Growth, Structure, and Properties of Uniformly a-Axis Oriented Ferroelectric Bi3.25La0.75Ti3O12 Thin Films on Si(100) Substrates

Published online by Cambridge University Press:  11 February 2011

D. Hesse ,
H. N. Lee ,
N. D. Zakharov  and
U. Gösele
D. Hesse
Affiliation:
Max-Planck-Institut für Mikrostrukturphysik, D-06120 Halle (Saale), Germany
H. N. Lee
Affiliation:
Now with Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831, USA
N. D. Zakharov
Affiliation:
Max-Planck-Institut für Mikrostrukturphysik, D-06120 Halle (Saale), Germany
U. Gösele
Affiliation:
Max-Planck-Institut für Mikrostrukturphysik, D-06120 Halle (Saale), Germany
Get access

Abstract

Uniformly a-axis-oriented, epitaxially twinned Bi3.25La0.75Ti3O12 (BLT) thin films having the major spontaneous polarization entirely along the film normal were grown by pulsed laser deposition on yttria-stabilized zirconia-buffered Si(100) substrates covered with very thin SrRuO3 bottom electrodes. Using SrRuO3 bottom electrodes of a specific low thickness in combination with a relatively high growth rate and a high oxygen pressure, the volume fraction of the BLT (100) orientation, which is competing with the BLT (118) orientation, was increased up to 99%. In this way the growth of fully a-axis-oriented BLT epitaxial films was achieved, attaining a remanent polarization of 32 mC/cm2. Initial fatigue experiments indicated hardly any fatigue after 109 switching cycles.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 748: Symposium U – Ferroelectric Thin Films XI , 2002 , U9.1/T4.1
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. de Araujo, C.A.P., Cuchiaro, J.D., McMillan, L.D., Scott, M.C., and Scott, J.F., Nature 374, 627 (1995).Google Scholar
2. Scott, J. F., Ferroelectric Memories. (Springer, Berlin, 2000).Google Scholar
3. Park, B. H., Kang, B. S., Bu, S. D., Noh, T. W., Lee, J., and Jo, W., Nature 401, 682 (1999).Google Scholar
4. Alexe, M., Harnagea, C., Hesse, D., and Gösele, U., Appl. Phys. Lett. 75, 1793 (1999).Google Scholar
5. Gruverman, A., Appl. Phys. Lett. 75, 1452 (1999).Google Scholar
6. Lettieri, J., Jia, Y., Urbanik, M., Weber, C. I., Maria, J-P., Schlom, D. G., Li, H., Ramesh, R., Uecker, R., and Reiche, P., Appl. Phys. Lett. 73, 2923 (1998).Google Scholar
7. Ishikawa, K. and Funakubo, H., Appl. Phys. Lett. 75, 1970 (1999).Google Scholar
8. Moon, S. E., Song, T. K., Back, S. B., Kwun, S.-I., Yoon, J.-G., and Lee, J. S., Appl. Phys. Lett. 75, 2827 (1999).Google Scholar
9. Lettieri, J., Zurbuchen, M. A., Jia, Y., Schlom, D. G., Streiffer, S. K., and Hawley, M. E., Appl. Phys. Lett. 76, 2937 (2000).Google Scholar
10. Lee, H. N., Visinoiu, A., Senz, S., Harnagea, C., Pignolet, A., Hesse, D., and Gösele, U., J. Appl. Phys. 88, 6658 (2000).Google Scholar
11. Lee, H. N., Senz, S., Pignolet, A., and Hesse, D., J. Europ. Ceram. Soc. 21, 1565 (2001).Google Scholar
12. Lee, H. N., Zakharov, D. N., Senz, S., Pignolet, A., and Hesse, D., Appl. Phys. Lett. 79, 2961 (2001).Google Scholar
13. Lee, H. N. and Hesse, D., Appl. Phys. Lett. 80, 1040 (2002).Google Scholar
14. Watanabe, T. and Funakubo, H., Appl. Phys. Lett. 81, 1660 (2002).Google Scholar
15. Lee, H. N., Senz, S., Visinoiu, A., Pignolet, A., Hesse, D., and Gösele, U., Appl. Phys. A: Mater. Sci. Processes 71, 101 (2000).Google Scholar
16. Lee, H. N., Senz, S., Zakharov, N. D., Harnagea, C., Pignolet, A., Hesse, D., and Gösele, U., Appl. Phys. Lett. 77, 3260 (2000).Google Scholar
17. Lee, H. N., Senz, S., Pignolet, A., and Hesse, D., Appl. Phys. Lett. 78, 2922 (2001).Google Scholar
18. Lee, H. N., Zakharov, D., Senz, S., Pignolet, A., and Hesse, D., Integrated Ferroelectrics 39, 73 (2001).Google Scholar
19. Lee, H. N., Hesse, D., Zakharov, N. D., and Gösele, U., Science 296, 2006 (2002).Google Scholar
20. Lee, H. N., Hesse, D., Zakharov, N. D., Lee, S.K., and Gösele, U., Submitted to J. Appl. Phys. (2002).Google Scholar
21. Asayama, G., Lettieri, J., Zurbuchen, M.A., Jia, Y., Trolier-McKinstry, S., Schlom, D.G., Streiffer, S. K., Maria, J.-P., Bu, S.D., and Eom, C.B., Appl. Phys. Lett. 80, 2371 (2002).Google Scholar
22. Hesse, D., Lee, H.N., and Zakharov, N.D., Submitted to Ferroelectrics (2002).Google Scholar
23. Lee, H. N., Zakharov, D. N., Reiche, P., Uecker, R., and Hesse, D. in Ferroelectric Thin Films X, edited by Gilbert, S. R., Miyasaka, Y., Wouters, D., Trolier-McKinstry, S., and Streiffer, S. K., (Mater. Res. Soc. Proc. 688, Pittsburgh, PA, 2002) pp. C8.5.1–C8.5.6.Google Scholar