Effects of Hydrogen on Fatigue Crack Growth of Iron Aluminides

Published online by Cambridge University Press:  22 February 2011

A. Castagna  and
N.S Stoloff
A. Castagna
Affiliation:
Rensselaer Polytechnic Institute, Materials Engineering Department, Troy, NY 12180–3590
N.S Stoloff
Affiliation:
Rensselaer Polytechnic Institute, Materials Engineering Department, Troy, NY 12180–3590
Get access

Abstract

Three Fe-Al alloys, FAP-Y, FA-129, and Fe-35a%Al, containing 16, 28, and 35a%Al, respectively, have been subjected to fatigue crack growth testing in moist air, in oxygen, and in gaseous hydrogen. In each case hydrogen and air were embrittling. Crack growth rates increased significantly as frequency decreased. Fatigue crack growth results have been compared with those for other structural iron-base alloys. Surprisingly, FAP-Y displays the highest crack growth rate of any alloy examined, except at very low levels of stress intensity range. The mechanisms for embrittlement by hydrogen and by moisture in air are discussed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 364: Symposium L – High-Temperature Ordered Intermetallic Alloys–VI , 1994 , 1171
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Liu, C.T., Lee, H.E. and McKamey, C.G., Scripta Met. 23, 875 (1989).Google Scholar
2. McKamey, C.G., DeVan, J.H., Tortorelli, P.F. and Sikka, V.K., J. Mat. Res. 6, 1779 (1991).Google Scholar
3. Castagna, A., Ph.D. Thesis, Rensselaer Polytechnic Institute (1994)Google Scholar
4. Castagna, A. and Stoloff, N. S., Mater, and Design 14, 73 (1993)Google Scholar
5. McEvily, A.J. and Wei, R. P., in Corrosion-Fatigue: Chemistry, Mechanics, and Microstructure, Devereux, O. F., McEvily, A. J., Staehle, R. W., Eds., (NACE, Houston, 1972), NACE-2, 381.Google Scholar
6. Tien, J.K and Richards, R.J., Scripta Metall. 9, 1097 (1975).Google Scholar
7. Tien, J.K., Thompson, A.W., Bernstein, I.M. and Richards, R.J., Met. Trans. A 7A, 821 (1976).Google Scholar
8. Albrecht, J., Bernstein, I.M. and Thompson, A.W., Met. Trans. A 13A, 811 (1982).Google Scholar
9. Louthan, M.R., Caskey, G.R., Donovan, J.A. and Rawl, D.E., Mat. Sci. Eng. 10, 357 (1972).Google Scholar
10. Nowick, A.S. and Burton, J.J., Diffusion in Solids-Recent Developments, 272–302, Academic Press, New York 1975 Google Scholar
11. Roven, H.J. and Nes, E., Acta Met. 39, 1735 (1991).Google Scholar
12. Marrow, T.J., Hippsley, C.A. and King, J.E., Acta Met. 39, 1367 (1991).Google Scholar
13. Cotterill, P.J. and Knott, J.F., Acta Met. 40, 2753 (1992).Google Scholar
14. Hebsur, M.G., Abraham, K.P. and Prasad, Y.V.R.K., Int. J. Fatigue 2, 147 (1980).Google Scholar