Chemical Vapor Deposition of ZrxTi1-xO and HfxTi1-xO Thin Films Using the Composite Anhydrous Nitrate Precursors

Published online by Cambridge University Press:  01 February 2011

Qi-Yue Shao ,
Ai-Dong Li ,
Wen-Qi Zhang ,
Di Wu ,
Zhi-Guo Liu  and
Nai-Ben Ming
Qi-Yue Shao
Affiliation:
[email protected] UniversityNational Laboratory of Solid State Microstructures, Materials Science and Engineering DepartmentNanjing Jiangsu 210093China, People's Republic of
Ai-Dong Li
Affiliation:
[email protected], Nanjing University, National Laboratory of Solid State Microstructures, Materials Science and Engineering Department, Nanjing, Jiangsu, 210093, China, People's Republic of
Wen-Qi Zhang
Affiliation:
[email protected], Nanjing University, National Laboratory of Solid State Microstructures, Materials Science and Engineering Department, Nanjing, Jiangsu, 210093, China, People's Republic of
Di Wu
Affiliation:
[email protected], Nanjing University, National Laboratory of Solid State Microstructures, Materials Science and Engineering Department, Nanjing, Jiangsu, 210093, China, People's Republic of
Zhi-Guo Liu
Affiliation:
[email protected], Nanjing University, National Laboratory of Solid State Microstructures, Physics Department, Nanjing, Jiangsu, 210093, China, People's Republic of
Nai-Ben Ming
Affiliation:
[email protected], Nanjing University, National Laboratory of Solid State Microstructures, Physics Department, Nanjing, Jiangsu, 210093, China, People's Republic of
Get access

Abstract

Zr/Ti an Hf/Ti composite nitrate were developed as single-source precursors for deposition of multi-component metal oxide films. X-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS) analyses confirmed that ZrxTi1-xO2 and HfxTi1-xO2 films were successfully prepared by the CVD technique from these composite precursors. The Zr/Ti nitrate can be taken as a solid solution of the individual Zr and Ti nitrate, and the Zr/Ti molar ratio in as-deposited ZrxTi1-xO2 films is nicely consistent with that of the precursor. The Hf/Ti nitrate appears to be a mixture of the Zr and Ti nitrates and the composition of the as-deposited HfxTi1-xO2 films depends remarkably on the heating time of precursor. Both ZrxTi1-xO2 and HfxTi1-xO2 films exhibit trading-off properties between band gap and dielectric constant, which suggesting that ZrxTi1-xO2 and HfxTi1-xO2 can be the promising candidates for gate dielectric application to improve the scalability and reduce the leakage current of the next generation complementary metal-oxide-semiconductor transistor (CMOS) devices.

Keywords

chemical vapor deposition (CVD) (deposition)dielectricfilm
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 917: Symposium E – Gate Stack Scaling – Materials Selection, Role of Interfaces, and Reliability Implications , 2006 , 0917-E05-13
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Wilk, G. D., Wallace, R. M., and Anthony, J. M., J. Appl. Phys. 89, 5243 (2001).Google Scholar
[2] Qiu, X. Y., Liu, H. W., Fang, F., Ha, M. J., and Liu, J. M., Appl. Phys. Lett. 88, 072906 (2006).Google Scholar
[3] Wilk, G. D. and Wallace, R. M., Appl. Phys. Lett. 76, 112 (2000).Google Scholar
[4] Auciello, O., Fan, W., Kabius, B., Saha, S., Carlisle, J. A., Chang, R. P. H., Lopez, C., Irene, E. A., and Baragiola, R. A., Appl. Phys. Lett. 86, 042904 (2005).Google Scholar
[5] Rahtu, A., Ritala, M., and Leskela, M., Chem. Mater. 13, 1528 (2001).Google Scholar
[6] Triyoso, D. H., Hegde, R. I., Zollner, S., Ramon, M. E., Kalpat, S., Gregory, R., Wang, X. D., Jiang, J., Raymond, M., Rai, R., Werho, D., Roan, D., White, B. E. Jr, and Tobin, P. J., J. Appl. Phys. 98, 054104 (2005).Google Scholar
[7] Gilmer, D. C., Colombo, D. G., Taylor, C. J., Roberts, J., Haugstad, G., Campbell, S. A., Kim, H., Wilk, G. D., Gribelyuk, M. A., and Gladfelter, W. L., Chem. Vap. Deposition 4, 9 (1998).Google Scholar
[8] Zhong, L. J., Chen, F., Campbell, S. A., and Gladfelter, W. L., Chem. Mater. 16, 1098 (2004).Google Scholar
[9] Conley, J. F. Jr,.,Ono, Y., Tweet, D. J., Zhuang, W., and Solanki, R., J. Appl. Phys. 93, 712 (2003).Google Scholar
[10] Field, B. O. and Hardy, C. J., J. Chem. Soc., 4428 (1964).Google Scholar
[11] Field, B. O. and Hardy, C. J., J. Chem. Soc., 5278 (1963).Google Scholar
[12] Zhuang, W. W., Conley, J. F., Ono, Y., Evans, D. R., and Solanki, R., Integrated Ferroelectrics 48, 3 (2002).Google Scholar
[13] Li, A. D., Shao, Q. Y., Ling, H. Q., Cheng, J. B., Wu, D., Liu, Z. G., Ming, N. B., Wang, C., Zhou, H. W., Nguyen, B.Y., Appl. Phys. Lett. 83, 3540 (2003).Google Scholar
[14] Shao, Q. Y., Li, A. D., Zhang, W. Q., Wu, D., Liu, Z. G. and Ming, N. B. (submitted).Google Scholar