Effects of Supercritical Carbon Dioxide on Adhesive Strength between Micro-sized Photoresist Patterns and Silicon Substrates

Published online by Cambridge University Press:  01 February 2011

Chiemi Ishiyama ,
Akinobu Shibata ,
Masato Sone  and
Yakichi Higo
Chiemi Ishiyama
Affiliation:
[email protected], Tokyo Institute of Technology, Precision and Intelligence Laboratory, 4259 R2-18 Nagatsuta, Midori-ku,, Yokohama, 226-8503, Japan, +81-45-924-5631, +81-45-924-5631
Akinobu Shibata
Affiliation:
[email protected], Tokyo Institute of Technology, Precision and Intelligence Laboratory, 4259 R2-18 Nagatsuta, Midori-ku,, Yokohama, 226-8503, Japan
Masato Sone
Affiliation:
[email protected], Tokyo Institute of Technology, Precision and Intelligence Laboratory, 4259 R2-18 Nagatsuta, Midori-ku,, Yokohama, 226-8503, Japan
Yakichi Higo
Affiliation:
[email protected], Tokyo Institute of Technology, Precision and Intelligence Laboratory, 4259 R2-18 Nagatsuta, Midori-ku,, Yokohama, 226-8503, Japan
Get access

Abstract

Adhesive bend testing for micro-sized photoresist components has been performed to clarify the effects of supercritical CO2 (ScCO2) treatment. Multiple microsized cylindrical specimens were fabricated on a silicon substrate using epoxy-type photoresist. The specimens were ScCO2 treated at a temperature of 323K at a pressure of 15MPa for 30 min, and then, decompressed to atmospheric pressure at two different rates. Double refraction appeared in the SU-8 specimens near by the interface between the SU-8 specimens and a substrate after ScCO2 treatment. Adhesive bend strength of ScCO2 treated specimen with slow decompression process is approximately 60% higher than that of non- ScCO2 treated specimens, however, the strength of the microsized photoresist was slightly degraded by ScCO2 treatment with quick decompression process. All the results suggest that ScCO2 treatment improves the adhesive strength between microsized photoresist components and a silicon substrate by control of the decompression process.

Keywords

adhesivemicroelectro-mechanical (MEMS)thin film
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1052: Symposium DD – Microelectromechanical Systems–Materials and Devices , 2007 , 1052-DD06-26
Copyright
Copyright © Materials Research Society 2008

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Weibel, G. L., Ober, C. K., Microelectro. Eng. 65, 145 (2003)Google Scholar
2 Bonavoglia, B., Storti, G., Morbidelli, M., Rajendran, A. and Mazzotti, M., J. Polym. Phys. Part B. 44, 1531 (2006)Google Scholar
3 Al-Enezi, S., Hellgardt, K. and Stapley, A. G. F., Int. J. Polym. Anal. Charact. 12, 171 (2007)Google Scholar
4 Takashima, K., Higo, Y., Sugiura, S., Shimojo, M., Mater. Trans. 42, 68 (2001)Google Scholar
5 Ishiyama, C., Sone, M. and Higo, Y., Proc. of SPIE. 6533 65331F-1Google Scholar