Thermodynamic Modeling and Solidification Simulation of Ti-Al-Cr alloys

Published online by Cambridge University Press:  03 March 2011

Y. Yang
Affiliation:
CompuTherm LLC, Madison, Wisconsin 53719, USA
B.P. Bewlay
Affiliation:
General Electric Global Research, Schenectady, New York 12301, USA
Y.A. Chang
Affiliation:
University of Wisconsin-Madison, Madison, Wisconsin 53706, USA
Get access

Abstract

Titanium aluminide based alloys are candidate materials for high temperature structural applications. They are typically alloyed with elements such as Nb, Ta, Mo, Cr and B for property enhancement. To understand the relationship between microstructure and alloy composition/processing condition, detailed models of phase equilibria in multicomponent Ti-Al based alloys are needed. In this work, we developed thermodynamic models for the phases in the Ti-Al-Cr system based on critically assessed binary models and ternary experimental data in literature, using the CALPHAD approach. Isothermal sections at 1200, 1150, 1000 and 800°C, and the liquidus projection, were calculated from the currently developed thermodynamic models; these are in satisfactory agreement with experimental data. Isopleths were calculated at specified Cr concentrations, and solidification paths were simulated under the Scheil conditions for a range of Ti-Al-Cr alloys. From the calculated phase diagrams and solidification paths, the effect of Cr on the microstructure of Ti-Al alloys can be understood.

Keywords

Type
Research Article
Copyright
Copyright © Materials Research Society 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Wu, X., Intermetallics, 14, 1114 (2006).Google Scholar
2. Kaufman, L., and Nesor, H., Can Metall Quart, 14, 221 (1975).Google Scholar
3. Yang, Y., Bewlay, B.P. and Chang, Y. A., J Phase Equilib Diff, 28, 107 (2007).Google Scholar
4. Hayes, F.H., J. Phase Equilib, 13, 79 (1992).Google Scholar
5. Raghavan, V., J. Phase Equilib, 26, 349 (2005).Google Scholar
6. Bochvar, N. et al. ., Al – Cr – Ti. Effenberg, Günter, Ilyenko, Svitlana (ed.). Springer Materials - The Landolt-Börnstein Database, Springer-Verlag Berlin Heidelberg, (2009).Google Scholar
7. Ence, E. et al. ., Wright Air Develop. Division, Techn. Rep., 60 (1960).Google Scholar
8. Nakayama, Y. et al. ., Metall Mater Trans A, 24, 141 (1993).Google Scholar
9. Brady, M. P. et al. ., Scr Metall Mater, 32, 1659 (1995).Google Scholar
10. Hao, S. and Zeng, L., Acta Metall Sin (China), 31, B152 (1995).Google Scholar
11. Jewett, T. J. and Dahms, M., Scr Metall Mater, 32, 1533 (1995).Google Scholar
12. Jewett, T. J. and Dahms, M., Z Metallkd, 87, 254 (1996).Google Scholar
13. Jewett, T. J. et al. , Intermetallics, 4, 543 (1996).Google Scholar
14. Jewett, T. J. et al. , Mater Sci Eng A, 225, 29 (1996).Google Scholar
15. Schwanold, G. and Inden, G., Revue de Metallurgie (France), 93, 121 (1996).Google Scholar
16. Park, J. Y. et al. ., Scr Mater, 36, 795 (1997).Google Scholar
17. Kainuma, R. et al. ., Intermetallics, 8, 855 (2000).Google Scholar
18. Mabuchi, H. et al. ., Mater. Trans., JIM, 38, 560 (1997).Google Scholar
19. Ichimaru, M. et al. ., J Jpn Inst Light Met, 51, 640 (2001).Google Scholar
20. Chen, H. et al. ., Metall Mater Trans A, 40, 2980 (2009).Google Scholar
21. Shao, G. and Tsakiropoulos, P., Intermetallics, 7, (1999).Google Scholar
22. Kaufman, L., Niob Sci Tech, 107 (2001).Google Scholar
23. Yang, Y. and Bewlay, B.P., Intermetallics, in preparation (2010).Google Scholar
24. Witusiewicz, V.T. et al. ., J. Alloy Compd, 465, 64 (2008).Google Scholar
25. Du, Y. and Schuster, J.C., Scand J Metall, 31, 25 (2002).Google Scholar
26. Huang, W. and Chang, Y.A., Intermetallics, 7, 863 (1999).Google Scholar
27. Chen, S.L. et al. ., Calphad, 26, 175 (2002).Google Scholar
28. Scheil, E., Z Metallkd, 34, 242 (1942).Google Scholar