Practical Limitations to Indentation Testing of Thin Films

Published online by Cambridge University Press:  10 February 2011

J. A. Schneider ,
K. F. McCarty ,
J. R. Heffelfinger  and
N. R. Moody
J. A. Schneider
Affiliation:
Sandia National Laboratories, Livermore, CA 94551
K. F. McCarty
Affiliation:
Sandia National Laboratories, Livermore, CA 94551
J. R. Heffelfinger
Affiliation:
Sandia National Laboratories, Livermore, CA 94551
N. R. Moody
Affiliation:
Sandia National Laboratories, Livermore, CA 94551
Get access

Abstract

A method that is becoming increasingly common for measuring the mechanical behavior of thin films is low-load indentation testing. However, there can be complications in interpreting the results as many factors can affect hardness and moduli measurements such as surface roughness and determination of the indentation contact area. To further our understanding, the mechanical properties of thin (50 nm) films of AlN on sapphire substrates were evaluated using a scanning force microscopy (SFM) based pico-indentation device to allow imaging of the surface and indentations. Our primary emphasis was the types of problems or limitations involved in testing very thin, as deposited films in which properties are desired over indentation depths less than 50 nm.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 505 , 1997 , 91
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1)Doerner, M. F., Nix, W. D., ”A method for interpreting the data from depth-sensing indentation instruments,” J. Mater. Res., 1, [ 4], 601 (1986).Google Scholar
2)Oliver, W. C., Pharr, G. M., ”An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments,” J. Mater. Res., 7, [ 6],1564 (1992).Google Scholar
3)Pethica, J. B., Hutchings, R., Oliver, W. C., ”Hardness measurement at penetration depths as small as 20 nm,” Phil. Mag., 48A, [ 4], 593 (1983).Google Scholar
4)Bhushan, B., Kulkarni, S. V., Bonin, W., Wyrobek, J. T., ”Nanoindentation and picoindentation measurements using a capacitive transducer system in atomic force microscopy,” Phil. Mag., 74A, [ 5], 1117 (1996).Google Scholar