Microstructure and Mechanical Properties of Dual Two-Phase Intermetallic Alloys Composed of GCP Ni3Al and Ni3V Phases containing Nb

Published online by Cambridge University Press:  26 February 2011

Wataru Soga
Affiliation:
[email protected], Osaka Prefecture University, Material Science, 1-1, Gakuen-cho, Sakai, 599-8531, Japan
Yasuyuki Kaneno
Affiliation:
[email protected], Osaka Prefecture University, Department of Materials Science, Graduate School of Engineering, 1-1 Gakuen-cho, Naka-ku, Sakai, Osaka, 599-8531, Japan
Takayuki Takasugi
Affiliation:
[email protected], Osaka Prefecture University, Department of Materials Science, Graduate School of Engineering, 1-1 Gakuen-cho, Naka-ku, Sakai, Osaka, 599-8531, Japan
Get access

Abstract

Dual multi-phase intermetallic alloys composed of Ni3X (X: Al and V) containing Nb were developed, on the basis of the Ni3Al-Ni3Nb-Ni3V pseudo-ternary alloy system. The dual multi-phase intermetallic alloys were characterized by scanning electron and transmission electron microscopies. High-temperature compression and tension tests, and compression creep test were conducted. It was found that the dual multi-phase intermetallic alloys show high yield and tensile strength with good temperature retention, accompanied with reasonable tensile ductility. The compression creep test conducted at high temperature showed lower creep rate in the dual multi-phase intermetallic alloys than in conventional Ni-base superalloys. The obtained results are superior to the dual multi-phase intermetallic alloys containing Ti.

Type
Research Article
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Nunomura, Y., Kaneno, Y., Tsuda, H., and Takasugi, T., Intermetallics 12, 389 (2004).Google Scholar
2. Nunomura, Y., Kaneno, Y., Tsuda, H., and Takasugi, T., Acta Mater. 54, 851 (2006).Google Scholar
3. Shibuya, S., Kaneno, Y., Tsuda, H., T. and Takasugi. Intermetallics in press.Google Scholar
4. Shibuya, S., Kaneno, Y., Yoshida, M., and Takasugi, T., Acta Mater. 54, 861 (2006).Google Scholar
5. Shibuya, S., Kaneno, Y., Yoshida, M., Shishido, T., and Takasugi, T., Intermetallics in press.Google Scholar
6. Soga, W., Kaneno, Y., and Takasugi, T., Intermetallics 14, 170 ( 2006).Google Scholar
7. Land, R.W. and Nix, W.D., Acta Metall. 24, 469 (1976).Google Scholar
8. Yamaguchi, M. and Umakoshi, Y., Prog. Mater. Sci. 34, 1 (1990).Google Scholar
9. Hagihara, K., Nakano, T., and Umakoshi, Y., Acta Mater. 48, 1469 (2000).Google Scholar
10. Hagihara, K., Nakano, T., and Umakoshi, Y., Scripta Mater. 248, 577 (2003).Google Scholar
11. Hagihara, K., Nakano, T., and Umakoshi, Y., Acta Mater. 51, 2623 (2003).Google Scholar
12. Hagihara, K., Tanaka, T., Nakano, T., and Umakoshi, Y., Acta Mater. 53, 5051 (2005).Google Scholar
13. von Mises, R., Z. Ang. Math. Mech. 18, 161(1928).Google Scholar
14. Soga, W., Kaneno, Y., Yoshida, M., and Takasugi, T., Mater. Sci. Eng. A, in press.Google Scholar