Growth of Large Grain Polycrystalline Silicon Thin Film on Soda-lime Glass at Low Temperature for Solar Cell Applications

Published online by Cambridge University Press:  27 July 2011

K. Wang  and
K. H. Wong
K. Wang
Affiliation:
Department of Applied Physics and Materials Research Centre, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong, China
K. H. Wong
Affiliation:
Department of Applied Physics and Materials Research Centre, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong, China
Get access

Abstract

High quality polycrystalline silicon (poly-Si) thin film solar cell was successfully fabricated on soda-lime glass substrates by electron beam (Ebeam) evaporation at low processing temperature. The initial poly-Si seed layer (p+-type 0.5 μm thick) was grown via the aluminum induced crystallization (AIC) method at 450 °C. Prominent interdiffusion and Si crystallization have been observed. X-ray diffraction (XRD) shows that (111) is the dominating crystalline orientation. Post annealing at 450 °C for six hours has produced densely packed Si grains with dimension of more than 10 μm in the plane of the film. Non-destructive Raman spectroscopy reveals the remarkable crystalline improvement for samples after thermal treatment. After removing the top diffused Al by chemical means, an absorber layer (p-type) of 0.9 μm thick was subsequently deposited onto the seed layer by Ebeam evaporation at 500 °C. Transmission electron microscopy (TEM) confirmed good homo-epitaxial growth. Without breaking the high vacuum, an n-type amorphous Si (a-Si) layer (0.7 μm thick) was coated onto the absorber layer to form p-n junction. The corresponding I-V characteristics suggest that our low temperature processing technique is applicable for production of poly-Si thin film solar cell on low cost substrates.

Keywords

polycrystalSiAl
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1321: Symposium A – Amorphous and Polycrystalline Thin-Film Silicon Science and Technology , 2011 , mrss11-1321-a06-12
Copyright
Copyright © Materials Research Society 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Müller, A., Ghosh, M., Sonnenschein, R. and Woditsch, P., Mater. Sci. Eng. B 134, 257 (2006).10.1016/j.mseb.2006.06.054Google Scholar
2. Hammond, A. L., Science 178, 732 (1972).10.1126/science.178.4062.732Google Scholar
3. Shah, A., Torres, P., Tscharner, R., Wyrsch, N. and Keppner, H., Science 285, 692 (1999).10.1126/science.285.5428.692Google Scholar
4. Green, M., Appl. Phys. A: Mater. Sci. & Process. 96, 153 (2009).10.1007/s00339-009-5090-9Google Scholar
5. Tan, Z., Heald, S. M., Rapposch, M., Bouldin, C. E. and Woicik, J. C., Phys. Rev. B 46, 9505 (1992).10.1103/PhysRevB.46.9505Google Scholar
6. Jin, Z., Bhat, G. A., Yeung, M., Kwok, H. S. and Wong, M., J. Appl. Phys. 84, 194 (1998).10.1063/1.368016Google Scholar
7. Nast, O. and Hartmann, A. J., J. Appl. Phys. 88, 716 (2000).10.1063/1.373727Google Scholar
8. Guliants, E. A. and Anderson, W. A., J. Appl. Phys. 89, 4648 (2001).10.1063/1.1359150Google Scholar
9. He, D., Wang, J. Y. and Mittemeijer, E. J., J. Appl. Phys. 97, 093524 (2005).10.1063/1.1890449Google Scholar
10. Wang, Z. M., Wang, J. Y., Jeurgens, L. P. H. and Mittemeijer, E. J., Phys. Rev. B 77, 045424 (2008).10.1103/PhysRevB.77.045424Google Scholar
11. Hiraki, A., Surf. Sci. Rep. 3, 357 (1983).10.1016/0167-5729(84)90003-7Google Scholar
12. Gleiter, H. and Chalmer, B., Prog. Mater. Sci. 16, 77 (1972).Google Scholar
13. Kim, H., Kim, D., Lee, G., Kim, D. and Lee, S. H., Sol. Energy Mater. Sol. Cells 74, 323 (2002).10.1016/S0927-0248(02)00091-0Google Scholar
14. Gong, S. F., Hentzell, H. T. G., Robertsson, A. E., Hultman, L., Hornstrom, S.-E. and Radnoczi, G., J. Appl. Phys. 62, 3726 (1987).10.1063/1.339256Google Scholar
15. Huang, S., Xu, S., Cheng, Q., Long, J. and Ostrikov, K., Appl. Phys. A: Mater. Sci. & Process. 97, 375 (2009).10.1007/s00339-009-5220-4Google Scholar