Template-Assisted Growth of Tungsten Oxide Nanorods on Substrates and Their Electrochemical Properties

Published online by Cambridge University Press:  01 February 2011

Sun Hwa Park ,
Jaeyong Song ,
Hyun Min Park  and
Hyunung Yu
Sun Hwa Park
Affiliation:
[email protected], University of Science and Technology, Daejeon, Korea, Republic of
Jaeyong Song
Affiliation:
[email protected], Korea Research Institute of Standard and Science, Daejeon, Korea, Republic of
Hyun Min Park
Affiliation:
[email protected], Korea Research Institute of Standard and Science, Daejeon, Korea, Republic of
Hyunung Yu
Affiliation:
[email protected], Korea Research Institute of Standard and Science, Daejeon, Korea, Republic of
Get access

Abstract

Tungsten oxide nanorods (TONs) with the diameters of 40 nm and the length of 130 nm have been synthesized on substrates using two step electrochemical anodizing processes. The TONs were vertically well-ordered on the substrates with the average interdistance of 100 nm. The TONs had amorphous structure and was mainly composed of W, Al, and O elements, of which the contents varied gradually along the nanorod length from the top surface to the bottom. The cyclic voltammograms (CVs) and galvanostatic charge-discharge analyses showed that TONs had the typical electrochemical pseudocapacitive features of rectangular CV hysteresis and symmetric charge-discharge behaviors, respectively. When the TONs were heat-treated at 600℃ in vacuum, they showed the maximum specific capacitance of 660 ㎌/cm2, which was higher, by an order of magnitude, than that (68 ㎌/cm2) of the TONs annealed at 300 ℃ in ambient atmosphere.

Keywords

nanostructureelectrochemical synthesisenergy storage
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1258: Symposia P/Q/R – Low-Dimensional Functional Nanostructures-Fabrication, Characterization and Applications , 2010 , 1258-Q04-14
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Arico, A.S. Bruce, P. Scrosati, B. Tarascon, J.M. and Schalkwijk, W. Van. Nature mater. 4, 366–377 (2005).Google Scholar
2 Gubbala, S. Thangala, J. Sunkara, M.K. Sol. Energy Mater. Sol. Cells. 91, 813–820 (2007).Google Scholar
3 Huang, C.C. Xing, W. and Zhuo, S.P. Scripta Mater. 61, 985–987 (2009).Google Scholar
4 Deb, B. Desai, S. Sumanasekera, G.U. and Sunkara, M.K. Nanotechnology 18, 285501 (2007).Google Scholar
5 Nazar, L.F. Goward, G. Leroux, F. Duncan, M. Huang, H. Kerr, T. Gaubicher, J. Int. J. Inorg. Mater. 3, 191–200 (2001).Google Scholar
6 Mozalev, A. Sakairi, M. and Takahashi, H. J. Electrochem. Soc. 151 (11) F257–F268 (2004).Google Scholar
7 Simon, P. gogotsi, Y. Nature mater. 7, 846–854 (2008).Google Scholar
8 Gubbala, S. Thangala, J. Sunkara, M.K. Sol. Energy Mater. Sol. Cells. 91, 813–820 (2007)Google Scholar
9 Liao, C.C. Chen, F.R. Kai, J.J, Sol. Energy Mater. Sol. Cells. 90, 1147–1155 (2006).Google Scholar
10 Mozalev, A. Khatko, V. Bittencourt, C. Hassel, A.W. Gorokh, G. Llobet, E. and Correig, X. Chem. Mater. 20, 6482–6493 (2008).Google Scholar
11 Sullivan, J. P. O', Wood, G. C. Proc. Roy. Soc. Lond. A 317, 511–543 (1970)Google Scholar
12 Girginov, A. Bojinov, M. J. of Univ. Chem. Technol. Metal. 43, 1, 29–36 (2008).Google Scholar
13 Tatarenko, N. I. Mozalev, A. M. Solid-State Elect. 45, 1009–1016 (2001).Google Scholar
14 Senthil, K. and Yong, K. Nanotechnology. 18, 395604 (2007).Google Scholar
15 Granquest, C.G. (Ed.), Handbook of Inorganic Electrochromic Materials, (Elsevier, Amsterdam, 1995) pp. 38–41.Google Scholar
16 Shigesato, Y. Murayama, A. Kamimori, T. and Matsuhiro, K. Appl. Surf. Sci. 33/34, 804 (1988).Google Scholar
17 Brezesinski, T. Wang, J. Tolbert, S.H. and Dunn, B. Nature Mater. 9, 146–151 (2010)Google Scholar
18 Wu, M.S. Appl. phys. lett. 87, 153102 (2005)Google Scholar