Atomic Layer Deposition for Improved Stability of Catalysts for the Conversion of Biomass to Chemicals and Fuels

Published online by Cambridge University Press:  22 August 2011

Monika K. Wiedmann ,
Yomaira J. Pagan-Torres ,
Mark H. Tucker ,
James A. Dumesic  and
T. F. Kuech
Monika K. Wiedmann
Affiliation:
Department of Chemical and Biological Engineering, University of Wisconsin-Madison, Madison, WI 53706
Yomaira J. Pagan-Torres
Affiliation:
Department of Chemical and Biological Engineering, University of Wisconsin-Madison, Madison, WI 53706
Mark H. Tucker
Affiliation:
Department of Chemical and Biological Engineering, University of Wisconsin-Madison, Madison, WI 53706
James A. Dumesic
Affiliation:
Department of Chemical and Biological Engineering, University of Wisconsin-Madison, Madison, WI 53706
T. F. Kuech
Affiliation:
Department of Chemical and Biological Engineering, University of Wisconsin-Madison, Madison, WI 53706
Get access

Abstract

Atomic layer deposition (ALD) has been used to coat SBA-15 and functionalized SBA-15 with various metal oxides. Use of SBA-15 coated with 4-10 ALD cycles of titania, alumina, niobia, or zirconia in the acid-catalyzed dehydration of fructose to 5-hydroxymethylfurfural (HMF) resulted in 24-57% conversion, with 0-22% selectivity, at 130 °C with 2 wt % fructose in 4:1 THF:H2O. Propylsulfonic acid functionalized SBA-15 (SBA-15-PrSO3H) had a 25% conversion and 48% selectivity for HMF under the same conditions. SBA-15-PrSO3H was also coated with 2 ALD cycles of titania followed by 8 ALD cycles silica. The deactivation rate constant for SBA-15-PrSO3H was 2.7 x 10-2 h-1 for the dehydration of fructose to HMF in a flow reactor at 130 °C with a feed of 2 wt % fructose in 4:1 THF:H2O. In comparison, the deactivation rate constant for the ALD coated SBA-15-PrSO3H-ALD was 7.9 x 10-3 h-1.

Keywords

atomic layer depositionfilmcatalytic
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1366: Symposium UU – Crystalline Nanoporous Framework Materials—Applications and Technological Feasibility , 2011 , mrss11-1366-uu04-04
Copyright
Copyright © Materials Research Society 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Román-Leshkov, Y., Chheda, J. N. and Dumesic, J. A., Science 312, 1933–1937 (2006).Google Scholar
2. Pagan-Torres, Y. J., Gallo, J. M. R., Pham, H. N., Wang, D., Libera, J. A., Elam, J. W., Marshall, C. L., Datye, A. K. and Dumesic, J. A., manuscript in preparation.Google Scholar
3. Galarneau, A., Nader, M., Guenneau, F., Di Renzo, F. and Gedeon, A., J. Phys. Chem. C 111, 8268–8277 (2007).Google Scholar
4. Zhang, F., Yan, Y., Yang, H., Meng, Y., Yu, C., Tu, B. and Zhao, D., J. Phys. Chem. B 109, 8723–8732 (2005).Google Scholar
5. Ritala, M. and Leskelä, M., Handbook of Thin Film Materials, ed. Nalwa, H. S., (Academic Press: San Diego, CA, 2002) pp. 103–159.Google Scholar
6. George, S. M., Chem. Rev. 110, 111–131 (2010).Google Scholar
7. King, D. M., Zhou, Y., Hakim, L. F., Liang, X., Li, P. and Weimer, A. W., Ind. Eng. Chem. Res. 48, 352–360 (2009).Google Scholar
8. Zhao, D., Huo, Q., Feng, J., Chmelka, B. F. and Stucky, G. D., J. Am. Chem. Soc. 120, 6024–6036 (1998).Google Scholar
9. Margolese, D., Melero, J. A., Christiansen, S. C., Chmelka, B. F. and Stucky, G. D., Chem. Mater. 12, 2448–2459 (2000).Google Scholar
10. Mahurin, S., Bao, L., Yan, W., Liang, C. and Dai, S., J. Non-Crystalline Solids 352, 3280–3284 (2006).Google Scholar
11. Melero, J. A., Stucky, G. D., van Grieken, R. and Morales, G., J. Mater. Chem. 12, 1664–1670 (2002).Google Scholar