Surface Morphology and Island Shape of MOVPE Grown InGaN Nano-Island Ensembles Studied by STM

Published online by Cambridge University Press:  01 February 2011

Subhashis Gangopadhyay ,
Thomas Schmidt ,
Sven Einfetdt ,
Tomohito Yamaguchi ,
Detlef Hommel  and
Jens Falta
Subhashis Gangopadhyay
Affiliation:
[email protected], University of Bremen, Institute of Solid State Physics, Germany
Thomas Schmidt
Affiliation:
[email protected]
Sven Einfetdt
Affiliation:
[email protected]
Tomohito Yamaguchi
Affiliation:
[email protected]
Detlef Hommel
Affiliation:
[email protected]
Jens Falta
Affiliation:
[email protected]
Get access

Abstract

The dependence of the InGaN/GaN(0001) surface morphology on the growth parameters of metal organic vapour phase epitaxy (MOVPE) at 650°C has been investigated using scanning tunneling microscopy. After deposition of InGaN under In-rich growth conditions, a preferential nucleation of islands at defects of the GaN substrate film is found. The islands have a large size (diameter ∼ 80 nm, height ∼10 nm) and show a spiral disc-like shape with an atomically flat surface, and the wetting layer surface appears very smooth. For thicker InGaN layers, In-droplets are formed on top of the large islands and the wetting layer becomes rougher. For InGaN growth at a reduced In partial pressure, hexagonal islands with an atomically flat top surface are formed and pyramidal islands of triangular base with smooth side facet structures are observed. The effects of growth rate and V/III flux ratio on the InGaN surface morphology have also been studied and the results indicate that a slower growth reduces the large island formation probability whereas a high V-III flux ratio enhances it. All findings are discussed in terms of thermal diffusion, In-incorporation and thermal decomposition.

Keywords

nanostructurenucleation & growthnitride
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 892 , 2005 , 0892-FF32-05
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Nakamura, S., Pearton, S. and Fasol, G., The Blue Laser Diode (Springer, Berlin, 2000).CrossRefGoogle Scholar
2. Matsuoka, T., Okamoto, H., Nakao, M., et al. , Appl. Phys. Lett. 81, 1246 (2002).CrossRefGoogle Scholar
3. Arakawa, Y., phys. stat. sol. (a) 188, 37 (2001).3.0.CO;2-Q>CrossRef3.0.CO;2-Q>Google Scholar
4. Tachibana, K., Someya, T. and Arakawa, Y., Appl. Phys. Lett. 74, 383 (1999).CrossRefGoogle Scholar
5. Kim, H. J., Na, H., Kwon, S.-Y., Seo, H.-C., Kim, H. J., Shin, Y., Lee, K.-H., Kim, D. H., Oh, H. J. and Yoon, S., J. Crystal Growth 269, 95 (2004).CrossRefGoogle Scholar
6. Grandjean, N. and Massies, J., Appl. Phys. Lett. 72, 1078 (1998).CrossRefGoogle Scholar
7. Adelmann, C., Simon, J., Feuillet, G., Pelekanos, N. T., Daudin, B. and Fishman, G., Appl. Phys. Lett. 76, 1570 (2000).CrossRefGoogle Scholar
8. Keller, S., Mishra, U.K., DenBaars, S.P. and Seifert, W., Jpn. J. Appl. Phys. 37, L431 (1998).CrossRefGoogle Scholar
9. Neugebauer, J., Zywietz, T. K., Scheffler, M., et al. , Phys. Rev. Lett. 90, 56101 (2003).CrossRefGoogle Scholar
10. Pretorius, A. et al. , Private communicationGoogle Scholar
11. Neugebauer, J. et al. , Private communicationGoogle Scholar