varieties of chalcedony and the presence of the nickel-bearing layered silicate mineral, willemseite, in chrysoprase, which is responsible for its green colouration. The chemical analysis displayed a homogeneous composition of agate, as well as high levels of nickel content in the chrysoprase variety. Aquaprase showed significant amounts (ppm by weight) of trace elements (Al, Mg, Na, K, Ca, Ti, U and Fe) characteristic of its formation environment, as well as high values of Cr, which are thought to be the cause of its bluish green colouration.

The new columbite-supergroup mineral dmitryvarlamovite, ideally Ti2(Fe3+Nb)O8, was discovered in weathered alkaline metasomatic assemblages formed after late Riphaean sedimentary carbonate rocks of the Verkhne-Shchugorskoe deposit, Middle Timan Mts., Russia. The associated minerals are columbite-(Fe), pyrochlore-group minerals, monazite-(Ce), xenotime-(Y), baryte, pyrite, drugmanite and plumbogummite. Dmitryvarlamovite occurs as isolated anhedral equant grains up to 0.5 mm across. The colour of dmitryvarlamovite is black, the streak is black and the lustre is submetallic. The new mineral is brittle, with the mean VHN hardness of 753 kg mm–2 corresponding to the Mohs’ hardness of 6. No cleavage is observed. The fracture is conchoidal. The calculated density is 4.891 g⋅cm–3. In reflected light, dmitryvarlamovite is light grey; no pleochroism is observed. The reflectance values (Rmin, % / Rmax, % / λ, nm) are: 19.8/20.3/470, 18.3/18.9/546, 17.8/18.5/589 and 17.3/17.8/650. The chemical composition is (electron microprobe data, with iron divided into Fe2O3 and FeO based on the charge balance, wt.%): MnO 0.11, FeO 1.51, V2O3 0.89, Cr2O3 0.28, Fe2O3 19.26, TiO2 37.72, Nb2O5 40.08, total 99.85. The IR and Raman spectra indicate the absence of H-, C- and N-bearing groups. The empirical formula is (Fe2+0.08V3+0.05Cr3+0.01Fe3+0.92Ti1.79Nb1.15)Σ4.00O8. The crystal structure was determined using single-crystal X-ray diffraction data and refined to R = 0.048. Dmitryvarlamovite is orthorhombic, space group P21212, a = 4.9825(6), b = 4.6268(4), c = 5.5952(6) Å and V = 5.5952(6) Å3 (Z = 1). The structure is related to those of wolframite-group minerals but differs in the scheme of cation ordering. The crystal-chemical formula derived based on the structural data is (Ti0.57Nb0.21Fe3+0.15Fe2+0.04V0.02Cr0.01)2(Nb0.36Ti0.33Fe3+0.31)2O8. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 3.58 (40) (011), 2.911 (100) (111), 2.809 (40) (002), 2.497 (38) (020), 2.447 (29) (103), 1.7363 (32) (103) and 1.7047 (29) (220). Dmitryvarlamovite is named after Dmitry Anatol'evich Varlamov (b. 1965).

The new mineral naalasite (IMA2023–027), NaAl(AsO3OH)2⋅H2O, was found at the Torrecillas mine, Iquique Province, Chile, where it is a secondary alteration phase associated with anhydrite, juansilvaite, magnesiokoritnigite and a lavendulan-like phase. Naalasite occurs in tightly intergrown aggregates and druses of equant crystals. Crystals are light to medium pink and transparent, with vitreous lustre and white streak. The Mohs hardness is ~3½. The density is 3.19(2) g⋅cm–3. Optically, naalasite is uniaxial (+), with ω = 1.630(3) and ɛ = 1.660(3) (white light). The empirical formula (based on 9 O apfu) is Na0.92Al0.61Fe3+0.39As2O9H4.07. Naalasite is trigonal, space group R32, with cell parameters: a = 8.494(4), c = 26.430(13) Å, V = 1651.5(4) Å3 and Z = 9. The structure, refined to R1 = 3.78% for 641 I > 2σI reflections, is based on a loose 3D framework of alternating AsO3OH tetrahedra and AlO6 octahedra. The structure is topologically equivalent to that of nafeasite and can be regarded as its Al analogue, even though nafeasite is monoclinic with space group C2.

