In situ measurement of growth stress in alumina scale

Published online by Cambridge University Press:  06 March 2012

E. D. Specht ,
P. F. Tortorelli  and
P. Zschack
E. D. Specht*
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6118
P. F. Tortorelli
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6118
P. Zschack
Affiliation:
University of Illinois at Urbana-Champaign, Argonne, Illinois 60439
*
a)Author to whom correspondence should be addressed; Electronic mail: [email protected]
Get access Rights & Permissions [Opens in a new window]

Abstract

Stress in the early stages of growth has been measured in α-Al2O3 (alumina) scales formed on FeCrAl- and NiAl-based alloys during heating in air at 1000 °C to 1200 °C. Scale thickness ranges from 0.5 to 5 μm, times from 5 to 720 min. Stress was measured using the multiple-tilt method. In order to measure the thinnest scales at the earliest times, focused, monochromatic synchrotron radiation was used for high intensity, and a fixed, small angle of incidence was used along with an appropriate wavelength to maximize scattering from the film relative to the background from the substrate. Depending on the composition, transient tensile stresses of up to 1.2 GPa were observed, with maximum stress at times ranging from >10 h at 1000 °C to <10 min at 1200 °C. Thermal stresses induced by an abrupt temperature change were found to relax much more quickly, suggesting that the kinetics observed during isothermal growth reflect a dynamic competition between stress generation and stress relaxation. These results challenge commonly accepted models of growth stress in scales that predict that a compressive stress will be generated as the metal converts to a larger-volume oxide in a constrained location such as an interface. The observed tensile stress may be due to another mechanism altogether (e.g., grain coalescence), or to the conversion of a transitional Al2O3 to the equilibrium α-Al2O3 phase. For one composition, transitional Al2O3 is observed during the period of tensile stress

Type
Technical Articles
Information
Powder Diffraction , Volume 19 , Issue 1 , March 2004 , pp. 69 - 73
Copyright
Copyright © Cambridge University Press 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Bull, S. J. (1998). Oxid. Met. OXMEAF 49, 1–17. oxm, OXMEAF CrossRefGoogle Scholar
Busing, W. R.and Levy, H. A. (1966). Acta Crystallogr. ACCRA9 22, 457. acc, ACCRA9 CrossRefGoogle Scholar
Cannon, R. M. and Hou, P. Y. (1998). In High-Temperature Corrosion and Materials Chemistry, edited by P. Y. Hou, M. J. McNallan, R. Oltra, and D. A. Shores (The Electrochemical Society, Pennington, NJ).Google Scholar
Evans, A. G.and Cannon, R. M. (1989). Mater. Sci. Forum MSFOEP 43, 243–268. msf, MSFOEP CrossRefGoogle Scholar
Evans, H. E. (1989). Mater. Sci. Eng. A MSAPE3 120, 139–146. msa, MSAPE3 CrossRefGoogle Scholar
Evans, H. E. (1994). Mater. High Temp. ZZZZZZ 12, 219–227.CrossRefGoogle Scholar
Floro, J. A., Hearne, S. J., Hunter, J. A., Kotula, P., Chason, E., Seel, S. C., and Thompson, C. V. (2001). J. Appl. Phys. JAPIAU 89, 4886–4897. jap, JAPIAU CrossRefGoogle Scholar
Goto, T., Anderson, O. L., Ohno, I., and Yamamoto, S. (1989). J. Geophys. Res. JGREA2 94, 7588–7602. jgr, JGREA2 CrossRefGoogle Scholar
Grabke, H. J. (1999). Intermetallics IERME5 7, 1153–1158. iez, IERME5 CrossRefGoogle Scholar
Huntz, A. M. (1988). Meas. Sci. Technol. MSTCEP 4, 1079–1088. mst, MSTCEP Google Scholar
Kanthal Appliance Heating Alloys Handbook, The Kanthal Corporation, Bethel, CT.Google Scholar
Levin, I.and Brandon, D. (1998). J. Am. Ceram. Soc. JACTAW 81, 1995–2012. jac, JACTAW CrossRefGoogle Scholar
Messaoudi, K., Huntz, A. M., and Di Menza, L. (2000). Oxid. Met. ZZZZZZ 53, 49–75.CrossRefGoogle Scholar
Nix, W. D.and Clemens, B. M. (1999). J. Mater. Res. JMREEE 14, 3467–3473. jmr, JMREEE CrossRefGoogle Scholar
Noyan, I. C. and Cohen, J. B. (1987). Residual Stress (Springer-Verlag, New York).CrossRefGoogle Scholar
Pilling, N. B.and Bedworth, R. E. (1923). J. Inst. Met. JIMEAP 29, 529–582. jil, JIMEAP Google Scholar
Sarioglu, C., Blachere, J. R., Pettit, F. S., and Meier, G. H. (1997). In Microscopy of Oxidation 3, edited by S. B. Newcomb and J. A. Little (The Institute of Materials, London), pp. 41–51.Google Scholar
Sarioglu, C., Schumann, E., Blachere, J. R., Pettit, F. S., and Meier, G. H. (2000). Mater. High Temp. ZZZZZZ 17, 109–115.CrossRefGoogle Scholar
Schumann, E., Sarioglu, C., Blachere, J. R., Pettit, F. S., and Meier, G. H. (2000). Oxid. Met. OXMEAF 53, 259–272. oxm, OXMEAF CrossRefGoogle Scholar
Schütze, M. (1997). Protective Oxide Scales and their Breakdown (Wiley, Chichester).Google Scholar
Stott, F. H.and Atkinson, A. (1994). Mater. High Temp. ZZZZZZ 12, 195–207.CrossRefGoogle Scholar
Tortorelli, P. F., More, K. L., Specht, E. D., and Zschack, P. (2003). Mater. High Temp. ZZZZZZ 20, 303–310.Google Scholar
Veal, B. W. (personal communication).Google Scholar