Suppression of the Phase Transition and Agglomeration of TiSi2 by Addition of Zr Element

Published online by Cambridge University Press:  10 February 2011

Sanghyun Yoon  and
Hyeongtag Jeon
Sanghyun Yoon
Affiliation:
Division of Materials Science and Engineering, CPRC, Hanyang Univ., Seoul, Korea, 133-791
Hyeongtag Jeon
Affiliation:
Division of Materials Science and Engineering, CPRC, Hanyang Univ., Seoul, Korea, 133-791
Get access

Abstract

The formation of C49 TiSi2 phase at high temperatures was investigated by adding the Zr contents in Ti-silicide film. Stabilizing the C49 TiSi2 phase which exhibits lower surface and interface energies than those of the C54 TiSi2 phase at high temperatures was expected to suppress the problems of Tisilicide, such as the phase transition and the film agglomeration. The thin films of Ti and Zr were codeposited (40 nm) on Si substrates in the dual e-beam evaporation system equipped with an ion pump and its base pressure of ∼5 × 10−9 torr. The amounts of Zr contents (5 and 10 atomic %) added on Tisilicide were monitored by in-situ quartz crystal monitor. Immediately after the deposition, this film was annealed by ex-situ vacuum furnace at temperatures between 600 °C and 900 °C in 100 °C increments. The identification of the phase and the chemical composition were investigated by XRD and AES, respectively. The surface and interface morphologies were examined using cross-sectional TEM. The phase transition temperature of TiSi2 was raised with increasing Zr contents. The agglomeration of TiSi2 film was also suppressed by adding Zr element and much improved interface morphologies were observed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 514: Symposium I – Advanced Interconnects & Contact Materials & Processes for… , 1998 , 225
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Muraka, S. P., J. Vac. Sci. Technol. 17, 775(1980)10.1116/1.570560Google Scholar
[2] Nemanich, R. J., Fiordalice, R. and Jeon, H., J. Quantum Electron. 25, 997(1989)Google Scholar
[3] Ottaviani, G. and Nobili, C., Thin Solid Films 163, 111(1988)Google Scholar
[4] Joswig, H., Kohlhase, A. and Kucher, P., Thin Solid Films 175, 17(1989)Google Scholar
[5] Beyers, R. and Sinclair, R., J. Appl. Phys. 57, 5240(1985)10.1063/1.335263Google Scholar
[6] Colgan, E. G., Clevenger, L. A. and Cabral., C. Jr., Appl. Phys. Lett. 65, 2009(1994)Google Scholar
[7] Jeon, H., Sukow, C. A., Honeycutt, J. W., Rozgonyi, G. A. and Nemanich, R. J., J. Appl. Phys. 71, 4269(1992)Google Scholar
[8] Hensel, J. C., Vandenderg, J. M., Unterwald, F. C. and Maury, , Appl. Phys. Lett. 51, 1100(1987)10.1063/1.98753Google Scholar
[9] Chou, T. C., Wong, C. Y. and Tu, K. N., J. Appl. Phys. 62, 2275 (1987)10.1063/1.339483Google Scholar
[10] Sukow, C. A. and Nemanich, R. J., J. Mater. Res. 9, 1214 (1994)10.1557/JMR.1994.1214Google Scholar
[1] Dao, Y., Edwards, A. M., Ying, H., Chen, Y. L., Sayers, D. E. and Nemanich, R. J., Appl. Phys. Lett. 65(19), 7(1994)Google Scholar
[12] Dao, Y., Sayers, D. E. and Nemanich, R. J., J. Appl. Phys. 78(11), 6584(1995)Google Scholar
[13] Pomoni, K. and Salmi, J., J. Phy. D(Appl. Phys) 24, 727(1991)Google Scholar
[14] Lin, J. H., Hsich, W. Y. and Chen, L. J., J. Appl. Phys. 79, 9123(1996)Google Scholar
[15] Setton, M. and van der Spiegel, J., J. Appl. Phys. 70, 3193 (1991)Google Scholar
[16] Jeon, H., Yoon, G. J. and Nemanich, R. J., Thin Solid Films, 299, 178(1997)Google Scholar