Effects of Al3Ti and (Al,Ni)3Ti Addition on the Sintering of TiB2

Published online by Cambridge University Press:  14 February 2012

Masashi Yoshida
Masashi Yoshida*
Affiliation:
Ube National College of Technology, 2-14-1 Tokiwadai, Ube, Yamaguchi 755-8555, Japan
Get access

Abstract

Titanium diboride has been sintered using spark plasma sintering (SPS). With the addition of tetragonal Al3Ti or cubic (Al,Ni)3Ti, the Vickers hardness, Hv, of TiB2 increases up to as high as 2000 by the sintering at 1273K, while that of the sample sintered without additives is as low as 20. Such a remarkable improvement is caused by the improvement of direct link between TiB2 grains in addition to the effect that Al3Ti or (Al,Ni)3Ti fills in the space between TiB2 grains and act as a binder.

Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1373: Symposium S4 – Advanced Structural Materials—2011 , 2012 , imrc-1373-s4-18
Copyright
Copyright © Materials Research Society 2012

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Samsonov, G.V. and Vinitskii, I.M., Handbook of Refractory Compounds, IFI/Plenum, New York, 1980.Google Scholar
2. Wen, G., Li, S.B., Zhang, B.S. and Guo, Z.X., Acta Mater. 49, 1463 (2001).Google Scholar
3. Wang, W., Fu, Z., Wang, H. and Yuan, R., J. Europ. Cer. Soc. 22, 1045 (2002).Google Scholar
4. Einarsrud, M. A., Hagen, E., Pettersen, G. and Grande, T., J.Am. Ceram. Soc. 80, 3013 (1997).Google Scholar
5. Park, J.H., Lee, Y.H., Koh, Y.H., Kim, H.E. and Baek, S.S., J. Am. Cer. Soc. 83, 154 (2000).Google Scholar
6. Yamaguchi, M., Inui, H. and Ito, K., Acta Mater. 48, 307 (2000).Google Scholar
7. Yamaguchi, M., Umakoshi, Y. and Yamane, T., Philos. Mag. A55, 301 (1987).Google Scholar
8. Umakoshi, Y., Yamaguchi, M., Sakagami, T. and Yamane, T., J. Mater. Sci. 24, 1599 (1989).Google Scholar
9. Kim, S.M., Kogachi, M., Kameyama, A. and Morris, D.G., Acta Metall. Mater. 43, 3139 (1995).Google Scholar
10. Fu, Z. Y., Min, X.M. and Yuan, R.Z., Ceramic Transaction Functionally Gradient Materials 34, 411 (1992).Google Scholar
11. Bernard-Granger, G. and Guizard, C., Acta Mater. 55, 3493 (2007).Google Scholar