Dielectric Characteristics of Donor Doped Nonlead Ba(Cu1/3Nb2/3)O3 Perovskite Material Synthesized by Microwave-assisted Citrate-nitrate Sol-gel Route

Published online by Cambridge University Press:  01 February 2011

Alp Manavbasi  and
Jeffrey C LaCombe
Alp Manavbasi
Affiliation:
[email protected], University of Nevada, Reno, Materials Engineering, 1664 N Virginia St, Reno, NV, 89557, United States, 775-682-6885
Jeffrey C LaCombe
Affiliation:
[email protected], University of Nevada, Reno, Chem. & Met. Engineering, Reno, NV, 89557, United States
Get access

Abstract

Nonlead perovskite type, Ba(Cu1/3Nb2/3−xWx)O3 (x = 0, 0.025), ferroelectric ceramic powders (BCN) were prepared by the microwave-assisted citrate-nitrate sol-gel technique. The gel was formed from a stable and homogeneous sol prepared by mixing stable solutions of barium- and copper-nitrate, tungsten citrate, and peroxo-citrato-niobium precursors. Microwave irradiation of the gel resulted in a dark, fluffy precursor material after auto-combustion. Calcination of the as-combusted samples produces a single phase with tetragonal splitting in X-Ray diffraction patterns. The crystallite size of the synthesized samples was found to be 41 nm. Particle morphology and the size of nanocrystalline powders were characterized by scanning electron microscopy and photon correlation spectroscopy, respectively. Electrical and dielectric properties of sintered samples were investigated by impedance spectroscopy. The isothermal ac measurements were performed from room temperature, up to 600 °C for W6+ doped and undoped BCN samples.

Keywords

dielectric propertiesferroelectriccombustion synthesis
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 997: Symposium I – Materials and Processes for Nonvolatile Memories II , 2007 , 0997-I06-05
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. http://www.rohs.gov.uk/ Google Scholar
2. Priya, S., Ando, A., and Sakabe, Y., J. Appl. Phys. 94(2), (2003) 1171.Google Scholar
3. Priya, S., Ahn, C.W., and Nahm, S., Ferroelectrics, 322, (2005) 75.Google Scholar
4. Toh, W.S., Garg, A., Xue, J.M., et.al., Integ. Ferro., 62, (2004) 163.Google Scholar
5. Zhang, W., Kumada, N., et.al, J. Sol. St. Chem. 179 (12), (2006) 4052 Google Scholar
6. Hornebecq, V., Raeu, J.M., and Ravez, J., Sol. Stat. Ionics 127, (2000) 231.Google Scholar
7. Livage, J., Henry, M., and Sanchez, C., Prog. Sol. Stat. Chem. 18, (1988) 259.Google Scholar
8. Montanari, G., Costa, A.L., et.al., J Sol-Gel Sci. Tech, 36, (2005) 203.Google Scholar
9. Jansen, C., et.al., In: Occellie, M.L., and Robinson, H. (Eds), "Synthesis of Microporous Materials, Vol. 1, (Van Nostrand Reinhold, NY, 1992) p. 507.Google Scholar
10. Narendar, Y. and Messing, G.L., Chem. Mater. 9, (1997) 580.Google Scholar
11.ZView ver. 2.9, Scribner Associates, Inc.Google Scholar
12. Ono, A., J. Mater. Sci. Lett. 11, (1992) 114.Google Scholar
13. Elissalde, C. and Ravez, J., J. Mater. Chem., 11, (2001) 1957.Google Scholar
14. Rao, K.S., Krishna, P.M., et.al., Mater. Sci. Eng. B 131 (2006) 127.Google Scholar
15. Toh, W.S., Garg, A., Xue, J.M., et.al., Integ. Ferro., 62, (2004) 163.Google Scholar
16. Raju, G.G., "Dielectrics in electric fields", (Mercel Dekker, Inc., NY, 2003).Google Scholar