Deep Level Defects in He-implanted n-6H-SiC Studied by Deep Level Transient Spectroscopy

Published online by Cambridge University Press:  15 March 2011

X. D. Chen
Affiliation:
Department of Physics, The University of Hong Kong, Pokfulam Road, Hong Kong, P. R. China
C. C. Ling
Affiliation:
Department of Physics, The University of Hong Kong, Pokfulam Road, Hong Kong, P. R. China
S. Fung
Affiliation:
Department of Physics, The University of Hong Kong, Pokfulam Road, Hong Kong, P. R. China
C. D. Beling
Affiliation:
Department of Physics, The University of Hong Kong, Pokfulam Road, Hong Kong, P. R. China
H. S. Wu
Affiliation:
Department of Physics, The University of Hong Kong, Pokfulam Road, Hong Kong, P. R. China
G. Brauer
Affiliation:
Institut für Ionenstrahlphysik und Materialforschung, Forschungszentrum Rossendorf, Postfach 510119, D-01314 Dresden, Germany
W. Anwand
Affiliation:
Institut für Ionenstrahlphysik und Materialforschung, Forschungszentrum Rossendorf, Postfach 510119, D-01314 Dresden, Germany
W. Skorupa
Affiliation:
Institut für Ionenstrahlphysik und Materialforschung, Forschungszentrum Rossendorf, Postfach 510119, D-01314 Dresden, Germany
Get access

Abstract

Deep level transient spectroscopy (DLTS) was used to study deep level defects in He-implanted n-type 6H-SiC samples. Low dose He-implantation (fluence ∼2×1011 ions/cm2) has been employed to keep the as-implanted sample conductive so that studying the introduction and the thermal evolution of the defects becomes feasible. A strong broad DLTS peak at 275K-375K (called signal B) and another deep level at EC-0.50eV were observed in the as-implanted sample. The intensity of the peak B was observed to linearly proportional to the logarithm of the filling pulse width, which is a signature for electron capture into a defect related to dislocation. After annealing at 500°C, the intensity of peak was significantly reduced and the remained signal has properties identical to the well known Z1/Z2 deep defects, although it is uncertain whether the Z1/Z2 exist in the as-implanted sample or it is the annealing product of the dislocation-related defect. The E1/E2 defect (EC-0.3/0.4eV) was not presence in the as-implanted sample, but was observed after the 300°C annealing.

Type
Research Article
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Morkoç, H., Strite, S., Gao, G. B., Lin, M. E., Sverdlov, B., and Burns, M., J. App. Phys. 76, 1362 (1994).Google Scholar
2. Pensl, G. and Choyke, W. J., Physica B 185, 264 (1993).Google Scholar
3. Dalibor, T., Pensl, G., Matsunami, H., Kimoto, T., Choyke, W. J., Schoener, A. and Nordell, N., Phys. Stat. Sol. (a) 162, 199 (1997).Google Scholar
4. Aboelfotoh, M. O. and Doyle, J. P., Phys. Rev. B 59, 10 823 (1999).Google Scholar
5. Lebedev, A. A., Veinger, A. I., Davydov, D. V., Kozlovski, V. V., Savkina, N. S., and Strel'chuk, A. M., J. Appl. Phys. 88, 6265 (2000).Google Scholar
6. Frank, Th., Pensl, G., Bai, Song, Devaty, R. P. and Choyke, W. J., Mat. Sci. For. 338–342, 753 (2000).Google Scholar
7. Hemmingsson, C. G., Son, N. T., Kordina, O., Janzén, E., and Lindström, J. L., J. Appl. Phys. 84, 704 (1998).Google Scholar
8. Gong, M., Fung, S., Beling, C. D., and You, Z., J. Appl. Phys. 85, 7604 (1999).Google Scholar
9. Weidner, M., Frank, T., Pensl, G., Kawasuso, A., Itoh, H., and Krause-Rehberg, R., Physica B 308–310, 633 (2001).Google Scholar
10. Chen, X. D., Fung, S., Ling, C. C., Beling, C. D., and Gong, M., J. Appl. Phys. 94, 3004 (2003).Google Scholar
11. Wosinski, T., J. Appl. Phys. 65, 1566 (1989).Google Scholar
12. Omling, P., Weber, E. R., Montelius, L., Alexander, H., and Michel, J., Phys. Rev. B 32, 6571 (1985).Google Scholar