Building of Protective Coating Against Corrosion by Flame Spraying of Mechanofused Composite Particles

Published online by Cambridge University Press:  01 October 2015

A. Molina-Díaz ,
J. Delgado-Venegas ,
F. Juárez-López ,
G. Velázquez-García  and
R. Cuenca-Álvarez
A. Molina-Díaz
Affiliation:
Instituto Politécnico Nacional-CIITEC, Cerrada de Cecati s/n, Santa Catarina Azcapotzalco, 02250 Mexico D.F., Mexico.
J. Delgado-Venegas
Affiliation:
Instituto Politécnico Nacional-CIITEC, Cerrada de Cecati s/n, Santa Catarina Azcapotzalco, 02250 Mexico D.F., Mexico.
F. Juárez-López
Affiliation:
Instituto Politécnico Nacional-CIITEC, Cerrada de Cecati s/n, Santa Catarina Azcapotzalco, 02250 Mexico D.F., Mexico.
G. Velázquez-García
Affiliation:
Instituto Politécnico Nacional-CIITEC, Cerrada de Cecati s/n, Santa Catarina Azcapotzalco, 02250 Mexico D.F., Mexico.
R. Cuenca-Álvarez
Affiliation:
Instituto Politécnico Nacional-CIITEC, Cerrada de Cecati s/n, Santa Catarina Azcapotzalco, 02250 Mexico D.F., Mexico.
Get access

Abstract

A protective coating was built and assessed in order to reduce the degradation of metallic substrates caused by corrosion damage. Hence, a set of coatings with different configurations, in terms of layer arrangement, was produced by flame-spraying of composite powder (AISI 316L stainless steel coated with an α-alumina layer) onto an AISI 1018 steel substrate. In order to ensure a homogeneous dispersion of phases, a correlation was established between the operating parameters of thermal spraying (roughness and surface temperature of substrate, spraying distance, passing speed) and the splat formation. Then, corrosion damage caused in the coated samples by exposure to a salt spray was monitored through weight measurements and observations with optical and scanning electron microscopy. The results show that corrosion still remains in all cases; however, it proceeds at lower rates for coatings made with composite particles plus an α-alumina layer. The weight loss due to corrosion damage was reduced in approximately 94% as compared with the substrate without protection. Coating adhesion was also improved by an increased substrate roughness, with no need for an intermediate layer.

Keywords

compositespray depositioncorrosion
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1765: Symposium 4A – Advanced Structural Materials—2014 , 2015 , pp. 37 - 44
Copyright
Copyright © Materials Research Society 2015 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Corrosion Costs and Preventive Strategies in the United States, (NACE International, Houston, USA, 2002).Google Scholar
McCafferty, E., Introduction to Corrosion Science, (Springer, USA, 2010).CrossRefGoogle Scholar
ASM Handbook - Volume 13 Corrosion, 9th ed. (ASM International, USA, 1992).Google Scholar
Sá Brito, V.R.S., Bastos, I.N. and Costa, H.R.M., Mater. Des. 41, 282–288 (2012), Switzerland.CrossRefGoogle Scholar
Cuenca-Alvarez, R., Monterrubio-Badillo, C., Juarez-Lopez, F., Ageorges, H. and Fauchais, P., in Advanced Plasma Spray Applications, edited by Jazi, H.S. (InTech, Rijeka, Croatia, 2012), pp. 39–60.Google Scholar
Cuenca-Alvarez, R., Monterrubio-Badillo, C., Ageorges, H. and Fauchais, P., in Advanced Structural Materials-2010, edited by Calderon, H.A., Salinas, A., Balmori, H., and Ishizaki, K., (Mater. Res. Soc. Symp. Proc. 1276, Pittsburgh, PA, 2010), pp. 169–174.Google Scholar
Cuenca-Alvarez, R., Ageorges, H. and Fauchais, P., Mater. Sci. Forum 560, 67–72 (2007).CrossRefGoogle Scholar
Molina-Diaz, A., B.Sc. Thesis (in Spanish), Instituto Politécnico Nacional, México, 2015.Google Scholar
Ramirez-Jaramillo, A., M.Sc. Thesis (in Spanish), Instituto Politécnico Nacional, México, 2010.Google Scholar
Velazquez-García, J.J., M.Sc. Thesis (in Spanish), Instituto Politécnico Nacional, México, 2009.Google Scholar
D7127–13 ASTM Standard, ASTM International, USA 2013.Google Scholar
Parameters for Metaceram 29XXX Alloys - Euctetic Terodyn System 2000 Manual Process, (Castolin Eutectic Corporation, Menomonee Falls, USA, 2006).Google Scholar
B-117 ASTM Standard, ASTM International, USA, 2011.Google Scholar
G1–03 ASTM Standard, ASTM International, USA, 2011.Google Scholar
Corrosion Tests and Standards: Application and Interpretation, 2nd. ed., edited by Baboian, R. (ASTM International, USA, 2005).CrossRefGoogle Scholar
Fauchais, P., Fukumoto, M., Vardelle, A. and Vardelle, M., J. Therm. Spray Technol. 13, 337–360 (2004).CrossRefGoogle Scholar
Chacon, R.R., Ph.D. Thesis (in Spanish), Universidad Carlos III, Madrid, Spain, 2007.Google Scholar
Briones-Rodríguez, C., Mayagoitia-Barragán, V. and Cuenca-Alvarez, R., Mater. Sci. Forum 534-536, 37–40 (2007).CrossRefGoogle Scholar