Experiments with in-situ thin film telephone cord buckling delamination propagation

Published online by Cambridge University Press:  11 February 2011

Alex A. Volinsky
Alex A. Volinsky*
Affiliation:
Motorola DigitalDNATM Labs, Process and Materials Characterization Lab, Tempe, AZ 85283, USA, Alex. [email protected]
Get access

Abstract

There are many different stress relief mechanisms observed in thin films. One of the mechanisms involves film debonding from the substrate. In the case of tensile residual stress a network of through-thickness cracks forms in the film. In the case of compressive residual stress thin film buckling and debonding from the substrate in the form of blisters is observed. The buckling delamination blisters can be either straight, or form periodic buckling patterns commonly known as telephone cord delamination morphology.

The mechanics of straight-sided blisters is well understood. Current study relies on the in-situ observation of phone cord delamination propagation in different thin film/substrate systems. Both straight and phone cord delaminations are shown to simultaneously propagate in the same film system. Straight-sided blisters propagate several times faster than the phone cords, and may be followed by thin film fracture along the line of maximum film buckling amplitude. Phone cord delaminations originally start as straight-sided blisters, but then deviate to the periodic phone cord geometry due to the fact that the compressive residual stress in the film is biaxial. Digital analysis of motion recordings shows that partial crack “healing” is present at the curved portions of the phone cords due to the “secondary” buckling pushing thin film back to the substrate. These experimental observations allow for the correct interpretation of the telephone cord delamination morphology.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 749: Symposium W – Morphological and Compositional Evolution of Thin Films , 2002 , W10.7
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Stoney, !G.G., Proc. Roy. Soc. Lond. A82, 72 (1909)Google Scholar
2. Thouless, M.D., J. Vac. Sci. Technol. A 9(4), 2510–2515, (1991)Google Scholar
3. Malzbender, J., de With, G., Thin Solid films 359, 210–214, (2000)Google Scholar
4. Volinsky, A.A., Vella, J.B., Gerberich, W.W., accepted in Thin Solid Films, (2002)Google Scholar
5. Vella, J. B., Adhihetty, I. S., Junker, K., Volinsky, A. A., accepted in International Journal of Fracture, (2002)Google Scholar
6. Volinsky, A.A., Moody, N.R., Gerberich, W.W., Acta Mater. 50(3), pp. 441–466, 2002 Google Scholar
7. Volinsky, A.A., Moody, N.R., Kottke, M.L., Gerberich, W.W., Philosophical Magazine A, 82, 2002 Google Scholar
8. Matuda, N., Baba, S., Kinbara, A., Thin Solid Films 81, 301, (1981)Google Scholar
9. Gille, G., Rau, B., Thin Solid films 120, 109–121, (1984)Google Scholar
10. Seth, J., Raghunath, R., Babu, S.V., J. Vac. Sci. Technol. A 10(2), (1992)Google Scholar
11. Yu, H.Y., Kim, C., Sanday, C., Thin Solid films 196, 229–233, (1991)Google Scholar
12. He, D., Cheng, W., Qin, J., Yue, J., Xie, E., Chen, G., Appl. Surf. Sci., 191, 338, (2002)Google Scholar
13. Coupeau, C., Naud, J.F., Cleymand, F., Goudeau, P., Grilhé, J., Thin Solid Films 353, 194–200, (1999)Google Scholar
14. Cotterell, B., Chen, Z., Key Eng. Mater. 183–187, 187–192, (2000)Google Scholar
15. Cotterell, B., Chen, Z., Int. J. of Fractrure, 104, 169–179, (2000)Google Scholar
16. Cleymand, F., Coupeau, C., Grilhé, J., Scripta mater. 44, 2623–2627, (2001)Google Scholar
17. Jensen, H.M., Acta mater. 41(2), 601–607, (1993)Google Scholar
18. Jensen, H.M., Sheinman, I., Int. J. of Fracture 110, 371–385, (2001)Google Scholar
19. Ortiz, M., Gioia, G., J. Mech. Phys. Solids 42(3), 531, (1997)Google Scholar
20. Crosby, K.M, Bradley, R.M., Phys. Rev. E 59(3), 2542–2545, (1999)Google Scholar
21. Moon, M.-W., Jensen, H.M., Hutchinson, J.W., Oh, K.H., Evans, A.G., J. Mech. Phys Solids, 50(11), 2355, (2002)Google Scholar
22. Audoly, B., Phys. Rev. Let., 83, 4124, (1999)Google Scholar
23. Volinsky, A.A. et al, to be publishedGoogle Scholar