Published online by Cambridge University Press: 22 February 2011
An investigation was undertaken to study the phase relations in Cr3Si alloyed with Mo varying from 10 to 83.5 wt. % of the material. Specimens were prepared from arc-melted buttons that were subsequently heat treated at 1673 K for 200 h and air quenched to room temperature to preserve the high temperature microstructures. Alloys containing more than 20 wt. % Mo were primarily two-phase materials of M3Si and M5Si3, where M is (Cr,Mo). Three alloys contained less than 5 % of a third phase, which also had the M5Si3 crystal structure. Differential thermal analysis (DTA) was performed on several specimens at temperatures up to 2073 K in order to determine a solidus curve for the M3Si phase. Since only one DTA peak was observed in each alloy, the M5Si3 phase must melt above 2073 K, the maximum temperature examined. A preliminary pseudo-binary phase diagram for (Cr,Mo)3Si and a portion of the 1673 K isothermal section of the Cr-Mo-Si ternary phase diagram are presented.