Self-Propagating, High Temperature Synthesis As A Technique To Join Metals

Published online by Cambridge University Press:  15 February 2011

J. A. Hawk
Affiliation:
U. S. Bureau of Mines, Albany Research Center, Albany, Oregon 97321-2198.
A. V. Petty
Affiliation:
U. S. Bureau of Mines, Albany Research Center, Albany, Oregon 97321-2198.
C. P. Dogan
Affiliation:
U. S. Bureau of Mines, Albany Research Center, Albany, Oregon 97321-2198.
J. C. Rawers
Affiliation:
U. S. Bureau of Mines, Albany Research Center, Albany, Oregon 97321-2198.
Get access

Abstract

Self-propagating, high temperature synthesis (SHS) can be used to bond both similar and dissimilar metals. A unique feature of this technique is the ability to stack either metal foils or metal foils and powder, and to process them to form two-dimensional, layered composites with a “graded” intermetallic interface between layers. This process can also be used to modify a surface for corrosion or wear resistance. To date Bureau of Mines research has focused on making iron-, titanium-, and nickel-aluminum composites. The elemental metal foils are stacked and placed in a hot press, and the temperature is raised until the composite sandwich undergoes the SHS reaction. At approximately 660°C (i.e., the melting point of aluminum), the aluminum reacts with the transition metal to form intermetallic phases. The SHS process is mass and energy limited; i.e., mass transport controls the chemical reaction rates, while the energy liberated by the chemical reaction is distributed to the surroundings by heat conduction, convection and radiation.

Type
Research Article
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Munir, Z. A., Ceram. Bull. 67, 342 (1988).Google Scholar
2. Subrahmanyam, J. and Vijayakumar, M., J. Mater. Sci. 27, 6249 (1992).Google Scholar
3. Rawers, J. C., Wrzesinski, W. R., Roub, E. K. and Brown, R. R., Mater. Sci. Technol. 6, 187 (1990).Google Scholar
4. Rawers, J. C. and Wrzesinski, W. R., Scripta Metall. Mater. 24, 1985 (1990).Google Scholar
5. Rawers, J. C. and Wrzesinski, W. R., J. Mater. Sci. 24, 2877 (1992).Google Scholar
6. Merzhanov, A. G., Fizik. Khim. Soverem. Problem, 6 (1983).Google Scholar
7. Naiberdenko, Y. S. and Itin, V. I., Combust. Explos. Shock Waves USSR 11,293 (1975).Google Scholar
8. Serkisyan, A. R., Dolukhanyan, S. K., Borovinskaya, I. P. and Merzhanov, A. G., Combust. Explos. Shock Waves USSR 14, 310 (1978).Google Scholar
9. Rogachev, A. S., Mukasyan, A. S. and Merzhanov, A. G., Dokl. Phys. Chem. 297, 1240 (1987).Google Scholar
10. Wrzesinski, W. R. and Rawers, J. C., J. Mater. Sci. Lett. 9, 432 (1990).Google Scholar
11. Maupin, H.E. and Rawers, J. C., J. Mater. Sci. Lett. 12, 165 (1993).Google Scholar
12. Maupin, H. E., Rawers, J. C. and Hawk, J. A., in International Conference on Advanced Synthesis of Engineered Structural Materials (ASM, Materials Park, OH, 1993), p. 9.Google Scholar
13. Anselmi-Tamburini, U. and Munir, Z. A., J. Appl. Phys. 66, 5039 (1989).Google Scholar
14. Anselmi-Tamburini, U. and Munir, Z. A., in Combustion and Plasma Synthesis of High-Temperature Materials (VCH Publishers, New York, 1990) p. 100.Google Scholar
15. Wright, J. K., Wright, R. N. and Moore, G. A., Scripta Metall. Mater. 28, 501 (1993).Google Scholar
16. Rabin, B. H., J. Am. Ceram. Soc. 75, 131 (1992).Google Scholar