“Recoil” Compressive Strength Test and the Evolution of Compressive Behavior in PAN-Based Carbon Fibers

Published online by Cambridge University Press:  15 February 2011

Hao Jiang ,
S. Damodaran ,
A. S. Abhiraman ,
P. Desai  and
S. Kumar
Hao Jiang
Affiliation:
Lawrence Associates Incorporated, Dayton, OH
S. Damodaran
Affiliation:
3M Co, MN
A. S. Abhiraman
Affiliation:
Georgia Institute of Technology, Atlanta, GA
P. Desai
Affiliation:
Georgia Institute of Technology, Atlanta, GA
S. Kumar
Affiliation:
Georgia Institute of Technology, Atlanta, GA
Get access

Abstract

The compressive properties of PAN-based carbon fibers were measured with the tensile recoil method. The recoil fracture morphology was also examined. In addition to the axial compression, flexure during recoil affects the test results. Compressive failure may be caused by shear failure and/or bending buckling of the microfibrils/fibrils. Study of the evolution of compressive and other mechanical properties discloses that, in general, the compressive strength bears a similar tendency to the tensile strength and torsion modulus up to the carbonization temperature of 1500 °C. However, the relative rate of evolution is different. To some extent, the bending buckling mechanism may relate to the structural units which govern the tensile strength.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 305: Symposium I – High-Performance Polymers and Polymer Matrix Composites , 1993 , 135
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Allen, S. R., J. Mat. Sci. 22, 853 (1987).Google Scholar
[2] Jiang, Hao, Abhiraman, A. S. and Tsui, K., 1993 (to be published in “Carbon”).Google Scholar
[3] Wang, C. S., Bai, S. J. and Price, B. P., Proc. ACS, Div. Polym. Mat. Sci. Engr. 61, 550 (1989).Google Scholar
[4] Damodaran, S., Ph. D. Thesis, Georgia Tech., Nov. 1991.Google Scholar
[5] Johnson, J. W. and Thorne, D. J., Carbon 7, 659 (1969).Google Scholar
[6] Thorne, D. J., Gough, V. J. and Hipkiss, G., Fiber Sci. and Technol. 3, 119 (1970).Google Scholar
[7] Cooper, G. A. and Mayer, R, H, J. Mat. Sci. 6, 60 (1971).CrossRefGoogle Scholar
[8] Jones, W. R. and Johns, J. W., Carbon 9, 645 (1971).Google Scholar
[9] Beetz, C. P. Jr., Fiber Sci. Technol. 16, 45 (1982).Google Scholar
[10] Dasilva, J. L. G. and Johnson, D. J., J. Mat. Sci. 19, 3201 (1984).Google Scholar
[11] Johnson, D. J. in Chemistry and Physics of Carbon Vol.20 edited by Thrower, P. A. (Marcel Dekker, Inc., N. Y., 1987), p. 46.Google Scholar
[12] Tsushima, E., 34th International SAMPE symposium (1989) pp. 2042.Google Scholar
[13] Perepelkin, K. E., Klynchnikova, N. V. and Kulikova, N. A., Khimicheskie Volokna No.2, p36 (1989)Google Scholar
[14] Dobb, M. G., Johnson, D. J. and Park, C. R., J. Mat. Sci. 25, 829 (1990).Google Scholar
[15] Vezie, D. L. and Adams, W. W., J. Mat. Sci. Lett. 9, 883 (1990).CrossRefGoogle Scholar
[16] Smith, S. (private communication).Google Scholar
[17] Huh, W., Kumar, S., Helminiak, T. E. and Adams, W. W., ANTEC'90, (1990) pp. 1245.Google Scholar
[18] Kumar, S., SAMPE Proceedings 35, 224 (1990)Google Scholar