A New Criterion for the Degradation of a Defective Spent Fuel Rod under Dry Storage Conditions Based on Nuclear Ceramic Cracking

Published online by Cambridge University Press:  01 February 2011

Lionel Desgranges ,
François Charollais ,
Isabelle Felines ,
Cécile Ferry  and
Jean Radwan
Lionel Desgranges
Affiliation:
[email protected], CEA, DEN/DEC, Saint Paul lez Durance, France
François Charollais
Affiliation:
[email protected], CEA, DEN/DEC, Saint Paul lez Durance, France
Isabelle Felines
Affiliation:
[email protected], CEA, DEN/DEC, Saint Paul lez Durance, France
Cécile Ferry
Affiliation:
[email protected], CEA, DEN/DPC, Saclay, France
Jean Radwan
Affiliation:
[email protected], CEA, DEN/DPC, sacaly, France
Get access

Abstract

Experimental results using environmental SEM on intentionally defected fuel particles showed that oxidation induced cracking could lead to the degradation of HTR coated particles. The interpretation proposed for the swelling resulting from cracking can be extended to irradiated nuclear fuels. That is why a new criterion was proposed to defined safe handling of defective fuel in dry storage condition. This criterion defines the time needed to create an oxidized layer thickness leading to significant cracking.

Keywords

nuclear materialsoxidationstorage
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1124: Symposium Q – Scientific Basis for Nuclear Waste Management XXXII , 2008 , 1124-Q02-06
Copyright
Copyright © Materials Research Society 2009

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. McEachern, R. J. and Taylor, P., J. Nucl. Mater. 254,, 87–121(1998).Google Scholar
2. McEachern, R. J., J. Nucl. Mater. 245, 238–247 (1997).Google Scholar
3. Poulesquen, A., Desgranges, L., Ferry., C., J. Nucl. Mater. 367, 402–410 (2007).Google Scholar
4. McEachern, R. J., Choi, J.W., Kolar, M., Long, W., Taylor, P. and Wood, D.D., J. Nucl. Mater. 249, 58–69 (1997).Google Scholar
5. Bae, K.K., Kim, B.G., Lee, Y.W., Yang, , Park, H.S., J. Nucl. Mat. 209, 274–279 (1994).Google Scholar
6. Quémard, L., Desgranges, L., Bouineau, V., Pijolat, M., Baldinozzi, G., Millot, N., Nièpce, J.C. and Poulesquen, A. submitted to the Journal of Nuclear MaterialsGoogle Scholar
7. Charollais, F. et al. Nuclear Engineering and Design 236, 534–542 (2006).Google Scholar
8. Verfondern, K. (Ed.), 1997. Fuel Performance and Fission Product Behaviour in Gas Cooled Reactors. IAEA Report IAEA-TECDOC-978Google Scholar
9. Desgranges, L. et al., “Study of the evolution of a defective fuel rod in contact with the atmosphere within the framework of the PRECCI Program”, ICEM'01, Proc. of the 8th International Conference on Radioactive Waste Management and Environmental Remediation (Taboas, A., Vanbrabrant, R., Benda, G., Eds), Bruges, Belgium, Sept.30- Oct. 4, 2001.Google Scholar
10. Desgranges, L., Rousseau, G., Ferroud-Plattet, M-P., Ferry, C., Giaccalone, H., Aubrun, I., Delion, P., Untrau, J-M., Mater. Res. Soc.Symp. Proc., 932, paper 18 (2005)Google Scholar
11. Einziger, R.E., Thomas, L.E., Buchanan, H.C., Stout, R.B. J. Nucl. Materials 190, 53 (1992)Google Scholar
12. Poulesquen, A. to be publishedGoogle Scholar