A Bond-Order Potential Incorporating Analytic Screening Functions for the Molybdenum Silicides

Published online by Cambridge University Press:  26 February 2011

Marc J. Cawkwell ,
Matous Mrovec ,
Duc Nguyen-Manh ,
David G. Pettifor  and
Vaclav Vitek
Marc J. Cawkwell
Affiliation:
Department of Materials Science and Engineering, University of Pennsylvania, 3231 Walnut Street, Philadelphia, PA 19104–6272, U.S.A.
Matous Mrovec
Affiliation:
Fraunhofer Institut für Werkstoffmechanik, Wöhlerstr. 11, 79108 Freiburg, GERMANY.
Duc Nguyen-Manh
Affiliation:
UKAEA Fusion, Culham Science Centre, Abingdon, OX14 3DB, UNITED KINGDOM.
David G. Pettifor
Affiliation:
Department of Materials, University of Oxford, Parks Road, Oxford, OX1 3PH, UNITED KINGDOM.
Vaclav Vitek
Affiliation:
Department of Materials Science and Engineering, University of Pennsylvania, 3231 Walnut Street, Philadelphia, PA 19104–6272, U.S.A.
Get access

Abstract

The intermetallic compound MoSi2, which adopts the C11b crystal structure, and related alloys exhibit an excellent corrosion resistance at high temperatures but tend to be brittle at room and even relatively high temperatures. The limited ductility of MoSi2 in ambient conditions along with the anomalous temperature dependence of the critical resolved shear stress (CRSS) of the {110)<111], {011)<100] and {010)<100] slip systems and departure from Schmid law behavior of the {013)<331] slip system can all be attributed to complex dislocation core structures. We have therefore developed a Bond-Order Potential (BOP) for MoSi2 for use in the atomistic simulation of dislocations and other extended defects. BOPs are a real-space, O(N), two-center orthogonal tight-binding formalism that are naturally able to describe systems with mixed metallic and covalent bonding. In this development novel analytic screening functions have been adopted to properly describe the environmental dependence of bond integrals in the open, bcc-based C11b crystal structure. A many-body repulsive term is included in the model that allows us to fit the elastic constants and negative Cauchy pressures of MoSi2. Due to the internal degree of freedom in the position of the Si atoms in the C11b structure which is a function of volume, it was necessary to adopt a self-consistent procedure in the fitting of the BOP. The constructed BOP is found to be an excellent description of cohesion in C11b MoSi2 and we have carefully assessed its transferability to other crystal structures and stoichiometries, notably C 40, C 49 and C 54 MoSi2, A15 and D03 Mo3Si and D8m Mo5Si3 by comparing with ab initio structural optimizations.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 842: Symposium S – Integrative and Interdisciplinary Aspects of Intermetallics , 2004 , S2.8
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Yamaguchi, M., Inui, H. and Ito, K., Acta Mater. 48, 307 (2000)Google Scholar
2. Ito, K., Inui, H., Shirai, Y. and Yamaguchi, M., Phil. Mag. A 72, 1075 (1995)Google Scholar
3. Daw, M. S. and Baskes, M. I., Phys. Rev. B 29, 6443 (1984)Google Scholar
4. Finnis, M. W. and Sinclair, J. E., Phil. Mag. A 50, 45 (1984)Google Scholar
5. Horsfield, A. P., Bratkovsky, A. M., Fearn, M., Pettifor, D. G. and Aoki, M., Phys. Rev. B 53, 12694 (1996)Google Scholar
6. Nguyen-Manh, D., Pettifor, D. G., Cockayne, D. J. H., Mrovec, M., Znam, S. and Vitek, V., Bull. Mater. Sci. 26, 43 (2003)Google Scholar
7. Mrovec, M., Nguyen-Manh, D., Pettifor, D. G. and Vitek, V., Phys. Rev. B 69, 094115 (2004)Google Scholar
8. Cawkwell, M. J., Nguyen-Manh, D., Vitek, V. and Pettifor, D. G., Mat. Res. Soc. Symp. Proc. Vol. 779, W5.5.1 (2003)Google Scholar
9. Znam, S., Nguyen-Manh, D., Pettifor, D. G. and Vitek, V., Phil. Mag. 83, 415 (2003)Google Scholar
10. Nguyen-Manh, D., Pettifor, D. G., Znam, S. and Vitek, V., Mat. Res. Soc. Symp. Proc. Vol. 491, 353 (1998)Google Scholar
11. Nguyen-Manh, D., Pettifor, D. G. and Vitek, V., Phys. Rev. Lett. 85, 4136 (2000)Google Scholar
12. Blaha, P., Schwarz, K., Madsen, G. K. H., Kvasnicka, D. and Luitz, J., WIEN2k, An Augmented Plane Wave + Local Orbitals Program for Calculating Crystal Properties, (Karlheinz Schwarz, Techn. Universität Wien, Austria), 2001. ISBN 3–9501031–1–2 Google Scholar
13. Sutton, A. P., Finnis, M. W., Pettifor, D. G. and Ohta, Y., J. Phys. C: Solid State Phys. 21, 35 (1988)Google Scholar
14. Ducastelle, F. and Cyrot-Lackmann, F., J. Phys. Chem. Sol. 31, 1295 (1970)Google Scholar
15. Lanczos, C., J. Res. Nat. Bur. Stand. 45, 255 (1950)Google Scholar
16. Tanaka, K., Nawata, K., Inui, H., Yamaguchi, M. and Koiwa, M., Intermetallics 9, 603 (2001)Google Scholar
17. Tanaka, K., Onome, H., Inui, H., Yamaguchi, M. and Koiwa, M., Mat. Sci. Eng. A 239–240, 188 (1997)Google Scholar