Preparation of (Pb, Ca)(Fe0.5Nb0.5)1-yTiyO3 Perovskite Ceramics by a Reaction-Sintering Process

Published online by Cambridge University Press:  01 February 2011

Yi-Cheng Liou ,
Jen-Hsien Chen  and
Hsueh-Yung Lu
Yi-Cheng Liou
Affiliation:
Department of Electronic Engineering, Kun-Shan University of Technology, Tainan Hsien 710, Taiwan, R.O.C.
Jen-Hsien Chen
Affiliation:
Department of Electronic Engineering, Kun-Shan University of Technology, Tainan Hsien 710, Taiwan, R.O.C.
Hsueh-Yung Lu
Affiliation:
Department of Electronic Engineering, Kun-Shan University of Technology, Tainan Hsien 710, Taiwan, R.O.C.
Get access

Abstract

Synthesis of (Pb0.45Ca0.55)(Fe0.5Nb0.5)1-yTiyO3 (y=0 and 0.1; PCFN and PCFNT) ceramics by a reaction-sintering process was investigated. The mixture of raw materials was pressed and sintered into ceramics without any calcination stage involved. The density 5.88g/cm3 (91.6% of the theoretical value) is reached at 1270°C for 2 h soak time in PCFN. Densification increased as B-site was substituted by 10% Ti and a density value 6.21g/cm3 (98.1% of theoretical value) was obtained after 2 h sintering at 1270°C. Grains are of 4.6–19.3μm in PCFN and 2.5–16.5μm in PCFNT at 1150–1270°C. Grain growth was retarded as the B-site was substituted by 10% Ti in PCFN ceramics.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 848: Symposium FF – Solid-State Chemistry of Inorganic Materials V , 2004 , FF3.4
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Wersing, W., Electronic Ceramics. Edited by Steele, B. C. H.. (Elsevier Applied Science, London, U. K., 1991) p.67.Google Scholar
2. Kato, J., Kagata, H. and Nishimoto, K., Jpn. J. Appl. Phys. 31, 3144 (1992).Google Scholar
3. Kagata, H., Kato, J., Nishimoto, K. and Inoue, T., Jpn. J. Appl. Phys. 32, 4332 (1993).Google Scholar
4. Kucheiko, S., Choi, J. W., Kim, H. J., Yoon, S. J. and Jung, H. J., J. Am. Ceram. Soc. 80, 2937 (1997).Google Scholar
5. Hu, M., Zhou, D., Zhang, D., Lu, W., Li, B., Huang, J. and Gong, S., Mater. Sci. & Eng. B 99, 403 (2003).Google Scholar
6. Wang, J., Wan, D. W., Xue, J. M. and Ng, W. B., Singapore Patent No. 9801566–2 (1998).Google Scholar
7. Hamada, K. and Senna, M., J. Mater. Sci. 31, 1725 (1996).Google Scholar
8. Gomez-Yanez, C., Benitez, C. and Balmori-Ramirez, H., Ceram. Int. 26, 271 (2000).Google Scholar
9. Kong, L. B., Ma, J., Huang, H., Zhang, R. F. and Que, W. X., J. Alloys and Comp. 337, 226 (2002).Google Scholar
10. Lee, S. E., Xue, J. M., Wan, D. W. and Wang, J., J. Acta Mater. 47(9), 2633 (1999).Google Scholar
11. Kong, L. B. and Ma, J., Mater. Lett. 51, 95 (2001).Google Scholar
12. Liou, Y. C., Tseng, K. H. and Yu, C. H., Proceedings of the 2001 annual Conference of the Chinese Society for Materials Science, 23–24 November 2001, National Chung Hsing University, Taichung, Taiwan, P03–09.Google Scholar
13. Liou, Y. C., Tseng, K. H. and Yu, C. H., Proceedings of the 2001 annual Conference of the Chinese Society for Materials Science, 23–24 November 2001, National Chung Hsing University, Taichung, Taiwan, P03–17.Google Scholar
14. Liou, Y. C., Shih, C. Y. and Yu, C. H., Proceedings of the 2001 annual Conference of the Chinese Society for Materials Science, 23–24 November 2001, National Chung Hsing University, Taichung, Taiwan, P03–102.Google Scholar
15. Liou, Y. C., Chen, J. H. and Sung, Y. L., Mater. Sci. & Eng. B (2004) submitted for publication.Google Scholar
16. Liou, Y. C., C., and Shiue, Y., 2004 MRS FALL MEETING, Boston, MA, November 29-December 3, 2004.Google Scholar
17. Shaw, T. M., J. Am. Ceram. Soc. 69 [1], 27 (1986).Google Scholar
18. Rhim, S. M., Bak, H., Hong, S. and Kim, O. K., J. Am. Ceram. Soc. 83[12], 3009 (2000).Google Scholar
19. Kim, E. S., Jeon, J. S. and Yoon, K. H., J. Eur. Ceram. Soc. 23, 2583 (2003).Google Scholar
20. Liou, Y. C., Shih, C. Y. and Yu, C. H., Mater. Lett. 57, 1977 (2003).Google Scholar
21. Ha, J. Y., Choi, J. W., Kim, H. J., Yoon, S. J. and Yoon, K. H., Mater. Chem. & Phy. 79, 261 (2003).Google Scholar
22. Yang, Q., Kim, E. S., Xu, J. and Meng, Z., Mater. Sci. & Eng. B 99, 332 (2003).Google Scholar