Fabrication of Porous SiC Sheets with Controlled Porosity from Waste Clutch Boards

Published online by Cambridge University Press:  31 January 2011

Yuya Domi  and
Shiro Shimada
Yuya Domi
Affiliation:
[email protected], Hokkaido University, Sapporo, Japan
Shiro Shimada
Affiliation:
[email protected], Hokkaido University, Sapporo, Japan
Get access

Abstract

When clutch boards are fabricated as friction sheets in automatic transmission of motorcars, their useless fragments are disposed of. In this study, an effective reuse of their waste clutch boards will be proposed. Clutch boards are composed of diatomaceous earth, carbon powder/fiber and phenol resin. Excess carbon in carbonized clutch boards was reacted with SiO formed from Si and SiO2 at 1500 °C in Ar to produce porous SiC sheets (79% porosity). High temperature treatment at 1700-1900 °C in vacuum made it possible to control the pore size of SiC sheets, having a main pore diameter range of 10 to 20 μm.

SiC sheets with porosity (79% to <60%) were also fabricated by heating carbonized/impregnated sheets with phenol resin in SiO gas at 1500 °C. SiC sheets obtained by the repeated cycle of impregnation/decomposition of resin heating at 1700 °C gave a tensile strength of 19 MPa.

When Aluminum-tri-sec-butoxide (ASB) solution was impregnated into SiC sheets oxidized at 1000-1200 °C in air and heated at 1400-1500 °C in Ar, SiC-mullite composite sheets with porosity (77%) were produced.

Keywords

environmentally benignporosityporosimetry
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1220: Symposium BB – Green Chemistry in Research and Development of Advanced Materials , 2009 , 1220-BB02-06
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Ohno, K., Ceramic Japan, 42 (6) (2007) 431–438. (in Japanese)Google Scholar
2 Oi-Uchisawa, Junko, Obuchi, Akira, Enomoto, Ryuji, Xu, Jiayu, Nanba, Tetsuya, Liu, Shetian, and Kushiyama, Satoshi, Appl. Catal. b32 (2001 257–268.Google Scholar
3 Shimada, S. and Murata, M., J. Am. Ceram. Soc. 92 (2009) 21–25.Google Scholar
4 Fukushima, M., Zhou, Y., Miyazaki, H., Yoshizawa, Y., Hirao, K., Iwamoto, Y., Yamazaki, S. and Nagano, T., J. Am. Ceram. Soc. 89 (2006) 1523–1529.Google Scholar
5 Scheppokat, S., Janssen, R. J. and Claussen, N. C, J. Am Am. Ceram. Soc. 82 (1999) 319–324.Google Scholar
6 Mechnich, P. M ., Schneider, H., Schmucker, M. S. and Saruhan, B. S, J. Am. Ceram. Soc. 81 (1998) 1931–1937.Google Scholar
7 She, J. H., Deng, Z. Y., Daniel-Doni, J. and Ohji, T., J. Mater. Sci. 37 (2002) 3615–3622.Google Scholar