Investigation of AuNi5 Films Deposited by Pulsed Laser Deposition for RF MEMS Switch Contacts

Published online by Cambridge University Press:  26 February 2011

Noha Farghal ,
Moustafa Yehia Ghannam ,
Amr M. Shaarawi ,
Hussein El Samman ,
Philippe Soussan  and
Kris Baert
Noha Farghal
Affiliation:
[email protected], The American University in Cairo, Yousef Jameel Science and Technology Research Center, 139 Al Haram Street, Giza, 00000000000, Egypt
Moustafa Yehia Ghannam
Affiliation:
[email protected], Kuwait University, EE Department, Kuwait City, N/A, Kuwait
Amr M. Shaarawi
Affiliation:
[email protected], the American University in Cairo, Yousef Jameel Science and Technology Research Center, Cairo, N/A, Egypt
Hussein El Samman
Affiliation:
[email protected], Menoufia University, Physics Department, Shibin, N/A, Egypt
Philippe Soussan
Affiliation:
[email protected], IMEC v.z.w., Leuven, N/A, Belgium
Kris Baert
Affiliation:
[email protected], IMEC v.z.w., Leuven, N/A, Belgium
Get access

Abstract

In this work, the material properties of AuNi5 films prepared by Pulsed Laser Deposition (PLD) to be used as contact materials in RF MEMS switches are investigated. PLD is used because it provides good wide range thickness control (few nanometers to tens of microns) while preserving ablation target stoichiometry. Films with thickness in the range 50 - 450 nm were deposited at Laser energy density (fluence) in the range 0.55 - 1.38 J.cm-2 on silicon substrates at room temperature. An aperture was placed between the plume and the substrate to filter out large particulates. The presence of the aperture reduced surface roughness from 8.5 nm to 4.3 nm as determined by optical profilometry. In addition, the presence of the aperture during deposition has been found to affect film stoichiometry. The latter was evaluated using X-ray Fluorescence and the Nickel content has been found to vary in the range 1.1 - 9.5%. Only films deposited with the aperture removed maintain target stoichiometry (5.2% Ni). Hence, it is believed that the presence of the aperture causes non-congruent transfer. The Nickel content within the range under investigation has practically no effect on film morphology or hardness. Laser fluence, however, has been found to be the dominant factor determining film properties. Finally, 100 µm wide AuNi5 strips 290 nm and 130 nm thick deposited at room temperature have been successfully formed on silicon wafers by lift-off photolithography.

Keywords

Aulaser ablationmicroelectro-mechanical (MEMS)
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 980: Symposium II – Advanced Intermetallic-Based Alloys , 2006 , 0980-II05-46
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Schimkat, J., “Contact Materials for Microrelays,” 11thAnnual Workshop on Micro Electro Mechanical Systems, Heidelberg, Germany (1998)Google Scholar
2. Krebs, H., Bremert, O., Störmer, Michael and Luo, Yuansu, Appl. Surf. Sci. 86 (1995)Google Scholar
3. Krebs, H. and Bremert, O., App. Phys. Lett. 62 (1993)10.1063/1.109412Google Scholar
4. Chrisey, D., Hubler, G. (Eds.): Pulsed Laser Deposition of Thin Films (Wiley, New York 1994)Google Scholar
5. van de Riet, E., Kools, J. C. S., Dieleman, J. J. Appl. Phys. 73, 8290 (1993)10.1063/1.353447Google Scholar
6. Arnold, C. B. and Aziz, M. J., Appl. Phys. A. 69 (1999)10.1007/s003399900183Google Scholar
7. van Ingen, R. P., Fastenau, R. H. J., Mittemeijer, E. J.: J. Appl. Phys. 76, 1871 (1994)10.1063/1.357711Google Scholar