Please note the copyright statement should read: Her Majesty the Queen in Right of Canada, as represented by the Minister of National Defence, [2010]. © Sa Majesté la Reine (en droit du Canada), telle que représentée par le ministre de la Défense nationale, [2010].

Two carbonates Cs2Sr2(CO3)3 and Rb2Sr2(CO3)3 were synthesized by solid-state reaction at high temperatures, and their crystal structures were determined from X-ray powder diffraction data. Because of the presence of heavy atoms and heavy peak overlapping, proper restrains on light-atom groups were found essential to obtain satisfactory results. The title compounds are isostructural to an early reported compound Cs2Ba2(CO3)3 and crystallize in cubic space group I213, with unit-cell dimensions a=10.072 64(2) Å for the cesium phase and a=9.855 56(7) Å for the rubidium phase. Unlike most carbonates, the title compounds feature in mutually perpendicular CO3 atomic groups. Our results also indicate that the global instability index is a more sensitive parameter in evaluating the structure rationality over the agreement factors. Moreover, differential thermal analysis and thermogravimetric analysis measurements reveal that Cs2Sr2(CO3)3 and Rb2Sr2(CO3)3 are stable in air up to 796 and 880 °C, respectively.

The crystal structure of the mineral strontiodresserite, (Sr,Ca)Al2(CO3)2(OH)4⋅H2O, from the Francon Quarry, Montreal, Quebec, Canada, has been solved from laboratory powder diffraction data using a combination of charge-flipping and simulated annealing methods. The structure is orthorhombic in space group Pnma with a=16.0990(7), b=5.6133(3), and c=9.1804(4) Å (Z=4) and the framework of the mineral is isostructural with that of dundasite. The strontium has a coordination number of 9 and the carbonate anions form a bridge between the SrO9 polyhedra and AlO6 octahedra. The water molecule lies in a channel that runs parallel to the b axis. An ordered network of hydrogen atoms could be uniquely determined from crystal-chemical principles in the channels of strontiodresserite. Ab initio density functional theory (DFT) energy minimization of the whole structure gave results in full agreement with X-ray refinement results for nonhydrogen atoms. The stability of this model (as well as that of the corresponding model of dundasite) in the proposed Pnma space group was tested by DFT optimization in space group P1 of random small distortions of this structure. This test confirms that both minerals are isostructural, including their hydrogen-bond networks.

A new cobalt hydroxide carbonate Co2(OH)2CO3 was successfully synthesized by a hydrothermal method. The compound is isomorphous with malachite [Cu2(OH)2CO3] and crystallizes in a monoclinic system [space group P21/a (No. 14); a=9.448(5) Å, b=12.186(9) Å, c=3.188(4) Å, β=98.593°, V=367.143(9) Å3, Z=4, and Dc=3.786(9) g/cm3]. Crystal structure of Co2(OH)2CO3 was refined by the Rietveld method with RP=4.3%, RWP=5.7%, Rexp=5.1%, RB=1.74%, and S=1.117 on the basis of the X-ray powder diffraction data. The crystal structure of Co2(OH)2CO3 obtained by the Rietveld refinement shows that all species Co2+, CO32−, and OH− ions occupy C1 site symmetry. Two crystallographically different Co2+ and OH− ions and one type CO32− ion exist in the lattice. Co(1) is coordinated to two oxygen atoms from CO32− ions and two OH− ions; Co(2) is coordinated to two oxygen atoms from CO32− ions and four OH− ions, thus forming a distorted octahedron with (4+2) coordination.

Crystal structure of Li2SrSiO4 was reinvestigated by laboratory X-ray powder diffraction. The title compound was trigonal with space group P3121, Z=3, unit-cell dimensions a=0.502 281 (4) nm and c=1.245 520(8) nm, and V=0.272 129(3) nm3. The initial structural model was derived by the direct methods and further refined by the Rietveld method. The maximum-entropy method-based pattern fitting (MPF) method was used to confirm the validity of the structural model, in which conventional structure bias caused by assuming intensity partitioning was minimized. The final reliability indices calculated from MPF were Rwp=8.04%, S=1.22, Rp=6.01%, RB=1.50%, and RF=0.66%. Atomic arrangements of the final structural model were in excellent agreement with the three-dimensional electron-density distributions determined by MPF.

The structure of bethanechol chloride C7H17ClN2O2 is solved from conventional X-ray powder diffraction data in direct space [monoclinic unit cell with a=8.8749(3) Å, b=16.4118(7) Å, c=7.1373(3) Å, β=93.803(1)°, V=1037.29(7) Å3, Z=4, and space group P21/n]. The existence of a second orthorhombic closely related form is discussed.

Amino acids often cocrystallize with water molecules, which make them pseudopolymorphs of their anhydrous forms. In this work, we discuss in detail the hydrogen bond patterns in anhydrous L-proline and DL-proline and its pseudopolymorphic forms: L-proline monohydrate and DL-proline monohydrate. For this propose, the crystal structure of L-proline anhydrous was determined from synchrotron X-ray powder diffraction data and refined using the Rietveld method. Special emphasis is given to the role played by the water molecule in the hydrogen bond network observed in the crystalline structures.

[Zr2F8(dmso)2(H2O)2], a dehydration product of [ZrF4(dmso)(H2O)2]⋅2H2O, crystallizes in the orthorhombic symmetry [space group Cmca, a=7.8266(3) Å, b=13.5847(5) Å, c=15.6119(6) Å, and Z=4]. The structure, solved ab initio in direct space from X-ray powder diffraction data, is built up from [Zr2F8O4] bipolyhedra formed by edge sharing of [ZrF5O2] pentagonal bipyramids (condensed from isolated [ZrF4O3] pentagonal bipyramids in the precursor). Difficulties associated with a fortuitous hexagonal pseudosymmetry were surmounted. The dmso departure at 220 °C leads to an amorphous phase.

X-ray powder diffraction was used for the structural study of nonlinear optical borates K1−xNaxSr4(BO3)3 (x≤0.5). Results show that up to 50% K+ can be substituted by Na+ in orthorhombic K1−xNaxSr4(BO3)3. Isolated BO3 triangles in the Na-substituted compound constrict to adjust to a local distribution of alkali-metal atoms, which explains the large range of structural homogeneity. An expansion of the c axis in a unit cell with increasing Na substitution was found probably caused by the tilted BO3 triangles and asymmetric distortion of (K/Na)O8 polyhedra. As the ratio of ionic radii of alkaline-earth and alkali-metal cations decreases and the electronegative difference between alkaline-earth and alkali-metal cations increases, the crystal system of MM′4(BO3)3 borates changes from cubic to orthorhombic and then to monoclinic.

A novel hexaborate, Na2ZnB6O11, has been successfully synthesized by solid-state reaction and ab initio crystal-structure analysis has been completed using powder X-ray diffraction data. The compound crystallizes in the monoclinic space group Cc with lattice parameters a=10.7329(2) Å b=7.4080(3) Å, c=11.4822(2) Å, and β=112.16(2)°. The number of chemical formula per unit cell is Z=4 and the calculated density is 2.768(3) g/cm3. It represents a new structure type in which double-bridge-ring [B6O11]4− groups were found as fundamental building units. The infrared spectrum confirms the presence of both [BO3]3− groups and [BO4]5− groups.