Hexavalent chromium (Cr6+) is a toxic carcinogenic pollutant that might be released by the mining and processing of ultramafic rocks and nickel laterites and which requires permanent removal from the contaminated biosphere. Ultramafic material can also serve as a feedstock for the sequestration of CO2 resulting from the growth of new minerals, raising the intriguing proposition of integrated sequestration of both pollutants, CO2 and chromium, into magnesium carbonates. Such a synergistic process downstream of ore recovery and mineral processing could be an elegant proposition for more sustainable utilisation and management of the Earth's resources. We have therefore carried out an experimental and microanalytical study to investigate potentially suitable carbonate minerals. Uptake of chromium in carbonate phases was determined, followed by identification of the crystalline phases and characterisation of the local structural environment around the incorporated chromium centres. The results suggest that neither nesquehonite nor hydromagnesite have the structural capacity to incorporate Cr6+ or Cr3+ significantly at room temperature. We therefore propose that further research into this technology should focus on laboratory assessments of other phases, such as layered double hyroxides, that have a natural structural capacity to uptake both chromium and CO2.

Plumboperloffite, PbMn2+2Fe3+2(PO4)3(OH)3, is a new mineral and member of the bjarebyite group from Wiperaminga Hill West Quarry, Boolcoomatta Reserve, Olary Province, South Australia, Australia. The mineral was found in a single cavity in triplite–barbosalite matrix associated with fluorapatite, phosphosiderite, natrodufrénite and fluorite. The mineral forms intergrowths of subparallel, thin tabular to bladed crystals. Individual crystals are up to 40 μm in length. Plumboperloffite is brownish orange in colour with a vitreous lustre. The mineral has brittle tenacity, an excellent cleavage on {100} and uneven fracture. The calculated density is 4.416 g/cm3. Plumboperloffite is biaxial (+), α = 1.87(1), β = 1.88(1) and γ = 1.89(1) as measured in white light. The measured 2V is 88(1)°. Dispersion is apparently strong, based on extinction colours and the orientation is Y = b. The pleochroism in shades of yellow brown is X < Z < Y. Electron microprobe analysis gave the empirical formula (based on 15 O apfu) (Pb0.92Ca0.04Ba0.01K0.01)Σ0.98(Mn2+1.84Fe2+0.13)Σ1.97(Fe3+1.97Al0.03)Σ2.00(P3.01O11.94)(OH)Σ3.06. Plumboperloffite is monoclinic, space group P21/m with a = 9.1765(18), b = 12.340(3), c = 5.0092(10) Å, β = 101.01(3)°, V = 556.8(2) Å3 and Z = 2. The crystal structure has been refined using X-ray single-crystal data to a final R1 = 0.0207 on the basis of 1417 reflections with Fo > 4σ(Fo). The mineral is isostructural with members of the bjarebyite-group minerals.

The high-temperature behaviour of a feldspar-group mineral, filatovite (with the simplified formula: K(Al,Zn)2(As,Si)2O8), in which the Al:As:Si ratio is close to 2:1:1), was studied by in situ high-temperature single-crystal X-ray diffraction and in situ high-temperature (hot stage) Raman spectroscopy up to 600°C. In the temperature range studied (25–600°С) filatovite does not undergo any phase transition, whereas at 800°C it decomposes to X-ray amorphous phase(s). The evolution of 12 main Raman bands was traced during heating, which indicates a gradual change in the crystal structure. The thermal expansion coefficients of filatovite demonstrate a sharply anisotropic character of thermal expansion: the maximal expansion is close to the a axis (α11 = 17.7(1) × 10–6 °C–1), whereas along the b and c axes the thermal expansion coefficients are close to zero. Such behaviour is typical for minerals with a similar crystal structure topology; it indicates the dominant role of structure geometry in the thermal behaviour of the mineral.

