Electromigration Induced Resistance Changes in Passivated Aluminum Thin Film Conductors

Published online by Cambridge University Press:  21 February 2011

U.E. Möckl ,
J.R. Lloyd  and
E. Arzt
U.E. Möckl
Affiliation:
Max-Planck-Institut für Metallforschung, Institut fuit Werkstoffwissenschaft, Seestrafle 92, 7000 Stuttgart 1, Germany
J.R. Lloyd
Affiliation:
also with Digital Equipment Corporation, 75 Reed Road, Hudson MA 07149-2895
E. Arzt
Affiliation:
Max-Planck-Institut für Metallforschung, Institut fuit Werkstoffwissenschaft, Seestrafle 92, 7000 Stuttgart 1, Germany
Get access

Abstract

The relative change in resistance due to electromigration was studied in thin (0.7 μm) film conductors of AI-0.5% Cu Alloy passivated with a 1 μm thick glass passivation using a sensitive AC bridge technique. In contrast to previous experiments performed on unpassivated structures where a roughly linear resistance increase was observed, a saturation value for the resistance increase was observed which was seen to be a function of temperature and the applied current density. The results were found to be consistent with a Shatzkes and Lloyd electromigration model.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 309: Symposium M2 – Materials Reliability in Microelectronics III , 1993 , 301
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Lloyd, J.R. and Koch, R.H., Appl. Phys. Lett. 52, 194 (1988).Google Scholar
2 Shatzkes, M. and Lloyd, J.R., J. Appl. Phys. 59, 3890 (1986).Google Scholar
3 Lloyd, J.R. and Kitchin, J., This Conference.Google Scholar
4 Berenbaum, L., Appl. Phys. Lett. 20, 434 (1972).Google Scholar
5 Hummel, R.E., DeHoff, R.T., and Geier, H.J., J. Phys. Chem. Solids 37, 73 (1976).Google Scholar
6 Schwarz, J.A., Semicond. Intern. March, 96 (1985).Google Scholar
7 Spitzer, S. and Schwartz, S., IEEE Trans. E.D. ED–16, 348 (1969).Google Scholar
8 Lloyd, J.R. and Smith, P.M., J. Vac. Sci. Technol. A 1, 455 (1983).Google Scholar
9 Clement, J.J. and Lloyd, J.R., J. Appl. Phys. 20, 1729 (1992).Google Scholar
10 Möckl, U.E., Untersuchung der Elektromigration in passivierten Al-i %Cu-Leiterbahnen mittels hochaufltsender Widerstandsmessung, Diploma Thesis, University of Stuttgart, Germany, 1992.Google Scholar
11 Sanchez, J.E. Jr., Microstructure and Electromigration Effects in Al and Al Alloy Thin SFilms, PhD Thesis, University of California, 1991.Google Scholar
12 Simmons, R.O. and Balluffi, R.W., Phys. Rev. 117, 52 (1960).Google Scholar