Synthesis of A1–xA'xNbO3 (A=Na+, K+; A'= La3+, Sr2+) and its Electrical Properties

Published online by Cambridge University Press:  15 February 2011

W. Sugimoto ,
T. Tahara ,
Y. Sugahara  and
K. Kuroda
W. Sugimoto
Affiliation:
Department of Applied Chemistry, Waseda University, Ohkubo 3, Shinjuku-ku, Tokyo 169, Japan
T. Tahara
Affiliation:
Department of Applied Chemistry, Waseda University, Ohkubo 3, Shinjuku-ku, Tokyo 169, Japan
Y. Sugahara
Affiliation:
Department of Applied Chemistry, Waseda University, Ohkubo 3, Shinjuku-ku, Tokyo 169, Japan
K. Kuroda
Affiliation:
Department of Applied Chemistry, Waseda University, Ohkubo 3, Shinjuku-ku, Tokyo 169, Japan
Get access

Abstract

Polycrystalline samples of A1–xA'xNbO3 (A=Na+, K+; A'= La3+, Sr2+) were prepared by solid-state reactions and the relationship between the structure and electrical properties was examined. Single-phase products were obtained for Na1–xLaxNbO3 (x ≤0.1), K1–xLaxNbO3 (x ≤0.15), Na1–xSrxNbO3 (x ≤0.3), and K1–xSrxNbO3 (x ≤0.5). The structures of the sodium-containing compounds and potassium-containing compounds were indexed according to a pseudocubic and cubic symmetry, respectively. The resistivity measurements showed semiconductive behavior for the lanthanum-containing samples. The strontium-containing samples showed semiconducting properties for x ≤0.2, while a transition to metallic conduction at low temperature was observed for x >0.2.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 453: Symposium R – Solid State Chemistry of Inorganic Materials , 1996 , 361
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCE

1. Kumada, N., Muramatu, S., Muto, F., and Kinomura, N., J. Solid State Chem. 73, 33 (1988).Google Scholar
2. Geselbracht, M.J., Richardson, T.J., and Stacy, A.M., Nature 345, 324 (1990).Google Scholar
3. Rzeznik, M.A., Geselbracht, M.J., Thompson, M.S., and Stacy, A.M., Angew. Chem. Int. Ed. Engl. 32, 254 (1993).Google Scholar
4. Meissner, V.W., Franz, H., and Westerhoff, H., Ann. Phys. 17, 593 (1933).Google Scholar
5. Ridgley, D. and Ward, R., J. Am. Ceram. Soc. 77, 6132 (1955).Google Scholar
6. Hessen, B., Sunshine, S.A., Siegrist, T., and Jimenez, R., Mat. Res. Bull. 26, 85 (1991).Google Scholar
7. Isawa, K., Sugiyama, J., Matsuura, K., Nozaki, A., and Yamauchi, H., Phys. Rev. B 47, 2849 (1993).Google Scholar
8. Isawa, K., Sugiyama, J., and Yamauchi, H., Phys. Rev. B 47, 11426 (1993).Google Scholar
9. Isawa, K., Itti, R., Sugiyama, J., Koshizuka, K., and Yamauchi, H., Phys. Rev. B 49, 3534 (1994).Google Scholar
10. Sugiyama, J., Isawa, K., and Yamauchi, H., Solid State Commun. 95, 181 (1995).Google Scholar
11. Krylov, E.I., Doki. Akad. Xauk. S.S.S.R. 104, 246 (1955).Google Scholar
12. Kreiser, R.R. and Ward, R., J. Solid State Chem. 1, 368 (1970).Google Scholar
13. Svensson, G. and Werner, P-E., Mat. Res. Bull. 25, 9 (1990).Google Scholar
14. Casais, M.T., Alonso, J.A., Rasines, I., and Hidalgo, M.A., Mat. Res. Bull. 30, 201 (1995).Google Scholar
15. McCarthy, G.J. and Greedan, J.E., Inorg. Chem. 14, 772 (1975).Google Scholar
16. Fayolle, J.P., Studer, F., Desgurdin, G., and Raveau, B., J. Solid State Chem. 13, 57 (1975).Google Scholar
17. Studer, F., Allais, G., and Raveau, B., J. Phys. Chem. Solids 41, 1187 (1980).Google Scholar
18. Ishikawa, K., Adachi, G., Tauida, M. and Shiokawa, J.. Bull. Chem. Soc. Jpn. 54, 159 (1981).Google Scholar
19. Ishikawa, K., Adachi, G., Hasegawa, M., Sato, K., and Shiokawa, J., J. Electrochem. Soc. 128, 1374 (1981).Google Scholar
20. Ishikawa, K., Adachi, G., and Shiokawa, J., Bull. Chem. Soc. Jpn. 55, 3317 (1982).Google Scholar
21. Ishikawa, K., Adachi, G., and Shiokawa, J., Mat. Res. Bull. 18, 653 (1983).Google Scholar
22. Kopnin, E.M., Istomin, S.Y., D'yachenko, O.G., Antipov, E.V., Bordet, P., Capponi, J.J., Chaillout, C., Marezio, M., de Brion, S., and Souletie, B., Mat. Res. Bull. 30, 1379 (1995).Google Scholar
23. Ellis, B., Doumerc, J.P., Pouchard, M., and Hagenmuller, P., Mat. Res. Bull. 19, 1237 (1984).Google Scholar
24. Ellis, B., Doumerc, J.P., Dordor, P., Pouchard, M. and Hagenmuller, P., Solid State Commun. 51, 913 (1984).Google Scholar
25. Sakowski-Cowley, A.C., Lukaszewicz, K., and Megaw, H.D., Acta Cryst. 18, 851 (1965).Google Scholar
26. Hewat, A.W., J. Phys. C 6, 2559 (1973).Google Scholar
27. Shannon, R.D., Acta Crystallogr. A32, 751 (1976).Google Scholar