Plumbogaidonnayite, ideally PbZrSi3O9⋅2H2O, is a new gaidonnayite-group mineral discovered as a secondary product derived from the alteration of eudialyte from the Saima alkaline complex, China. It occurs as aggregates (up to 1 mm) composed of subhedral to anhedral or platy crystals (individually 5–50 μm), associated closely with microcline, natrolite, aegirine, gaidonnayite, georgechaoite, zircon, bobtraillite and britholite-(Ce) in eudialyte pseudomorphs. The crystals are transparent, colourless or light brown with a vitreous lustre. Plumbogaidonnayite is brittle with conchoidal fracture, and it has a Mohs hardness of ~5 and a calculated density of 3.264 g/cm3. It is optically biaxial (+) with α = 1.61(3), β = 1.63(3) and γ = 1.66(4). The calculated 2V is 80°, with the optical orientations X, Y and Z parallel to the crystallographic a, b and c axes, respectively. The empirical formula is (Pb0.70Ca0.17Ba0.01K0.11Na0.01Y0.01)Σ1.01(Zr1.00Hf0.01Ti0.01)Σ1.02Si3.01O9⋅2H2O calculated on the basis of nine oxygen atoms per formula unit and assuming the occurrence of two H2O groups. Plumbogaidonnayite is orthorhombic, P21nb, a = 11.7690(4) Å, b = 12.9867(3) Å, c = 6.66165(16) Å, V = 1018.17(5) Å3 and Z = 4. The nine strongest lines of its powder XRD pattern [d in Å (I, %) (hkl)] are: 6.489 (36) (020), 5.803 (100) (101), 4.661 (27) (021), 4.336 (29) (121), 3.640 (30) (221), 3.114 (79) (112), 2.947 (27) (400), 2.622 (27) (241) and 2.493 (27) (312). Plumbogaidonnayite has a similar spiral chain framework structure with gaidonnayite and georgechaoite, which is composed of SiO4 tetrahedra and ZrO6 octahedra, but with disordered extra-framework sites (cations and H2O groups) characterised by the substitution of 2Na+ (K+)→Pb2+ (Ca2+) + □ (vacancy). The discovery of plumbogaidonnayite adds a new perspective on the cation ordering and heterovalent substitution mechanism in gaidonnayite-group minerals.

Natromelansonite, Na3Zr[Si7AlO19]⋅4–5H2O, was found at the Poudrette (Demix) quarry, Mont Saint-Hilaire, Quebec, Canada in a highly altered pegmatite together with a clay mineral, steacyite, polylithionite and rhodochrosite. It occurs as an outer zone of tabular crystals to 0.1 × 0.3 × 1 mm in size flattened on (001). The inner zone is made of melansonite. The mineral is grey with white powder colour and vitreous lustre. The cleavage is parallel to {010}, perfect. The Mohs hardness is 3.5. The mineral has green fluorescence under short-wave ultraviolet light. The Dcalc is 2.31 g/cm3. The infrared spectrum is reported. The composition (wt.%, average of 8 analyses) is Na2O 10.08, K2O 1.72, CaO 0.24, BaO 0.32, MnO 0.10, Al2O3 6.86, Y2O3 0.35, Yb2O3 0.55, SiO2 56.23, ZrO2 14.78, H2O 9.52, total 100.75. The empirical formula calculated on the basis of O = 23 apfu and H = 8 apfu is Na(□Na0.38Ca0.02Mn0.01)2(Na0.70K0.28Ba0.02)Σ1.00(Zr0.91Y0.02Yb0.02)Σ0.95(Si7.08Al1.02)Σ8.10O19⋅4H2O. The mineral is monoclinic, P21/m, a = 6.5156(3) Å, b = 24.061(1) Å, c = 6.9759(6) Å, β = 90.453(5)° and V = 1093.61(9) Å3 and Z = 2. The strongest reflections of the powder X-ray diffraction pattern [d,Å(I)(hkl)] are: 12.02(100)(020), 6.97(89)(001), 6.51(39)(100), 3.416(37)(160), 3.062(42)($\bar{1}$61, 102, 161 and $\bar{1}$12), 3.018(38)(230 and 042), 2.864(40)(240 and 132). The crystal structure, solved and refined from single-crystal X-ray diffraction data (R1 = 0.042), is based on a double sheet of tetrahedra (T) and a sheet of octahedra (O) that alternate along the [010] direction forming a TOT structure typical for members of the rhodesite mero-plesiotype series.