The Effect of Cu Concentration and Distribution on the Lifetimes of Submicron, Bamboo Al(Cu) Runners

Published online by Cambridge University Press:  10 February 2011

Silva K. Theiss ,
J. A. Prybyla  and
M. A. Marcus
Silva K. Theiss
Affiliation:
Bell Laboratories, Lucent Technologies, 700 Mountain Ave., Murray Hill, NJ 07974
J. A. Prybyla
Affiliation:
Bell Laboratories, Lucent Technologies, 700 Mountain Ave., Murray Hill, NJ 07974
M. A. Marcus
Affiliation:
Bell Laboratories, Lucent Technologies, 700 Mountain Ave., Murray Hill, NJ 07974
Get access

Abstract

We have studied the effect of Cu concentration and initial distribution on the electromigration lifetimes of 0.3 – 0.8 μm wide, ≥ 99% bamboo Al interconnects. The mechanism by which Cu reduces electromigration in polygranular interconnects may not be important in bamboo interconnects, so it is not possible to predict whether Cu will have a positive or negative effect in this case. Samples containing 0.0, 0.5, and 0.9 wt. % Cu were tested at 225° and 2×106 A/cm2. For the Cu-containing samples, two different initial Cu distributions were tested: one in which the Cu was quenched into supersaturated solution within the Al grains (no precipitates) and another with many small, closely-spaced Al2Cu precipitates. We find that Cu still improves the mean time to fail of bamboo lines, although not as dramatically as in polygranular lines. More importantly, it significantly decreases the standard deviation in failure time, thus increasing the time to the first failure. Unlike in polygranular lines, increasing the Cu concentration from 0.5 to 0.9 wt. % has little effect on lifetime, and deliberately forming Cu precipitates prior to electromigration stressing reduces lifetimes. The best performance for submicron, highly bamboo runners was obtained from Al(0.5 wt. % Cu) with no precipitates prior to electromigration stressing.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 473: Symposium J – Materials Reliability in Microelectronics VII , 1997 , 387
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Ames, I., d'Heurle, F.M., and Horstmann, R.E., IBM J. Res. Dev. 14, 461 (1970).Google Scholar
2. d'Heurle, F.M., Metal. Trans. 2, 683 (1971).Google Scholar
3. Frear, D. R., Michael, J. R., Kim, C., Romig, A. D. Jr, Morris, J. R. Jr, Proc. SPIE 1596, 72 (1991).Google Scholar
4. Anthony, T.R., in Atomie Transport in Solids and Liquids, edited by Lodding, A. and Lagerwall, T. (Verlag der Zeitschrift für Naturforshung, Tübingen, 1971) p. 138.Google Scholar
5. Oates, A.S. and Barr, D.L., J. Electron. Mater. 23, 63 (1994);Google Scholar
Oates, A.S., J. Appl. Phys. 79, 163 (1996).Google Scholar
6. Doan, N.V. and Bocquet, J.L., Thin Solid Films 25, 15 (1975).Google Scholar
7. Hu, C.-K., Thin Solid Films 260, 124 (1995).Google Scholar
8. Copel, M., Rodbell, K.P., and Tromp, R.M., Appl. Phys. Lett. 68, 1625 (1996).Google Scholar
9. Rose, J.H., Appl. Phys. Lett. 61, 2170 (1992).Google Scholar
10. Kim, Choongun and Morris, J.W. Jr, J. Appl. Phys. 72, 1837 (1992).Google Scholar
11. Nogami, Takeshi and Nemoto, Takenao, AIP Conf. Proc. 373, 198 (1996).Google Scholar
12. Colgan, E.G. and Rodbell, K.P., J. Appl. Phys. 75, 3423 (1994).Google Scholar
13. Knowlton, B.D., Ph.D. Thesis, MIT (1997).Google Scholar
14. Knowlton, B.D., Frank, R.I., and Thompson, C.V., Mat. Res. Soc. Proc. 391, 361 (1995).Google Scholar
15. Witt, C., private communication, based on Blech testers with linewidths and microstructure similar to those used here.Google Scholar
16. Marcus, Matthew A. and Eric Bower, J., J. Appl. Phys., submitted.Google Scholar
17. Theiss, Silva K. and Prybyla, J. A., Mat. Res. Soc. Proc. 428, 207 (1996).Google Scholar
18. Cu increases the electrical resistance of Al lines. Also, Al2Cu precipitates, which are more likely to form during processing as the Cu concentration increases, can cause corrosion during patterning.Google Scholar