Structural Defects in Laterally Overgrown GaN Layers Grown on Non-polar Substrates

Published online by Cambridge University Press:  01 February 2011

Zuzanna Liliental-Weber ,
X. Ni  and
H. Morkoc
Zuzanna Liliental-Weber
Affiliation:
[email protected], Lawrence Berkeley National Laboratory, Materials Science Division, 1 Cyclotron Rd, M/S 62R0203-8255, BERKELEY, CA, 94720-8139, United States, 510-486-6276, 510-486-4995
X. Ni
Affiliation:
[email protected], Virginia Commonwealth University, Richmond, VA, 23284, United States
H. Morkoc
Affiliation:
[email protected], Virginia Commonwealth University, Richmond, VA, 23284, United States
Get access

Abstract

Transmission electron microscopy was used to study defects in lateral epitaxial layers of GaN which were overgrown on a template of a-plane (1120) GaN grown on (1102) r-plane Al2O3. A high density of basal stacking faults is formed in these layers because the c-planes of wurtzite structure are arranged along the growth direction. Density of these faults is decreasing at least by two orders of magnitude lower in the wings compared to the seed areas. Prismatic stacking faults and threading dislocations are also observed, but their densities drastically decrease in the wings. The wings grow with opposite polarities and the Ga-wing width is at least 6 times larger than N-wing and coalescence is rather difficult. Some tilt and twist was detected using Large Angle Convergent Beam Electron Diffraction.

Keywords

defectsnitridetransmission electron microscopy (TEM)
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 955: Symposium I – Advances in III-V Nitride Semiconductor Materials and Devices , 2006 , 0955-I11-04
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Lefebvre, P., Allegre, J., Gil, B., et al., Phys. Rev. B 59, 15363 (1999).Google Scholar
2. Seo, I. Jin, Kollmer, H., Off, J., et al., Phys. Rev. B57, R9435 (1998).Google Scholar
3. Takeuchi, T., Wetzel, C., Yamaguchi, S., et al., Appl. Phys. Lett. 73, 1691 (1998).Google Scholar
4. Zakharov, D.N., Liliental-Weber, Z., Wagner, B., Reitmeier, Z.J., Preble, E.A., and Davis, R.F., Phys. Rev. B 71, 235334 (2005).Google Scholar
5. Hull, D. and Bacon, D.J., Introduction to Dislocations (Pergamon Press, Oxford, 1984).Google Scholar
6. Liliental-Weber, Z., Zakharov, D., Wagner, B., and Davis, R.F., Proceedings of SPIE-The International Society for Optical Engineering, vol.6121, 612101–10, San Jose CA (2006).Google Scholar