Formation of Polycrystalline Silicon Films Using Electrical-Current-Induced Joule Heating

Published online by Cambridge University Press:  17 March 2011

Nobuyuki Andoh ,
Hiroyuki Takahashi  and
Toshiyuki Sameshima
Nobuyuki Andoh
Affiliation:
Faculty of Technology, Tokyo University of Agriculture and Technology, Koganei, Tokyo 184-8588, JAPAN
Hiroyuki Takahashi
Affiliation:
Faculty of Technology, Tokyo University of Agriculture and Technology, Koganei, Tokyo 184-8588, JAPAN
Toshiyuki Sameshima
Affiliation:
Faculty of Technology, Tokyo University of Agriculture and Technology, Koganei, Tokyo 184-8588, JAPAN
Get access

Abstract

Electrical current induced joule heating method was applied to crystallization of 50 nm-thick amorphous silicon films formed on glass substrates. Voltages were applied to silicon films connected with a capacitance in parallel. Irradiation with 5 ns-pulsed-laser melted films partially and caused electrical current induced joule heating because of reduction of electrical resistance. Lateral grain growth with 12.6 µm was realized using the tapered-shaped-electrodes to apply voltages to silicon films with a capacitance of 0.33 µF. For 2.6×10 17 cm−3 phosphorus-doped films, analysis of temperature change in the electrical conductivity gave that defect states at grain boundaries was low of ∼1017 cm−3.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 664: Symposium A – Amorphous and Heterogeneous Silicon-Based Films-2001 , 2001 , A6.2
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Sameshima, T., Usui, S. and Sekiya, M., IEEE Electron Device Lett. 7, 276 (1986).Google Scholar
2. Sera, K., Okumura, F., Uchida, H., Itoh, S., Kaneko, S. and Hotta, K., IEEE Trans. Electron Devices. 36, 2868 (1989).Google Scholar
3. Serikawa, T., Shirai, S., Okamoto, A. and Suyama, S., Jpn. J. Appl. Phys. 28, L1871 (1989).Google Scholar
4. Kohno, A., Sameshima, T., Sano, N., Sekiya, M. and Hara, M., IEEE Trans. Electron Devices. 42, 251 (1995).Google Scholar
5. Matsuda, A., J. Non-Cryst. Solids. 59/60, 767 (1983).Google Scholar
6. Chida, Y., Kondo, M. and Matsuda, A., J. Non-Cryst. Solids. 198–200, 1121 (1996).Google Scholar
7. Sameshima, T. and Ozaki, K., Jpn. J. Appl. Phys. 39, L651 (2000).Google Scholar
8. Andoh, N., Ozaki, K., Takahashi, H. and Sameshima, T., Proc. Workshop on Active Matrix Liquid Crystal Displays (Tokyo, Japan 2000) p. 261.Google Scholar
9. Sameshima, T., Ozaki, K., Takahashi, H. and Andoh, N., Proc. Workshop on Active Matrix Liquid Crystal Displays (Tokyo, Japan 2000) p.207.Google Scholar
10. Sameshima, T., Ozaki, K. and Andoh, N., Appl. Phys. A71, 1 (2000).Google Scholar
11. Seto, J. Y. W., J. Appl. Phys. 46, 5247 (1975).Google Scholar
12. Sakamoto, K., Sameshima, T., Tsunoda, Y. and Higashi, S., Proc. Workshop on Active Matrix Liquid Crystal Displays (Tokyo, Japan 1999) p.131.Google Scholar
13. Baccarani, G., Ricco, B., J. Appl. Phys. 19, 5565 (1978).Google Scholar
14. Asada, K., Sakamoto, K., Watanabe, T., Sameshima, T. and Higashi, S., Jpn. J. Appl. Phys. 39, 3883 (2000).Google Scholar